Rodrigo Martins

Transparent and highly conducting gallium-doped zinc oxide films were successfully deposited by rf sputtering at room temperature. The lowest resistivity achieved was 2.6×10-4 Ω cm for a thickness of 1100 nm (sheet resistance ≈1.6 Ω/sq), with a Hall mobility of 18 cm2/Vs and a carrier concentration of 1.3×1021 cm-3. The films are polycrystalline with a hexagonal structure and a strongly preferred orientation along the c-axis. A linear dependence between the mobility and the crystallite size was obtained. The films present a transmittance in the visible spectra between 80 and 90% and a refractive index of approximately 2, which is very close to the value reported for bulk material. © 2003 Elsevier B.V. All rights reserved.

This work presents the I-V results of a-Si:H/SiOx/Pd MIS (metal-insulator-semiconductor) structures. The a-Si:H was deposited by non-conventional modified triode PECVD. This new configuration allows the deposition of high quality a-Si:H with a photosensitivity of 106, indicating the presence of low density of defects. Spectroscopic ellipsometry measurements revealed that these films are highly dense and present a very smooth surface so allowing a low defect interface between the Pd and the a-Si:H. As a result, we could make MIS photodiodes with barrier heights of 1.17 eV, which give a high reduction of the reverse dark current, an increase of the signal to noise ratio of 106 and an open circuit voltage VOC = 0.5 V. © 2002 Elsevier Science B.V. All rights reserved.

Molybdenum-doped indium oxide (IMO) thin films were deposited at 450 °C for varying molybdenum concentrations in the range of 0.5-2 at% by the spray pyrolysis technique. These films confirmed the cubic bixbyite structure of polycrystalline In2O3. The preferred growth orientation along the (2 2 2) plane shifts to (4 0 0) on higher Mo doping levels. The films doped with 0.5 at% Mo showed high mobility of 76.9 cm2/(V s). The high visible transmittance extends well into the near-infrared region. A possibility of using the produced IMO films in nanocrystalline (nc) silicon solar cell applications is discussed in this article. The morphological studies showed a change in the microstructure, which is consistent with the change in crystallographic orientation. © 2008 Elsevier B.V. All rights reserved.

Molybdenum (0-1 at. %) doped indium oxide thin films with high near-infrared (NIR) transparency and high carrier mobility were deposited on Corning-1737 glass substrates at 400 °C by a spray pyrolysis experimental technique. X-ray diffraction (XRD) analysis confirmed the cubic bixbyite structure of indium oxide. The preferred growth orientation along the (222) plane for the low Mo doping level (0.5 at. %) shifts to (400) for higher Mo doping levels (<0.6 at. %). The crystallite size extracted from the XRD data corroborates the changes in full width at half maximum due to the variation in Mo doping. A scanning electron microscopy study illustrated the evolution in the surface microstructure as a function of Mo doping. The negative sign of the Hall coefficient confirmed the n -type conductivity. A high carrier mobility of ∼122.4 cm2 /V s, a carrier concentration of ∼9.5× 1019 cm-3, a resistivity of ∼5.3× 10-4cm, and a high figure of merit of ∼4.2× 10-2 -1 are observed for the films deposited with 0.5 at. % Mo. The obtained high average transparency of ∼83% in the wavelengths ranging from 400 to 2500 nm confirmed the extension of transmittance well into the NIR region. © 2009 American Institute of Physics.

In this paper we present results of indium doped zinc oxide deposited at room temperature by rf magnetron sputtering, with electron mobility as high as 60 cm2/Vs. The films present a resistivity as low as 5×10 -4 Ωcm with an optical transmittance of 85%. The structure of these films look-like polymorphous (mixed of different amorphous and nanocrystalline phases from different origins) as detected from XRD patterns (no clear peak exists) with a high smooth surface, as detected from SEM micrographs, highly important to ensure long life time when used in display devices.

High mobility bottom gate thin film transistors (TFTs) with an amorphous gallium tin zinc oxide (a-GSZO) channel layer have been produced by rf magnetron cosputtering using a gallium zinc oxide (GZO) and tin (Sn) targets. The effect of postannealing temperatures (200, 250, and 300 °C) was evaluated and compared with two series of TFTs produced at room temperature (S1) and 150 °C (S2) during the channel deposition. From the results, it was observed that the effect of postannealing is crucial for both series of TFTs either for stability as well as for improving the electrical characteristics. The a-GSZO TFTs (WL=5050 μm) operate in the enhancement mode (n -type), present a high saturation mobility of 24.6 cm2 V s, a subthreshold gate swing voltage of 0.38 V /decade, a turn-on voltage of -0.5 V, a threshold voltage of 4.6 V, and an Ion Ioff ratio of 8× 107, satisfying all the requirements to be used as active-matrix backplane. © 2008 American Institute of Physics.

High mobility bottom gate thin film transistors (TFTs) with an amorphous gallium tin zinc oxide (a-GSZO) channel layer have been produced by rf magnetron cosputtering using a gallium zinc oxide (GZO) and tin (Sn) targets. The effect of the post annealing temperatures (200 °C, 250 °C and 300 °C) was evaluated and compared with two series of TFTs produced at room temperature and 150 °C during the channel deposition. From the results it was observed that the effect ofpos annealing is crucial for both series of TFTs either for stability as well as for improving the electrical characteristics. The a-GSZO TFTs operate in the enhancement mode (n-type), present a high saturation mobility of 24.6 cm2/Vs, a subthreshold gate swing voltage of 0.38 V/decade, a turn-on voltage of -0.5 V, a threshold voltage of 4.6 V and an ION/IOFF ratio of 8x107, satisfying all the requirements to be used in active-matrix backplane.

This paper deals with high transparent and high conductive oxides based on polycrystalline titanium (Ti) doped (0.5-3 at.%) indium oxide (IO) thin films produced on glass substrates at 400 °C by spray pyrolysis technique. X-ray diffraction analysis confirmed the cubic bixbyite structure of indium oxide. A high mobility of ∼ 97 cm2 V- 1 s- 1, a carrier concentration of ∼ 1.55 × 1020 cm- 3 and a resistivity of ∼ 4.11 × 10- 4 Ω-cm with ∼ 83% of transmittance in the wavelength ranging between 400 and 2500 nm were obtained for 2 at.% Ti doping films, rivalling so to the best known transparent conducting oxide based on indium tin oxide. Moreover, the transmittance in the broad wavelength ranging between 400 and 2500 nm is over 83%, leading so to an increasing carrier generation towards the near infrared region of the spectrum, as required for applications such as solar cells. We also notice that increasing the doping concentration widened the optical band gap and caused a small Burstein-Moss shift, due to mobility decrease, as expected. © 2012 Published by Elsevier B.V.

Staggered bottom gate transparent thin film transistors (TTFTs) have been produced by rf magnetron sputtering at room temperature, using amorphous indium zinc oxide (IZO) semiconductor, for the channel as well as for the drain and source regions. The obtained TTFTs operate in the enhancement mode with threshold voltages of 2.4 V, saturation mobility of 22.7 cm2/V s, gate voltage swing of 0.44 V/dec and an ON/OFF current ratio of 7 × 107. The high performances presented by these TTFTs produced at room temperature, make these TFTs a promising candidate for flexible, wearable, disposable portable electronics as well as battery-powered applications. © 2007 Elsevier Ltd. All rights reserved.

In this paper we present results of indium zinc oxide deposited at room temperature by rf magnetron sputtering, with an electron mobility as high as 60 cm2/Vs. The films present a resistivity as low as 5 × 10 - 4 Ω cm with an optical transmittance of 85%. The structure of these films seems to be polymorphous (mix of different amorphous and nanocrystalline phases from different origins) as detected from XRD patterns with a smooth surface and from SEM micrographs, is highly important to ensure a long lifetime when used in display devices. © 2005 Elsevier B.V. All rights reserved.

The effect of oxygen partial pressure on the properties of In2 O3 - Ga2 O3 thin films produced by sputtering at room temperature aimed at thin film transistor (TFT) application is reported in this work. When produced in the absence of oxygen, the films are polycrystalline, while in the presence of oxygen, the films are amorphous. The films' resistivity is tuned between 10-3 and 104 γ cm. Moreover, the films present a high transmittance (> 80%) and a smooth surface (rrms =1.2 nm). The high performance as-produced transistors present high saturation mobility (μsat ≈43 cm2 /V s) and a subthreshold gate-voltage swing of 0.51 V/dec, which is reduced to 0.27 V/dec after 150°C annealing. © 2009 The Electrochemical Society.

In this work the electrical and structural properties of two high k materials as hafnium oxide (HfO2) and tantalum oxide (Ta2O5) produced at room temperature are exploited. Aiming low temperature processing two techniques were employed: r.f. sputtering and electron beam evaporation. The sputtered HfO2 films present a nanocrystalline structure when deposited at room temperature. The same does not happen for the evaporated films, which are essentially amorphous. The density and the electrical performance of both sputtered and evaporated films are improved after annealing them at 200 °C. On the other hand, the Ta2O5 samples deposited at room temperature are always amorphous, independently of the technique used. The density and electrical performance are not so sensitive to the annealing process. The set of data obtained show that these dielectrics processed at temperatures below 200 °C present promising properties aiming to produce devices at low temperature with improved interface properties and reduced leakage currents. © 2007 Elsevier B.V. All rights reserved.

In this paper we present the first results of thin film transistors produced completely at room temperature using ZnO as the active channel and silicon oxynitride as the gate dielectric. The ZnO-based thin film transistors (ZnO-TFT) present an average optical transmission (including the glass substrate) of 84% in the visible part of the spectrum. The ZnO-TFT operates in the enhancement mode with a threshold voltage of 1.8 V. A field effect mobility of 70 cm2/Vs, a gate voltage swing of 0.68 V/decade and an on-off ratio of 5×105 were obtained. The combination of transparency, high field-effect mobility and room temperature processing makes the ZnO-TFT very promising for the next generation of invisible and flexible electronics. © 2004 Elsevier B.V. All rights reserved.

Hydrogenated nanocrystalline silicon (nc-Si:H) n-layers have been used to prepare heterojunction solar cells on flat p-type crystalline silicon (c-Si) wafers. The nc-Si:H n-layers were deposited by radio-frequency (RF) plasma enhanced chemical vapor deposition (PECVD), and characterized using Raman spectroscopy, optical transmittance and activation energy of dark-conductivity. The nc-Si:H n-layers obtained comprise fine grained nanocrystallites embedded in amorphous matrix, which have a wider bandgap and a smaller activation energy. Heterojunction solar cells incorporated with the nc-Si n-layer were fabricated using configuration of Ag (100 nm)/lT0 (80 nm)/n-nc-Si:H (15 nm)/buffer a-Si:H/p-c-Si (300 μm)/Al (200 nm), where a very thin intrinsic a-Si:H buffer layer was used to passivate the p-c-Si surface, followed by a hydrogen plasma treatment prior to the deposition of the thin nanocrystalline layer. The results show that heterojunction solar cells subjected to these surface treatments exhibit a remarkable increase in the efficiency, up to 14.1% on an area of 2.43 cm2. © 2006 Elsevier B.V. All rights reserved.