Rodrigo Martins

In this study, amorphous indium-tungsten oxide (IWO) semiconductor thin films were prepared by an eco-friendly spin-coating process using ethanol and water as solvents. The electrical properties of IWO thin-film transistors (TFTs), together with the structural and morphological characteristics of IWO thin films, were systematically investigated as functions of tungsten concentration and annealing temperature. The optimized IWO channel layer was then integrated on an aqueous aluminum oxide (AlOx) gate dielectric. It is observed that the solution-processed IWO/AlOx TFT presents high stability and improved characteristics, such as an on/off current ratio of 5 × 107, a field-effect mobility of 15.3 cm2 V-1 s-1, a small subthreshold slope of 68 mV dec-1, and a threshold voltage shift of 0.15 V under bias stress for 2 h. The IWO/AlOx TFT could be operated at a low voltage of 2 V, which was 15 times lower than that of conventional SiO2-based devices. The solution-processed IWO thin films synthesized in a green route would be promising candidates for large-area and high-performance low-cost devices. © The Royal Society of Chemistry 2016.

Abstract: The present work reports the synthesis of zinc oxide (ZnO) nanoparticles with hexagonal wurtzite structure considering a solvothermal method assisted by microwave radiation and using different solvents: water (H2O), 2-ethoxyethanol (ET) and ethylene glycol (EG). The structural characterization of the produced ZnO nanoparticles has been accessed by scanning electron microscopy, X-ray diffraction, room-temperature photoluminescence and Raman spectroscopies. Different morphologies have been obtained with the solvents tested. Both H2O and ET resulted in rods with high aspect ratio, while EG leads to flower-like structure. The UV absorption spectra showed peaks with an orange shift for synthesis with H2O and ET and blue shift for synthesis with EG. The different synthesized nanostructures were tested for photocatalyst applications, revealing that the ZnO nanoparticles produced with ET degrade faster the molecule used as model dye pollutant, i.e. methylene blue. Graphical Abstract: [Figure not available: see fulltext.] © 2015 Springer Science+Business Media New York

When thinking on low cost and sustainable electronic systems, paper can be considered as an interesting option to be used as substrate but also as a component of such systems. In this work we have tailored paper samples that were used simultaneously as physical support and dielectric in oxide based paper field effect transistors (FETs). It was observed that the gate leakage current in these devices depends directly from fibril's dimension and arrangement, being lower for micro/nano fibrillated cellulose paper. Moreover, extra ionic charge added to the paper during its production results in the improvement of FETs' electrical properties, with saturation mobility of 16 cm 2V -1s -1 and on/off current ratio close to 105. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

The aim of this study was to investigate the influence of ultrasound and high-shear mixing on the properties of microparticles obtained by spray congealing. Dispersions containing 10% carbamazepine and 90% carrier Gelucire® 50/13 (w/w) were prepared using magnetic stirring, high-shear mixing, or ultrasound. Each preparation was made using hot-melt mixing spray congealing to obtain the microparticles. All microparticles presented a spherical shape with high encapsulation efficiency (>99%). High-shear mixing and ultrasound promoted a decrease in the size of microparticles (D90) to 62.8 ± 4.1 μm and 64.9 ± 3.3 μm, respectively, while magnetic stirring produced microparticles with a size of 84.1 ± 1.4 μm. The use of ultrasound led to microparticles with increased moisture content as identified through sorption isotherm studies. In addition, rheograms showed distinct rheological behaviour among different dispersion preparations. Therefore, the technique used to prepare dispersions for spray congealing can affect specific characteristics of the microparticles and should be controlled during the preparation. © 2013 Informa UK Ltd. All rights reserved.

Nitrogen and Phosphorus co-doped (N+P)- zinc oxide (ZnO) films were RF sputtered on corning glass substrates at 350 °C and comparatively studied with undoped, N-, and P- doped ZnO. X-ray diffraction spectra confirmed that the ZnO structure with a preferred orientation along <002> direction. Scanning electron microscope analysis showed different microstructure for the N+P co-doping, and thus probably confirming the co-existence of both the dopants. X-ray photoelectron spectroscopy spectra revealed that the chemical composition in N+P co-doped ZnO are different from that found in undoped, N-, and P- doped ZnO. The atomic ratio of N and P in N+P co-doped ZnO is higher than that in single N or P doped ZnO. One broad ZnO emission peak around 420 nm is observed in photoluminescence spectra. The relative intensity of the strongest peak obtained from co-doped ZnO films is about twice than the P- doped and thrice than the pure and N- doped films. © (2013) Trans Tech Publications, Switzerland.

The effect of substrate temperature (Ts) on the properties of pyrolytically deposited nitrogen (N) doped zinc oxide (ZnO) thin films was investigated. The Ts was varied from 300 °C to 500 °C, with a step of 50 °C. The positive sign of Hall coefficient confirmed the p-type conductivity in the films deposited at 450 °C and 500 °C. X-ray diffraction studies confirmed the ZnO structure with a dominant peak from (1 0 0) crystal plane, irrespective of the variation in Ts. The presence of N in the ZnO structure was evidenced through X-ray photoelectron spectroscopy (XPS) analysis. The obtained high N concentration reveals that the 450 °C is the optimal Ts. Atomic force microscope (AFM) analysis showed that the surface roughness was increased with the increasing Ts until 400 °C but then decreased. It is found that the transmittance of the deposited films is increased with the increasing Ts. The optical band gap calculated from the absorption edge showed that the films deposited with T s of 300 °C and 350 °C possess higher values than those deposited at higher Ts. © 2012 Elsevier B.V.

We present the results obtained with an extended-gate ISFET totally based on amorphous oxides (GIZO as the semiconductor, +{\hbox{Ta}}-{2}{\hbox{O}}-{5}{\ hbox{:SiO}}-inf2-inf as the dielectric and +{\hbox{Ta}}-{2}{\hbox{O}}-inf5-inf as the sensitive layer). A full characterization of the device was performed with constant ionic strength pH buffer solutions, revealing a sensitivity of 40 mV/pH with small hysteresis, and good linearity in the pH 4-pH 10 range buffer solutions. These results clearly show that it is possible to produce room-temperature disposable and low cost bio-sensors. © 2005-2012 IEEE.

Thin films of (Ta 2O 5) 0.85(TiO 2) 0.15 were deposited on quartz and p-Si substrates by DC reactive magnetron sputtering at different substrate temperatures (T s) in the range 303 - 873 K. The films deposited at 303 0K were in the amorphous and it transformed to crystalline at substrate temperatures ≥ 573 0K. The crystallite size was increased from 50 nm to 72 nm with the increase of substrate temperature. The surface morphology was significantly influenced with the substrate temperature. After deposition of the (Ta 2O 5) 0.85(TiO 2) 0.15 films on Si, aluminium (Al) electrode was deposited to fabricate metal/oxide/semiconductor (MOS) capacitors with a configuration of Al/(Ta 2O 5) 0.85(TiO 2) 0.15/Si. A low leakage current of 7.7 × 10 -5 A/cm 2 was obtained from the films deposited at 303 K. The leakage current was decreased to 9.3 × 10 -8 A/cm 2 with the increase of substrate temperature owing to structural changes. The conduction mechanism of the Al/(Ta 2O 5) 0.85(TiO 2) 0.15/Si capacitors was analyzed and compared with mechanisms of Poole-Frenkel and Schottky emissions. The optical band gap (E g) was decreased from 4.45 eV to 4.38 eV with the increase in substrate temperature. © Published under licence by IOP Publishing Ltd.

Indium molybdenum oxide (IMO) thin films were radio-frequency (RF) sputtered at room temperature (RT) and studied as a function of base pressure (BP). The crystallinity of the films is decreased with the increase in BP. A maximum mobility (μ) of 49.6 cm 2 V -1 s -1 was obtained from the IMO films deposited at RT without any post-annealing treatment. The electronic behaviour of the deposited films was investigated by temperature-dependent (100-550 K) Hall measurements. Study on the scattering mechanisms based on the experimental data and theoretical models show that the ionized scattering centres are dominating. The films possess wide work function (4.91 eV) and high transmittance (> 70%) over visible and near infrared (NIR) range. The obtained results, especially the high work function and NIR transmittance, are very promising particularly in applications such as optical detectors and solar cells. Copyright © EPLA, 2012.

The influence of doping on the morphology, physical and electrical properties of zinc oxide produced by the sol-gel method was examined. Undoped zinc oxide was observed to form relatively porous films. Addition of an Al dopant influenced the sheet resistance, but did not result in a change in morphology, examined by atomic force microscopy when compared to undoped films. In the case of electrical measurements, undoped ZnO films were extremely resistive. A minimum dopant concentration of 2 at.%. Al was required to produce materials which were more conductive, as observed by sheet resistance measurements, which were shown to vary with annealing temperature. The versatile nature of sol-gel processing was demonstrated by selective ink-jet deposition of sol-gel droplets which were annealed to form oxide materials. © 2011 Elsevier B.V. All rights reserved.

The high visible-near infrared transparent and high carrier mobility (μ) Mo doped (0.5 at%) indium oxide (IMO) films were deposited by the spray pyrolysis technique. The deposited films were irradiated by 50MeV Li 3+ ions with different fluences of 1×1011, 1×1012 and 1×1013 ions cm-2. X-ray diffraction analysis confirmed the cubic bixbyite structure of indium oxide. A fascinating feature is that the ion irradiation process has introduced a fraction of the molybdenum oxide phase. The μ of as-deposited IMO films is decreased from ̃122.4 to 93.3 cm2 V-1 s-1, following the ion irradiation. The theoretically calculated μ and carrier density values were correlated with those measured experimentally. The transport mechanism has been analysed based on the ionized and neutral impurity scattering centres. The average transmittance (400-2500 nm) of the as-deposited IMO films is decreased from 83% to 60% following irradiation. © 2011 IOP Publishing Ltd.

Indium oxide thin films deposited by spray pyrolysis were irradiated by 100 MeV O7+ ions with different fluences of 5 × 1011, 1 × 1012 and 1 × 1013 ions/cm2. X-ray diffraction analysis confirmed the structure of indium oxide with cubic bixbyite. The strongest (2 2 2) orientation observed from the as-deposited films was shifted to (4 0 0) after irradiation. Furthermore, the intensity of the (4 0 0) orientation was decreased with increasing fluence together with an increase in (2 2 2) intensity. Films irradiated with maximum fluence exhibited an amorphous component. The mobility of the as-deposited indium oxide films was decreased from ∼78.9 to 43.0 cm2/V s, following irradiation. Films irradiated with a fluence of 5 × 1011 ions/cm2 showed a better combination of electrical properties, with a resistivity of 4.57 × 10-3 Ω cm, carrier concentration of 2.2 × 1019 cm-3 and mobility of 61.0 cm2/V s. The average transmittance obtained from the as-deposited films decreased from ∼81% to 72%, when irradiated with a fluence of 5 × 1011 ions/cm2. The surface microstructures confirmed that the irregularly shaped grains seen on the surface of the as-deposited films is modified as "radish-like" morphology when irradiated with a fluence of 5 × 1011 ions/cm2. © 2011 Elsevier B.V. All rights reserved.

Today there is a strong interest in the scientific and industrial community concerning the use of biopolymers for electronic applications, driven mainly by low-cost and disposable applications. Adding to this interest, we must recognise the importance of the dream of wireless auto-sustained and low-energy-consumption electronics. This dream can be fulfilled by cellulose paper, the lightest and the cheapest known substrate material, as well as the Earth's major biopolymer and of tremendous global economic importance. Most of the paper used up to now is optimised in terms of the required mechanical and physical properties to be used as the support of inks of different origins. In the future, specific electronic heterogeneous paper sheets should be fabricated aiming to get paper fibers with required bulk and surface functionalities, proper water/vapour barrier, size and diameter/thickness of the fibrils and full paper thickness. This will be the function of components/devices to be incorporated/integrated such as thin-film transistors, complementary metal oxide semiconductor devices, passive electronic components (resistances, inductors and capacitors), memory transistors, electrochromics and thin-film paper batteries. © 2011 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

In this paper, we report the environmental, optical, and gate bias stress stability of amorphous zinc-tin-oxide (ZTO) thin-film transistors (TFTs) fabricated by sol-gel spin-coating method. The ZTO TFTs showed excellent environmental and optical stability. The threshold voltage stability of ZTO TFTs was sensitive to both positive and negative gate bias stress. Maximum threshold voltage shifting of +1.9 and -3.2 V was observed under a gate bias stress of +10 and -10 V, respectively, with no significant change to subthreshold swing value. © 2006 IEEE.

Copper oxide thin films were obtained by annealing (temperature ranging between 100 and 450 °C) the metallic Cu films deposited on glass substrates by e-beam evaporation. XRD studies confirmed that the cubic Cu phase of the asdeposited films changes into single cubic Cu 2Ophase and single monoclinic CuO phase, depending on the annealing conditions. The crystallite size is varied betweeñ12 and 31 nm. The lattice parameters of cubic Cu and Cu 2Ophases are estimated tõ3.60 and ̃4.26 Å , respectively. The films with Cu 2O phase showed p-type characteristics. The conductivity is decreased linearly with the decreasing temperature (1/T), which has confirmed the semiconductor nature of the deposited films. The calculated activation energy is varied between 0.10 and 0.16 eV. The surface microstructure is changed depending on the variation in the annealing temperature. The poor transmittance of the asdeposited films (<1%) is increased to a maximum of ̃80% (800 nm) on annealing at 200 °C. The estimated direct allowed band gap is varied between 1.73 and 2.89 eV. © 2009 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

In this paper ageing effects of the solution used to prepare fluorine-doped ZnO films by the spray pyrolysis technique were investigated, concerning its role on the structure, the electrical and optical properties of films produced. The data reveal that the sheet resistance of the ZnO:F thin film decreases with the age of the solution used, reaching a minimum of 24 Ω/□, after 15 days. On the other hand the optical transmittance increases for films deposited using 6 days aging solution, decreasing afterwards as the aging time increases, being the optical transmittance in the visible range below 55%, for films deposited from solutions 36 days in age. The X-ray diffraction spectra show that the aged films are polycrystalline in nature with a [100] predominant orientation. The data also show that the intensity of (100) peak increases as the time of solution age increases, which is related to an improvement of the film crystallinity. © 2009 Elsevier B.V. All rights reserved.

Thin films of molybdenum doped indium oxide (IMO) were deposited on glass at room temperature using an in-built three-source RF magnetron sputtering. The films were studied as a function of oxygen volume percentage (O2 vol. %; ranging from 0.0 to 17.5%) in the sputtering chamber. The as-deposited amorphous films were crystallized on post-annealing. The as-deposited films are low conducting and Hall coefficients were undetectable; whereas post-annealed films possess fairly high conductivity. The lowest transmittance (11.96% at 600 nm) observed from the films deposited without oxygen increased to a maximum of 88.01% (3.5 O2 vol. %); whereas this transmittance was decreased with the increasing O2 vol. % to as low as 81.04% (15.6 O2 vol. %); a maximum of 89.80% was obtained from the films annealed at 500 °C in open air (3.5 O2 vol. %). The optical band gap of 3.80 eV obtained from the films deposited without oxygen increased with increasing O2 vol. % to as high as 3.91 eV (17.5 O2 vol. %). A maximum of 3.92 eV was obtained from the films annealed at 300 °C in N2:H2 gas atmosphere (17.5 O2 vol. %). © 2008 Elsevier Ltd. All rights reserved.

N-doped ZnO films were deposited by RF magnetron sputtering in N2/Ar gas mixture and were post-annealed at different temperatures (Ta) ranging from 400 to 800 °C in O2 gas at atmospheric pressure. The as-deposited and post-annealed films were characterized by their structural (XRD), compositional (SIMS, XPS), optical (UV-vis-NIR spectrometry), electrical (Hall measurements), and optoelectronic properties (PL spectra). The XRD results authenticate the improvement of crystallinity following post-annealing. The weak intensity of the (0 0 2) reflection obtained for the as-deposited N-doped ZnO films was increased with the increasing Ta to become the preferred orientation at higher Ta (800 °C). The amount of N-concentration and the chemical states of N element in ZnO films were changed with the Ta, especially above 400 °C. The average visible transmittance (400-800 nm) of the as-deposited films (26%) was increased with the increasing Ta to reach a maximum of 75% at 600 °C but then decreased. In the PL spectra, A0X emission at 3.321 eV was observed for Ta = 400 °C besides the main D0X emission. The intensity of the A0X emission was decreased with the increasing Ta whereas D0X emission became sharper and more optical emission centers were observed when Ta is increased above 400 °C. © 2008 Elsevier B.V. All rights reserved.

Indium molybdenum oxide thin films radio-frequency sputtered at room temperature on glass were studied as a function of oxygen volume percentage. The as-deposited films were post-annealed in the temperature range of 300-500 °C in oxidizing (open air) and reducing (N2:H2 gas) atmospheres for 1 h. The as-deposited amorphous films become crystalline on post-annealing irrespective of the annealing conditions. In most cases, the (2 2 2) diffraction line is emerged as the high intensive peak. The films annealed at ≥400 °C in N2:H2 show a carrier concentration >1020 cm-3. The better electrical properties are obtained for the films post-annealed at 300 °C. The optical transmittance of the as-deposited films varies between 10% and 85% depending on the deposition and annealing conditions. Atomic force microscope analysis reveal that the films annealed at 300 °C are composed of closely packed crystallites (size of which varies between 5 nm and 150 nm) whose size varies noticeably when the annealing temperature is raised to 400 °C. On the other hand, the surface of the films annealed at 500 °C becomes rougher, with the RMS roughness varying between 2.00 nm and 16.97 nm. The surface of the films deposited in the presence of oxygen shows metal like features when annealed at ≥400 °C in N2:H2 that is attributed to the segregation of indium. Further, the segregation of In is substantiated from the scanning electron microscope analysis of these samples. © 2008 Elsevier B.V. All rights reserved.

The influence of oxygen content, radio-frequency (rf) sputtering power, and postdeposition annealing on the electrical properties of gallium-indium-zinc oxide (GIZO) thin-film transistors (TFTs) is analyzed. Little to no oxygen content in the sputtering chamber is crucial to obtain high-performance devices, even before annealing. In contrast, a high oxygen content and rf power lead, respectively, to unstable/poor performing and depletion mode TFTs before annealing, and mainly for these "nonideal" conditions, annealing proves to be effective to improve device performance/stability and to decrease the performance discrepancy among TFTs processed under different oxygen and rf power conditions. Best TFTs present a field-effect mobility of 46 cm2 / V s, subthreshold swing of 0.26 V/dec, threshold voltage of 0.70 V, and an on/off ratio 108 - 109. These results are a consequence of the optimized processing and of the usage of proper GIZO target composition, 1:2:1 mol. © 2008 The Electrochemical Society.

Thin films of copper oxide were obtained through thermal oxidation (100-450 °C) of evaporated metallic copper (Cu) films on glass substrates. The X-ray diffraction (XRD) studies confirmed the cubic Cu phase of the as-deposited films. The films annealed at 100 °C showed mixed Cu-Cu2O phase, whereas those annealed between 200 and 300 °C showed a single cubic Cu2O phase. A single monoclinic CuO phase was obtained from the films annealed between 350 and 450 °C. The positive sign of the Hall coefficient confirmed the p-type conductivity in the films with Cu2O phase. However, a relatively poor crystallinity of these films limited the p-type characteristics. The films with Cu and CuO phases show n-type conductivity. The surface of the as-deposited is smooth (RMS roughness of 1.47 nm) and comprised of uniformly distributed grains (AFM and SEM analysis). The post-annealing is found to be effective on the distribution of grains and their sizes. The poor transmittance of the as-deposited films (<1%) is increased to a maximum of ∼80% (800 nm) on annealing at 200 °C. The direct allowed band gap is varied between 2.03 and 3.02 eV. © 2008 Elsevier B.V. All rights reserved.

In the present work we investigate, the role of zinc oxide (ZnO) thin films passivating layer deposited by rf magnetron sputtering at room temperature on low (18%) and high (80%) porosity porous silicon (PS). The micro-Raman spectroscopy, Fourier transform infrared spectroscopy (FTIR) and atomic force microscopy (AFM) analysis have been carried out to understand the effect of ZnO films coating on PS. A systematic investigation from Raman spectroscopy suggests the formation of a good quality ZnO wurtzite structure on PS. The photoluminescence (PL) measurements on PS and ZnO coated PS shows a red, blue and UV emission bands at around ∼1.8, ∼2.78 and ∼3.2 eV. An enhancement of all PL emission bands have been achieved after ZnO films deposition on high porosity PS. © 2007 Elsevier B.V. All rights reserved.

The electron transport in n-type polycrystalline zinc oxide, nanocrystalline Zinc-Gallium-Oxygen and amorphous Indium-Zinc-Oxygen systems produced by rf magnetron sputtering at room temperature, under different oxygen partial pressure were investigated. It was found that the carrier transport is not band tail limited, being governed by metal cations irrespective to the film's structure. The highest net room temperature electron mobility was achieved on the amorphous films and noticed that for the single component oxides the mobility decreases as the carrier concentration increases, while the reverse behaviour was observed for the multicomponent oxides, independently of their structure. These behaviours are related to the role that negative charge defects in excess of 1010 cm- 2 generated on multicomponent oxides have on carriers scattering and so on their electronic performances. © 2007 Elsevier B.V. All rights reserved.

This work shows the effect of the annealing temperature and atmosphere on the properties of r.f. magnetron sputtered indium-zinc oxide (IZO) thin-films of two types: one a conductive film (as-deposited, room temperature) that exhibits a resistivity of 3.5 × 10- 4 Ω cm; the other, a semiconductor film with a resistivity ∼ 102 Ω cm. The annealing temperatures were changed between 125 and 500 °C. Crystallization of the more conductive films was already noticeable at temperatures around 400 °C. Three different annealing atmospheres were used - vacuum, air and oxygen. For the conductive films, only the oxygen atmosphere was critical, leading to an increase of the electrical resistivity of more than one order of magnitude, for temperatures of 250 °C and above. Concerning the semiconductor films, both temperature and atmosphere had a strong effect on the film's properties, and the resistivity of the annealed films was always considerably smaller than the as-deposited films. Finally, some results of the application of these films to transparent TFTs are shown. © 2007 Elsevier B.V. All rights reserved.