In this paper we present the first results of thin film transistors produced completely at room temperature using ZnO as the active channel and silicon oxynitride as the gate dielectric. The ZnO-based thin film transistors (ZnO-TFT) present an average optical transmission (including the glass substrate) of 84% in the visible part of the spectrum. The ZnO-TFT operates in the enhancement mode with a threshold voltage of 1.8 V. A field effect mobility of 70 cm2/Vs, a gate voltage swing of 0.68 V/decade and an on-off ratio of 5×105 were obtained. The combination of transparency, high field-effect mobility and room temperature processing makes the ZnO-TFT very promising for the next generation of invisible and flexible electronics. © 2004 Elsevier B.V. All rights reserved.

In this paper we present results of indium doped zinc oxide deposited at room temperature by rf magnetron sputtering, with electron mobility as high as 60 cm2/Vs. The films present a resistivity as low as 5×10 -4 Ωcm with an optical transmittance of 85%. The structure of these films look-like polymorphous (mixed of different amorphous and nanocrystalline phases from different origins) as detected from XRD patterns (no clear peak exists) with a high smooth surface, as detected from SEM micrographs, highly important to ensure long life time when used in display devices.

Transparent and highly conducting gallium-doped zinc oxide films were successfully deposited by rf sputtering at room temperature. The lowest resistivity achieved was 2.6×10-4 Ω cm for a thickness of 1100 nm (sheet resistance ≈1.6 Ω/sq), with a Hall mobility of 18 cm2/Vs and a carrier concentration of 1.3×1021 cm-3. The films are polycrystalline with a hexagonal structure and a strongly preferred orientation along the c-axis. A linear dependence between the mobility and the crystallite size was obtained. The films present a transmittance in the visible spectra between 80 and 90% and a refractive index of approximately 2, which is very close to the value reported for bulk material. © 2003 Elsevier B.V. All rights reserved.

The hybrid-{T}refftz displacement element is applied to the elastodynamic analysis of bounded and unbounded media in the frequency domain. The displacements are approximated in the domain of the element using local solutions of the wave equation, the Neumann conditions are enforced directly and the surface forces are approximated on the Dirichlet and inter-element boundaries of the finite element mesh. Two alternative elements are developed to model unbounded media, namely a finite element with absorbing boundaries and an unbounded element that satisfies explicitly the Sommerfeld condition. The finite element equations are derived from the fundamental relations of elastodynamics written in the frequency domain. The numerical implementation of these equations is discussed and numerical tests are presented to assess the performance of the formulation.

In this letter we compare the room temperature ozone sensing properties of intrinsic zinc oxide (ZnO) thin films deposited by spray pyrolysis, dc and r.f. magnetron sputtering. Their sensor response exceeds 8 orders of magnitude when the film structure is constituted by nanocrystallites. These preliminary results clearly demonstrate that the films could be potentially used for ozone detection at room temperature.

This work presents the I-V results of a-Si:H/SiOx/Pd MIS (metal-insulator-semiconductor) structures. The a-Si:H was deposited by non-conventional modified triode PECVD. This new configuration allows the deposition of high quality a-Si:H with a photosensitivity of 106, indicating the presence of low density of defects. Spectroscopic ellipsometry measurements revealed that these films are highly dense and present a very smooth surface so allowing a low defect interface between the Pd and the a-Si:H. As a result, we could make MIS photodiodes with barrier heights of 1.17 eV, which give a high reduction of the reverse dark current, an increase of the signal to noise ratio of 106 and an open circuit voltage VOC = 0.5 V. © 2002 Elsevier Science B.V. All rights reserved.

Transparent conducting ZnO:Al thin films have been deposited on polyester (Mylar type D, 100 μm thickness) substrates at room temperature by r.f. magnetron sputtering. The structural, optical and electrical properties of the deposited films have been studied. The samples are polycrystalline with a hexagonal wurtzite structure and a strong crystallographic c-axis orientation (002) perpendicular to the substrate surface. As deposited ZnO:Al thin films have an 85% transmittance in the visible and infra-red region and a resistivity as low as 3.6×10-2 Ωcm. The obtained results are comparable to those ones obtained on glass substrates, opening a new field for low cost, light weight, small volume, flexible and unbreakable large area optoelectronic devices.

We have produced amorphous intrinsic silicon thin films by hot-wire plasma assisted chemical vapor deposition, a process that combines the traditional rf plasma and the recent hot-wire techniques. In this work we have studied the influence of hydrogen gas dilution and rf power on the surface morphology, composition, structure and electro-optical properties of these films. The results show that by using this deposition technique it is possible to obtain at moderate rf power and filament temperature, compact i-type silicon films with ημτ of the order of 10 -5cm 2V -1, without hydrogen dilution. © 2002 American Institute of Physics.