Rodrigo Martins

In the production of porous silicon (PS) to optoelectronic application one of the most significant constrains is the surface defects passivation. In the present work we investigate, gallium-doped zinc oxide (GZO) thin films deposited by rf magnetron sputtering at room temperature on PS obtained with different etching times. The X-ray diffraction (XRD), Fourier transform infrared (FTIR) and atomic force microscopy (AFM) analysis have been carried out to understand the effect of GZO films coating on PS. Further, the XRD analysis suggests the formation of a good crystalline quality of the GZO films on PS. From AFM investigation we observe that the surface roughness increases after GZO film coating. The photoluminescence (PL) measurements on PS and GZO films deposited PS shows three emission peaks at around 1.9 eV (red-band), 2.78 eV (blue-band) and 3.2 eV (UV-band). PL enhancement in the blue and ultraviolet (UV) region has been achieved after GZO films deposition, which might be originated from a contribution of the near-band-edge recombination from GZO. © 2007 Elsevier B.V. All rights reserved.

Aqueous suspensions of cordierite-based glass ceramics were prepared by using four types of dispersants and binders and different solids loading. The experiments were designed according to the Taguchi method, which shows great advantages in optimising more than two factors that need to be considered in an experimental design. Different parameters such as the type and concentration of the dispersants and the binders, and the solids loading were optimised to obtain homogeneous and crack-free green tapes. Dolapix CE 64 (1.0 wt.%) and Duramax B-1080 or Duramax B-1070 (10 wt.%) with 65 wt.% solids loading represent an optimal selection of the parameters to obtain low viscosity suspension, and crack-free green tapes with the highest green and sintered density. Microstructural differences between crack-free and cracked samples were observed by scanning electron microscopy (SEM). The crack-free green tapes show homogenous microstructures from top to bottom with organic additives uniformly surrounding the powders, whereas cracked samples exhibit heterogeneous microstructures and non-uniform distribution of the organics. © 2002 Elsevier Science B.V. All rights reserved.

The aim of this work is to optimize the metal/silicon ratio on nickel metal induced crystallization of silicon. For this purpose amorphous silicon layers with 80, 125 and 220 nm thick were used on the top of which 0.5 nm of Ni was deposited and annealed during the required time to full crystallize the a-Si. The data show that the 80 nm a-Si layer reaches a crystalline fraction of 95.7% (as detected by spectroscopic ellipsometry) after annealed for only 2 hours. No significant structural improvement is detected by ellipsometry neither by XRD when annealing the films for longer times. However, on 125 nm thick samples, after annealing for 2 hours the crystalline fraction is only 59.7%, reaching a similar value to the one with 80 nm only after 5 hours, with a crystalline fraction of 92.2%. Here again no significant improvements were achieved by using longer annealing times. Finally, the 220 nm thick a-Si sample is completely crystallized only after 10 hours annealing. These data clear suggest that the crystallization of thicker a-Si layers requires thicker Ni films to be effective for short annealing times. A direct dependence of the crystallization time on the metal/silicon ratio was observed and estimated. © 2005 Materials Research Society.

Transparent electronics is today one of the most advanced topics for a wide range of device applications. The key components are wide bandgap semiconductors, where oxides of different origins play an important role, not only as passive component but also as active component, similar to what is observed in conventional semiconductors like silicon. Transparent electronics has gained special attention during the last few years and is today established as one of the most promising technologies for leading the next generation of flat panel display due to its excellent electronic performance. In this paper the recent progress in n- and p-type oxide based thin-film transistors (TFT) is reviewed, with special emphasis on solution-processed and p-type, and the major milestones already achieved with this emerging and very promising technology are summarizeed. After a short introduction where the main advantages of these semiconductors are presented, as well as the industry expectations, the beautiful history of TFTs is revisited, including the main landmarks in the last 80 years, finishing by referring to some papers that have played an important role in shaping transparent electronics. Then, an overview is presented of state of the art n-type TFTs processed by physical vapour deposition methods, and finally one of the most exciting, promising, and low cost but powerful technologies is discussed: solution-processed oxide TFTs. Moreover, a more detailed focus analysis will be given concerning p-type oxide TFTs, mainly centred on two of the most promising semiconductor candidates: copper oxide and tin oxide. The most recent data related to the production of complementary metal oxide semiconductor (CMOS) devices based on n- and p-type oxide TFT is also be presented. The last topic of this review is devoted to some emerging applications, finalizing with the main conclusions. Related work that originated at CENIMAT|I3N during the last six years is included in more detail, which has led to the fabrication of high performance n- and p-type oxide transistors as well as the fabrication of CMOS devices with and on paper. Transparent electronics is one of the most advanced science topics for a broad range of device applications. In this article an overview is presented of state-of-the-art n- and p-type oxides for TFTs and their integration, processed by physical vapor deposition and by solution processing techniques. Some of the most relevant emerging applications are also presented, including CMOS devices based on oxide TFTs fabricated on glass and even on paper. Copyright © 2012 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

The effect is considered of order and disorder on the electrical and optical performance of ionic oxide semiconductors used to produce optoelectronic devices such as p-n heterojunction solar cells and thin-film transistors (TFTs). The results obtained show that p-type c-Si/a-IZO/poly-ZGO solar cells exhibit efficiencies above 14% in device areas of about 2.34 cm2, whereas amorphous oxide TFTs based on the Ga-Zn-Sn-O system demonstrate superior performance to the polycrystalline ZnO TFTs, with ION/I OFF ratio exceeding 107, turn-on voltage below 1-2 V and saturation mobility above 25 cm2 V-1 s-1. In addition, preliminary data on a p-type oxide TFT based on the Zn-Cu-O system are presented. © 2009 Taylor & Francis.

Long-term electrical stability measurements, including current/bias stress and aging over 18 months of idle shelf life are presented for GIZO-based TFTs. The effects of oxygen partial pressure, annealing temperature and passivation are discussed. Optimized devices show highly stable properties, such as a recoverable ΔVT<0.5 V after 24h of 1D=10 μA stress, quite promising for integration in electronic circuits.

Long-term electrical stability measurements, including current/bias stress and aging over 18 months of idle shelf life are presented for GIZO-based TFTs. The effects of oxygen partial pressure, annealing temperature and passivation are discussed. Optimized devices show highly stable properties, such as a recoverable ΔV T<0.5 V after 24h of I D=10 μA stress, quite promising for integration in electronic circuits. © 2010 SID.

Thin-films of copper oxide Cu x were sputtered from a metallic copper (Cu) target and studied as a function of oxygen partial pressure. A metallic Cu film with cubic structure obtained from 0% O PP has been transformed to cubic Cu x phase for the increase in O PP to 9% but then changed to monoclinic CuO phase (for. The variation in crystallite size (calculated from x-ray diffraction data) was further substantiated by the variation in grain size (surface microstructures). The Cu x films produced with O PP ranging between 9% and 75% showed p-type behavior, which were successfully applied to produce thin-film transistors. © 2006 IEEE.

Thin-films of copper oxide Cu O were produced by thermal oxidation of metallic copper (Cu) at different temperatures (150-450 C). The films produced at temperatures of 200, 250 and 300 C showed high Hall motilities of 2.2, 1.9 and 1.6 cm V s , respectively. Single Cu O phases were obtained at 200 C and its conversion to CuO starts at 250 C. For lower thicknesses 40 nm, the films oxidized at 250 C showed a complete conversion to CuO phase. Successful thin-film transistors (TFTs) were produce by thermal oxidation of a 20 nm Cu film, obtaining p-type Cu O (at 200 C) and CuO (at 250 C) with On/Off ratios of 6 10 and 1 10 , respectively. © 2005-2012 IEEE.

P-type thin-film transistors (TFTs) using room temperature sputtered tin and copper oxide as a transparent oxide semiconductor have been produced on rigid and paper substrates. The SnO x films shows p-type conduction presenting a polycrystalline structure composed with a mixture of tetragonal β-Sn and α-SnO x phases, after annealing at 200°C. These films exhibit a hole carrier concentration in the range of ≈ 10 16-10 18 cm -3, electrical resistivity between 101-102 Ωcm, Hall mobility of 4.8 cm 2/Vs, optical band gap of 2.8 eV and average transmittance ≈ 85 % (400 to 2000 nm). Concerning copper oxide Cu xO thin films they exhibit a polycrystalline structure with a strongest orientation along (111) plane. The Cu xO films produced between an oxygen partial pressure of 9 to 75% showed p-type behavior, as it was measured by Hall effect and Seebeck measurements. The bottom gate p-type SnO x TFTs present field-effect mobility above 1.24 cm 2/Vs (including the paper p-type oxide TFT) and an on/off modulation ratio of 10 3 while the Cu xO TFTs exhibit a field-effect mobility of 1.3×10 -3 cm 2/Vs and an on/off ratio of 2×10 2. © 2012 Copyright Society of Photo-Optical Instrumentation Engineers (SPIE).

The aim of this research is to study the role of concentration variations on precursor solution of nitrogen doped ZnO (ZnO:N) thin films which has been prepared by spray pyrolysis technique. SEM micrographs show that ZnO:N films in 0.1 ML concentration have a mono-disperse surface with nano-spheres of 50 nm in diameter. In higher molarities the nano-spheres agglomerate leading to particle formation. For 0.4 ML concentrations this change is observed, where plume like particles are seen over the surface of ZnO:N thin film. This change corresponds also to changes observed in the XRD spectra, where crystal orientation of ZnO:N thin films changes from (002) to (100). All of the ZnO:N thin films have kept their sharp ultra violet absorption edge, but the transparency in visible spectra region decreases as the molarities in precursor solution increase. Photoluminescence spectra at room temperature revealed emissions at 2.33 eV, 2.54 eV and 3.16 eV that can be attributed to the presence of nitrogen in ZnO structure. We also observe that all samples analyzed show a p-type Hall effect behavior, and that as the molarities in the precursor solution increase, the electrical resistivity of the films decreases, due to an enhancement of free carriers, while the mobility decreases. These data prove the capability of spray pyrolysis as a viable technique in preparing p-type TCO materials and so, fully transparent CMOS-like devices. © 2009 Elsevier B.V. All rights reserved.

In this paper we report results concerning the use of paper as substrate and as an electronic component for the next generation of sustainable low cost electronic systems, where different examples of applications are given. © 2013 Society for Information Display.

In this paper we report the use of a sheet of cellulose fiber-based paper as the dielectric layer used in oxide based semiconductor thin film field-effect transistors (FETs). In this new approach we are using the cellulose fiber-based paper in an "interstate" structure since the device is build on both sides of the cellulose sheet. Such hybrid FETs present excellent operating characteristics such as high channel saturation mobility (>30 cm 2/Vs), drain-source current on/off modulation ratio of approximately 104, near-zero threshold voltage, enhancement n-type operation and sub-threshold gate voltage swing of 0.8 V/decade. The cellulose fiber-based paper FETs characteristics have been measured in air ambient conditions and present good stability. The obtained results outpace those of amorphous Si TFTs and rival with the same oxide based TFTs produced on either glass or crystalline silicon substrates. The compatibility of these devices with large-scale/large-area deposition techniques and low cost substrates as well as their very low operating bias delineates this as a promising approach to attain high-performance disposable electronics like paper displays, smart labels, smart packaging, RFID and point-of-care systems for self analysis in bio-applications, among others. © 2009 SPIE.

To determine self-consistently the time evolution of particle size and their number density in situ multi-angle polarization-sensitive laser light scattering was used. Cross-polarization intensities (incident and scattered light intensities with opposite polarization) measured at 135° and ex situ transmission electronic microscopy analysis demonstrate the existence of nonspherical agglomerates during the early phase of agglomeration. Later in the particle time development both techniques reveal spherical particles again. The presence of strong cross-polarization intensities is accompanied by low-frequency instabilities detected on the scattered light intensities and plasma emission. It is found that the particle radius and particle number density during the agglomeration phase can be well described by the Brownian free molecule coagulation model. Application of this neutral particle coagulation model is justified by calculation of the particle charge whereby it is shown that particles of a few tens of nanometer can be considered as neutral under our experimental conditions. The measured particle dispersion can be well described by a Brownian free molecule coagulation model including a log-normal particle size distribution. © 1996 American Institute of Physics.

The first successful ablation of magnesium oxide through a home-made continuous-wave Cr:Nd:YAG ceramic solar laser is reported. A stationary heliostat-parabolic mirror solar energy collection and concentration system was used. A stable continuous-wave laser output power of 19.2 W was attained with laser beam brightness figure of merit 7.6 times higher than that of the previous scheme, enabling therefore the direct ablation of pure magnesium by our solar-pumped laser with only 1.6 m2 effective collection area. This could be an important step towards renewable magnesium production, offering multiple advantages, such as reducing agent avoidance, in relation to that of the previous Fresnel lens Cr:Nd:YAG continuous-wave solar laser system. © 2016 Elsevier B.V.

High performance transparent thin-film transistors deposited on glass substrates and entirely processed at a low temperature not exceeding 150°C are presented and analyzed in this paper. Besides being based on an amorphous oxide semiconductor, the main innovation of this work relies on the use of sputtered multicomponent oxides as dielectric materials based on mixtures of Ta2O5 with SiO2 or Al2O3. These multicomponent dielectrics allow to obtain amorphous structures and low leakage currents while preserving a high dielectric constant. This results in transistors with remarkable electrical properties, such as field-effect mobility exceeding 35 cm2 V-1 s-1, close to 0 V turn-on voltage, on/off ratio higher than 106, and a subthreshold slope of 0.24 V decade-1, obtained with a Ta2O5: SiO2 dielectric. When subjected to severe current stress tests, optimized devices show little and reversible variation in their electrical characteristics. The devices presented here have properties comparable to the ones using plasma-enhanced chemical vapor deposited SiO2 at 400°C, reinforcing the success of this amorphous multicomponent dielectric approach for low temperature, high performance, and transparent electronic circuits. © 2009 The Electrochemical Society.

Position sensitive detectors (PSD) using hydrogenated amorphous silicon as the active layer have been widely proposed either with the p-i-n or the Schottky structure. In this case, the devices are tailored to respond to light in the range 620-650 nm. Little is known about the use of silicon carbide active layers in such devices, which is important when the detected light is in the blue region of the light spectrum. In this paper we present for the first time the electro-optical properties of the a-Six:C1-x:H/Pd and p-ic-n PSD, using a-Six:C1-x:H layers deposited by plasma enhanced chemical vapour deposition (PECVD). These sensors are able to distinguish the wavelength of the impinging visible radiation (from red to blue light). In addition, the sensors respond to light intensities as lower as 1 × 10-6 W cm-2 with a resolution better than 0.04 mm and a linearity between ±0.12% and ±0.8%. © 2002 Elsevier Science B.V. All rights reserved.

This work refers to the main electro-optical characteristics exhibited by large area indium tin oxide films (300 × 400 mm) produced by r.f. magnetron sputtering under different oxygen concentrations and deposition pressures. Besides that, the ageing effect on the electro-optical characteristics of the films produced was also analyzed. The results achieved show that the film transparency and conductivity were highly improved (more than four orders of magnitude) by first annealing them in air at 470°C, followed by a reannealed stage under vacuum, in a hydrogen atmosphere, at 350°C. The ageing tests show that film degradation occurs when the films are produced at oxygen concentrations above 10% and/or at deposition pressures above 1.2 × 10-2 mbar. © 1999 Elsevier Science S.A. All rights reserved.

This work reports on the performances of undoped and doped amorphous/nanocrystalline silicon films grown by hot wire plasma assisted technique. The structure (including the presence of several nanoparticles with sizes ranging from 5 nm to 50 nm), composition (oxygen and hydrogen content) and transport properties of the films are highly dependent on the temperature of the filament and on the hydrogen dilution. The undoped films grown under low r.f. power (≈4mWcm-2) and filament temperatures around 1850 K present dark conductivities below 10-10 Scm-1, optical gaps of about 1.6 eV and photosensitivities above 105, (under AM 1.5 light intensities), with almost no traces of oxygen content. For the n- and the p-doped silicon films also fabricated under the same conditions the conductivities obtained are of about 10-2Scm-1 and 10-5Scm-1, respectively. © 1998 Elsevier Science Ltd. All rights reserved.

This paper presents the performances of an in-line plasma enhanced chemical vapor deposition system constituted by 5 chambers and one external unloaded chamber used in the simultaneous manufacturing of 4 large (30 cm × 40 cm) solar cells deposited on glass substrates. The system is fully automatically controlled by a Programmable Logic Controller using a specific developed software that allows devices mass production without losing the flexibility to perform process innovations according to the industrial requests, i.e. fast and secure changes and optimizations. Overall, the process shift is of about 15 min per each set of 4 solar cells. Without a buffer layer, solar cells with efficiencies of about 9% were produced by the proper tuning of the i-layer production conditions. © 2005 Elsevier B.V. All rights reserved.

The aim of this work is to determine the role of different metal contacts on the performances of one-dimensional thin-film position-sensitive detectors produced by plasma-enhanced chemical vapour deposition, to be used in optical rulers for alignment applications. The device consists on an indium tin oxide/p-i-n structure where the metal contacts used were based on Al, Al + Cu and Ag. The results achieved show that the contact mainly influences the final sensor range by limiting the magnitude of the analogue signals recorded. In spite of soldering problems the Al contact was the contact that lead to better discrimination of the sensor, with a nonlinearity of ±0.8% and a fall-off parameter of 3.2 × 10-3 cm-1. The Al + Cu contact also exhibits good performances (nonlinearity, of ±1.1%; fall-off parameter, 1.4 × 10-2 cm-1) and should be chosen since it is much easier to solder but requires protection against oxidation. The integration of these sensors on the optical ruler lead to the production of a system with a response time below 0.5 ms, an accuracy better than ±1% and a mechanical precision of better than 0.25 mm in 100 mm, with a full-scale noise below ±0.1%.

The search for new dielectric materials to be used in metal-insulator- semiconductor (MIS) structures to replace the silicon oxide (SiO2) has been growing up. The aim is to have materials with high dielectric constants that could allow the use of thicker films and so, to reduce the role of leakage currents that happens in devices using very thin SiO2 layers or to allow the MIS devices to support high currents, besides having a retain memory effect. In this work, we present data concerning the production of hafnium oxide (HfO2) thin films by radio frequency (rf) sputtering that present suitable characteristics to be used as a gate dielectric, taking advantage of its high dielectric constant and stoichiometry reached under certain deposition conditions. Data concerning the role of the deposition parameters in the films structure and in the electrical properties of the films produced using capacitance-voltage (C-V) and current-voltage (I-V) measurements will be shown, together with data concerning the degree of films' compactness measured by spectroscopic ellipsometry (SE). © 2003 Elsevier B.V. All rights reserved.

In this work, we report results concerning the performances of thin-film transistors (TFTs) where the channel layer is based on microcrystalline zinc tin oxide (ZTO) processed by spray pyrolysis technique. TFTs made with 30 nm thick ZTO channel layer deposited at a substrate temperature of 400 C and 300 Cexhibited, respectively, a saturation mobility of 2.9 cm V s and 1.45 cm V s ; voltage of 0.15 V, and 0.2 V; a sub-threshold swing of 400 mV/dec and 500 mV/dec; ON/OFF ratio at the onset of hard saturation current of 3.5 10 and 6 10 , for a drain to source voltage of 10 V (close to or below the gate to source voltage). This indicates that the substrate temperature is relevant in determining the devices' electronic performances. © 2013 IEEE.

This work reports on the performances of undoped and n doped amorphous/nano-crystalline silicon films grown by hot wire plasma assisted technique. The film's structure (including the presence of several nanoparticles with sizes ranging from 5 nm to 50 nm), the composition (oxygen and hydrogen content) and the transport properties are highly dependent on the filament temperature and on the hydrogen dilution. The undoped films grown under low r.f. power (≈4 mWcm-2) and with filament temperatures around 1850 °K have dark conductivities below 10-10 Scm-1, optical gaps of about 1.5 eV and photo-sensitivities above 105, (under AM1.5), with almost no traces of oxygen content. N-doped silicon films were also fabricated under the same conditions which attained conductivities of about 10-2 Scm-1.