In this work the electrical and structural properties of two high k materials as hafnium oxide (HfO2) and tantalum oxide (Ta2O5) produced at room temperature are exploited. Aiming low temperature processing two techniques were employed: r.f. sputtering and electron beam evaporation. The sputtered HfO2 films present a nanocrystalline structure when deposited at room temperature. The same does not happen for the evaporated films, which are essentially amorphous. The density and the electrical performance of both sputtered and evaporated films are improved after annealing them at 200 °C. On the other hand, the Ta2O5 samples deposited at room temperature are always amorphous, independently of the technique used. The density and electrical performance are not so sensitive to the annealing process. The set of data obtained show that these dielectrics processed at temperatures below 200 °C present promising properties aiming to produce devices at low temperature with improved interface properties and reduced leakage currents. © 2007 Elsevier B.V. All rights reserved.

Staggered bottom gate transparent thin film transistors (TTFTs) have been produced by rf magnetron sputtering at room temperature, using amorphous indium zinc oxide (IZO) semiconductor, for the channel as well as for the drain and source regions. The obtained TTFTs operate in the enhancement mode with threshold voltages of 2.4 V, saturation mobility of 22.7 cm2/V s, gate voltage swing of 0.44 V/dec and an ON/OFF current ratio of 7 × 107. The high performances presented by these TTFTs produced at room temperature, make these TFTs a promising candidate for flexible, wearable, disposable portable electronics as well as battery-powered applications. © 2007 Elsevier Ltd. All rights reserved.

High mobility bottom gate thin film transistors (TFTs) with an amorphous gallium tin zinc oxide (a-GSZO) channel layer have been produced by rf magnetron cosputtering using a gallium zinc oxide (GZO) and tin (Sn) targets. The effect of the post annealing temperatures (200 °C, 250 °C and 300 °C) was evaluated and compared with two series of TFTs produced at room temperature and 150 °C during the channel deposition. From the results it was observed that the effect ofpos annealing is crucial for both series of TFTs either for stability as well as for improving the electrical characteristics. The a-GSZO TFTs operate in the enhancement mode (n-type), present a high saturation mobility of 24.6 cm2/Vs, a subthreshold gate swing voltage of 0.38 V/decade, a turn-on voltage of -0.5 V, a threshold voltage of 4.6 V and an ION/IOFF ratio of 8x107, satisfying all the requirements to be used in active-matrix backplane.

High mobility bottom gate thin film transistors (TFTs) with an amorphous gallium tin zinc oxide (a-GSZO) channel layer have been produced by rf magnetron cosputtering using a gallium zinc oxide (GZO) and tin (Sn) targets. The effect of postannealing temperatures (200, 250, and 300 °C) was evaluated and compared with two series of TFTs produced at room temperature (S1) and 150 °C (S2) during the channel deposition. From the results, it was observed that the effect of postannealing is crucial for both series of TFTs either for stability as well as for improving the electrical characteristics. The a-GSZO TFTs (WL=5050 μm) operate in the enhancement mode (n -type), present a high saturation mobility of 24.6 cm2 V s, a subthreshold gate swing voltage of 0.38 V /decade, a turn-on voltage of -0.5 V, a threshold voltage of 4.6 V, and an Ion Ioff ratio of 8× 107, satisfying all the requirements to be used as active-matrix backplane. © 2008 American Institute of Physics.

Molybdenum doped indium oxide (IMO) thin films were deposited on the glass substrates preheated to 450 °C by spray pyrolysis technique. The Mo doping was varied between 0 and 2.0 at.%. The films were characterized by their structural, electrical and optical properties. The films are confirmed to be cubic bixbyite In2O3 with a strongest orientation along (222) plane, which is shifted to (400) plane for the increase in Mo doping to 1.25 and 2 at.%. The film deposited with 0.5 at.% Mo doping shows high mobility of 76.9 cm2V- 1s- 1 , resistivity of 1.8 × 10- 3 Ω-cm and high carrier concentration of 4.6 × 1019 cm- 3 with 81.3% transmittance in the visible range between 500 and 800 nm. Further, the transparency extents well into the near-IR range. © 2008 Elsevier B.V. All rights reserved.

In this letter, we report for the first time the use of a sheet of cellulose-fiber-based paper as the dielectric layer used in oxide-based semiconductor thin-film field-effect transistors (FETs). In this new approach, we are using the cellulose-fiber-based paper in an "interstrate"structure since the device is built on both sides of the cellulose sheet. Such hybrid FETs present excellent operating characteristics such as high channel saturation mobility (> 30 cm2Vs), drain-source current on/off modulation ratio of approximately 104, near-zero threshold voltage, enhancement n-type operation, and subthreshold gate voltage swing of 0.8 V/decade. The cellulose-fiber-based paper FETs' characteristics have been measured in air ambient conditions and present good stability, after two months of being processed. The obtained results outpace those of amorphous Si thin-film transistors (TFTs) and rival with the same oxide-based TFTs produced on either glass or crystalline silicon substrates. The compatibility of these devices with large-scale/large-area deposition techniques and low-cost substrates as well as their very low operating bias delineates this as a promising approach to attain high-performance disposable electronics like paper displays, smart labels, smart packaging, RFID, and point-of-care systems for self-analysis in bioapplications, among others. © 2008 IEEE.

Transparent and highly conducting gallium zinc oxide (GZO) films were successfully deposited by RF sputtering at room temperature. A lowest resistivity of∼2.8 × 10-4 ωcm was achieved for a film thickness of 1100nm (sheet resistance ∼2.5ω/□), with a Hall mobility of 18cm2/Vs and a carrier concentration of 1.3 × 1021 cm-3. The films are polycrystalline with a hexagonal structure having a strong crystallographic c-axis orientation. A linear dependence between the mobility and the crystallite size was obtained. The films are highly transparent (between 80% and 90% including the glass substrate) in the visible spectra with a refractive index of about 2, very similar to the value reported for the bulk material. These films were applied to single glass/TCO/pin hydrogenated amorphous silicon solar cells as front layer contact, leading to solar cells with efficiencies of about 9.52%. With the optimized deposition conditions, GZO films were also deposited on polymer (PEN) substrates and the obtained results are discussed. © 2008 Elsevier B.V. All rights reserved.

Recent fieldwork in the Namibe province in southern Angola yielded cranial and postcranial elements of at least two individuals of the rare and enigmatic mosasaur Halisaurus from a single small excavation. The genus Halisaurus is unique in retaining a primitive configuration of the temporal arcade, specifically a broad, vertically oriented contact between the parietal and the supratemporal. The supratemporal is broadly sutured to the opisthotic and prootic, unlike the condition in varanoids in which the simple lunate element lies between the parietal ramus and the squamosal and does not form a sutural contact with the opisthotic or prootic, but as in other halisaurines retains a plesiomorphic, vertically oriented contact with the parietal rami. The squamosal is lightly built and broadly arched as in Varanus. Comparison with known halisaurines indicates the new material is referable to the species Halisaurus arambourgi.
The locality that yielded the new specimens has also yielded a large number of isolated teeth, bones, articulated, and associated skeletons of Mosasaurus, Prognathodon, Globidens, and Plioplatecarpus, which with Halisaurus comprise a mosasaur assemblage most similar to that reported from the Maastrichtian of Morocco.

We extend a result of Bottcher and Silbermann on higher order asymptotics of determinants of block Toeplitz matrices with symbols in Wiener algebras with power weights to the case of Wiener algebras with general weights satisfying natural submultiplicativity, monotonicity, and regularity conditions.

Hydrogenated nanocrystalline silicon (nc-Si:H) n-layers have been used to prepare heterojunction solar cells on flat p-type crystalline silicon (c-Si) wafers. The nc-Si:H n-layers were deposited by radio-frequency (RF) plasma enhanced chemical vapor deposition (PECVD), and characterized using Raman spectroscopy, optical transmittance and activation energy of dark-conductivity. The nc-Si:H n-layers obtained comprise fine grained nanocrystallites embedded in amorphous matrix, which have a wider bandgap and a smaller activation energy. Heterojunction solar cells incorporated with the nc-Si n-layer were fabricated using configuration of Ag (100 nm)/lT0 (80 nm)/n-nc-Si:H (15 nm)/buffer a-Si:H/p-c-Si (300 μm)/Al (200 nm), where a very thin intrinsic a-Si:H buffer layer was used to passivate the p-c-Si surface, followed by a hydrogen plasma treatment prior to the deposition of the thin nanocrystalline layer. The results show that heterojunction solar cells subjected to these surface treatments exhibit a remarkable increase in the efficiency, up to 14.1% on an area of 2.43 cm2. © 2006 Elsevier B.V. All rights reserved.

In this paper we present results of indium zinc oxide deposited at room temperature by rf magnetron sputtering, with an electron mobility as high as 60 cm2/Vs. The films present a resistivity as low as 5 × 10 - 4 Ω cm with an optical transmittance of 85%. The structure of these films seems to be polymorphous (mix of different amorphous and nanocrystalline phases from different origins) as detected from XRD patterns with a smooth surface and from SEM micrographs, is highly important to ensure a long lifetime when used in display devices. © 2005 Elsevier B.V. All rights reserved.

A wide bandgap and highly conductive p-type hydrogenated nanocrystalline silicon (nc-Si:H) window layer was prepared with a conventional RF-PECVD system under large H dilution condition, moderate power density, high pressure and low substrate temperature. The optoelectrical and structural properties of this novel material have been investigated by Raman and UV-VIS transmission spectroscopy measurements indicating that these films are composed of nanocrystallites embedded in amorphous SiHx matrix and with a widened bandgap. The observed downshift of the optical phonon Raman spectra (514.4 cm-1) from crystalline Si peak (521 cm-1) and the widening of the bandgap indicate a quantum confinement effect from the Si nanocrystallites. By using this kind of p-layer, a-Si:H solar cells on bare stainless steel foil in nip sequence have been successfully prepared with a Voc of 0.90 V, a fill factor of 0.70 and an efficiency of 9.0%, respectively. © 2006 Elsevier B.V. All rights reserved.

Hydrogenated silicon carbon nitride (SiCN:H) thin film alloys were produced by hot wire (HWCVD), plasma assisted hot wire (PA-HWCVD) and plasma enhanced chemical vapor (PECVD) deposition techniques using a Ni buffer layer as catalyst for inducing crystallization. The silicon carbon nitride films were grown using C2H4, SiH4 and NH3 gas mixtures and a deposition temperature of 300 °C. Prior to the deposition of the SiCN:H film a hydrogen etching of 10 min was performed in order to etch the catalyst material and to facilitate the crystallization. We report the influence of each deposition process on compositional, structural and morphological properties of the films. Scanning Electron Microscope-SEM and Atomic Force Measurement-AFM images show their morphology; the chemical composition was obtained by Rutherford Backscattering Spectrometry-RBS, Elastic Recoil Detection-ERD and the structure by Infrared-IR analysis. The thickness of the catalyst material determines the growth process and whether or not islands form. The production of micro-structured SiCN:H films is also dependent on the gas pressure, gas mixture and deposition process used. © 2006 Elsevier B.V. All rights reserved.