Rodrigo Martins

In this paper the influence of the DC grid bias on the plasma impedance and the I-V behaviour of silane plasmas used to grow undoped amorphous silicon films by plasma enhanced chemical vapour deposition technique using a triode configuration at or close to the powder regime is studied. The aim is to determine the correlation between the r.f. power and the DC grid voltage with the plasma parameters, under isothermal gas conditions. The results should lead to the production of nanostructured films, with the required optoelectronic characteristics for photovoltaic applications. The results achieved show the existence of a boundary region close to the γ-regime (powder formed) where nanoparticles can be formed by moderated ion bombardment of the growing surface. This is characterised by the plasma resistance of the same order of magnitude of the plasma reactance. Under this condition, it is possible to grow amorphous silicon films that can incorporate nanoparticles, exhibiting photosensitivities of about 107 (two orders of magnitude larger than the one exhibited by films grown under conventional conditions) with densities of states determined by the constant photocurrent method below 3 × 1015 cm3. Apart from that, the growth of the films is less affected by light soaking than the conventional films grown by standard techniques. © 2001 Elsevier Science Ltd. All rights reserved.

This paper presents the process conditions that lead to the production of nanostructured silicon films grown by plasma enhanced chemical vapour deposition close to the so-called gamma regime (powder formation), highly dense and with low density of bulk states. Thus, the powder management is one important issue to be addressed in this paper. As a general rule we observed that high quality films (low density of states and high μτ products) are obtained when films are grown under low ion bombardment at high hydrogen dilution and deposition pressure conditions, to allow the proper surface passivation and surface activation.

This paper reports the performance of small area solar cells, 128 linear integrated position sensitive detector arrays and thin film transistors based on nanostructured silicon thin films produced by plasma-enhanced chemical vapour deposition technique, close to the onset of dusty plasma conditions, within the transition region from amorphous to microcrystalline. The small area solar cells, produced in a modified single chamber reactor, exhibited very good electrical characteristics with a conversion efficiency exceeding 9%. The 128 integrated position sensitive detector arrays, based on a similar pin structure, allow real-time 3D object imaging with a resolution higher than 90 l p/mm. The thin film transistors produced exhibited field effect mobility of 2.47 cm 2/V/s, threshold voltage of 2 V, on/off ratio larger than 10 7 and sub-threshold slopes of 0.32 V/decade, which are amongst the best results reported for this type of device. © 2009 Taylor & Francis.

This work focuses on the role of the native oxide layer (SiO2) on the nickel (Ni)-assisted crystallization of amorphous silicon (a-Si). In some samples, the native oxide was removed using a HF-diluted solution before Ni layers with 0.5 nm be deposited on a-Si. The results show that the presence of a thin SiO2 layer of about 3 nm between the a-Si and the Ni delays the crystallization process. Ellipsometry data show that, after annealing for 5 h at 500 °C, the HF-cleaned sample presents a crystalline fraction of 88%, while the one with the native oxide has only 35%. This difference disappears after 20 h where both samples present similar crystalline fraction. These facts are also reflected on the film's electrical properties, where the activation energy for samples annealed for 5 h rises from 0.42 eV to 0.55 eV, when the oxide layer is removed. After 20 h and 30 h, the activation energy is around 0.55 eV for both kinds of samples, meaning that films with similar electrical properties are now obtained. However, the XRD data suggest the presence of some structural differences attributed to slight differences on the crystallization process. © 2005 Elsevier B.V. All rights reserved.

Nanostructured silicon (na-Si:H) thin films were fabricated using plasma enhanced chemical vapour deposition (PECVD) technique under high silane hydrogen dilution and a discharge frequency of 27 MHz, where the substrate was located in the dark region of the plasma, protected by a grounded metal grid. By not exposing the growth surface directly to the plasma we avoid the silicon growth surface to sustain a high ion bombardment leading to a less defective surface and highly compact films. The intrinsic films grown under these conditions were used to produce the channel region of thin film transistors (TFTs) with a bottom gate staggered configuration, integrating different dielectric layers. The devices produced exhibit a field effect mobility close to 1.84 cm 2 V -1S -1, threshold voltage around 2 V, on/off ratio above 10 7 and sub-threshold slope below 0.5 V/decade, depending on the dielectric used. Copyright © 2010 American Scientific Publishers All rights reserved.

In this work, the optical and structural properties of high k materials such as tantalum oxide and titanium oxide were studied by spectroscopic ellipsometry, where a Tauc-Lorentz dispersion model based in one (amorphous films) or two oscillators (microcrystalline films) was used. The samples were deposited at room temperature by radio frequency magnetron sputtering and then annealed at temperatures from 100 to 500 °C. Concerning the tantalum oxide films, the increase of the annealing temperature, up to 500 °C does not change the amorphous nature of the films, increasing, however, their density. The same does not happen with the titanium oxide films that are microcrystalline, even when deposited at room temperature. Data concerning the use of a four-layer model based on one and two Tauc-Lorentz dispersions is also discussed, emphasizing its use for the detection of an amorphous incubation layer, normally present on microcrystalline films grown by sputtering. © 2006 Elsevier B.V. All rights reserved.

In this work, we investigate the role of amorphous silicon (a-Si:H) thin films deposited by a plasma enhanced chemical vapor deposition (PECVD) technique on porous silicon (PS) to facilitate its water vapor and oxygen gas sensing properties using its electrical response. Overall we notice a rectifying behavior from a-Si:H/PS heterojunction device, where a current enhancement of one and four orders of magnitude was observed in the presence of oxygen gas and water vapor, in comparison with atmospheric air at room temperature, respectively. The photoluminescence (PL) investigation of PS shows a slight blue shift in the PL emission band from 1.72 to 1.77 eV and the intensity of the PL is enhanced by a factor of 5.4 with increase of porosity from 21% to 77%. This PL emission may originate from the O-Si-H related absorbance bands. Alternatively, quenching of the PL intensity was observed after a-Si:H films were deposited on PS specimens. Besides, micro-Raman and atomic force microscopic (AFM) analyse were carried out to understand the structure and morphological features of the PS and a-Si:H/PS specimens. © 2007 Elsevier B.V. All rights reserved.

Total hip replacement is a common practice in every day clinical work. Artificial hip implants consist of a femoral component and an acetabular component. Nowadays the acetabular component is composed of a polymeric cup and a metallic shell. This study focuses the development of an innovative acetabular component substituting the metallic shell by a multilayer coating on the acetabular cup. A titanium coating was deposited onto ultra-high molecular weight polyethylene (UHMWPE) samples by physical vapour deposition (PVD), having an in situ pre-treatment with argon ion bombardment in order to optimize the adhesive strength by surface modification, followed by the deposition of a thin film of hydroxyapatite (HA) using rf magnetron sputtering technique, at room temperature. Results obtained seem to indicate that these multilayer coatings can be a viable alternative to the metallic shell, leading to the substitution of a two part for a one part acetabular component.

The aim of this paper is to present a set of electric data concerning the performances before and after ageing of Cu-Sn-Cu joins used to solder power diodes and to compare the results achieved with the ones obtained in diodes soldered using the conventional technology. The set of results achieved show that the Cu-Sn-Cu joins present even better performances than the ones exhibited by diodes soldered using the conventional technology, without requiring the use of Mo discs to be inserted between the silicon crystal and the metal contacts (stud or finger) to compensate thermal mismatches.

Here we describe an innovative optoelectronic platform which enables the specific detection of unamplified nucleic acid sequences with the integration of oligonucleotide-derivatized gold nanoparticles, a colour sensor and a light emission source for a colorimetric detection method. This new low cost, fast and simple optoelectronic platform permits detection of less than 1 picomole quantities of nucleic acid without target or signal amplification. ©2007 IEEE.