Regina Monteiro

The surfaces of cordierite and glass particles were modified by coating them with an alumina precursor using a precipitation process in the presence of urea. Scanning electron microscopy (SEM), high-resolution transmission electron microscopy, X-ray diffraction, electrophoresis, and rheological measurements were used to characterize the coated powders. SEM and transmission electron microscopy morphologies of the coated powders revealed that amorphous and homogeneous coatings have been formed around the particles. The morphology of the coated powders showed a coiled wormlike surface. The coating Al2O3 layer dominated the surface properties of the coated glass and cordierite powders. The influence of the coating layer on the processing ability of cordierite-based glass-ceramics substrates by tape casting was studied in aqueous media. It could be concluded that the coating of the powders facilitates the processing and yields green and sintered tapes with denser, more homogeneous microstructures compared with the uncoated powders.

Hall effect measurements are one of the most powerful techniques for obtaining information about the conduction mechanism in polycrystalline semiconductor materials, which is the basis for understanding semiconductor gas sensors. In order to investigate the correlation between the microscopic characteristics and the macroscopic performances exhibited by undoped tin oxide gas sensors deposited by spray pyrolysis, Hall effect measurements were performed at different temperatures, from room temperature up to 500 K, and in the presence of two different atmospheres, air and methane. From these measurements, it was possible to infer the potential barrier and its dependence with the used atmosphere. The obtained results were analysed in terms of the oxygen mechanism at grain boundaries on the basis of the grain boundary-trapping model. In the presence of methane gas, the electrical resistivity decreases due to the lowering of the inter-grain boundary barrier height.

The crystallization of a commercial borosilicate glass powder has been studied in the temperature range 750-900°C. Crystal growth was investigated by high temperature XRD and cristobalite precipitation was identified. Glass devitrification exhibited a characteristic incubation period that decreased with increasing temperature: 25-30 min at 750°C, 9-12 min at 775°C, 5-10 min at 810°C, and 0-5 min at 840°C. Cristobalite is an unfavorable transformation product in terms of thermal expansion behavior. The precipitation of cristobalite in sintered glass compacts was confirmed by dilatometric analysis, where the increase in thermal expansion coefficient due to the presence of cristobalite and its transition from the tetragonal to the cubic phase were verified. Correlation between the XRD results and the dilatometric data from sintered glass compacts showed the partial dissolution of cristobalite when the glass was heated at the highest temperatures.

Cobalt oxide doped silica films were synthesized by a dip-coating technique. Initial compounds were cobalt acetate Co(CH3COO)2-4H 2O and tetraethoxysilane Si(OC2H5)4. The chemical composition was studied by X-ray diffraction and UV-Vis spectroscopy. The morphology analyses were carried out by means of atomic force microscopy. The average diameter of cobalt oxide dispersed particles increases with the molar ratio Co:Si and with the aging time of the initial colloidal solution. © 2009 American Institute of Physics.

Borosilicate glass-alumina composites with (1 - x) Glass + x Al 2O 3 (x = 0, 5, 10, 25 vol.%) were prepared and the effect of Al 2O 3 addition on the structural, electrical and thermal characteristics was investigated. XRD patterns revealed the presence of cristobalite (SiO 2) in sintered borosilicate glass and that the addition of Al 2O 3 hinders cristobalite formation. This behavior is due to the diffusion of some Al 3+ ions from alumina to glass, which leads to changes in glass structure and composition as identified by SEM/EDS. Cristobalite was undetected in composites containing 10% Al 2O 3 that attained the lowest thermal expansion coefficient value (∼4.6 × 10 -6 °C -1). Conductivity (dc and ac) increased with the amount of Al 3+ ions present in the glass structure as modifiers and formers. Dielectric constant values, in the range 5.0-7.2, increased with Al 2O 3 addition and the values of loss tan δ (1.5-2.1 × 10 -2) indicate that these materials are good insulators. © 2012 Elsevier B.V. All rights reserved.

This study deals with SiO2-P2O5 powders obtained by sol-gel process, starting from tetraethoxysilane (TEOS) as precursor for SiO2 and either triethylphosphate (TEP) or phosphoric acid (H3PO4) as precursors for P2O5. In the case of samples prepared with H3PO4, TG-DTA data showed an accentuated weight loss associated to an endothermic effect up to about 140 °C, specific for the evaporation of water and ethylic alcohol from structural pores, and also due to alkyl-amines evaporation. Sol-gel samples prepared with TEP exhibited different thermal effects, depending on the type of atmosphere used in the experiments, i.e. argon or air. XRD analysis revealed that annealed sol-gel samples prepared with H3PO4 showed specific peaks for silicophosphate compounds such as Si3(PO4)4, Si2P2O9, and SiP2O7. XRD results for annealed sol-gel samples prepared with TEP indicated mainly the presence of a vitreous (amorphous) phase, which could be correlated with SEM images. The presence of SiO2 in the sample might be expected. Thus, we have searched for any SiO2 polymorph possible to crystallize. Only potential peaks of cristobalite were identified but some of them are overlapping with peaks of other crystalline phosphates. SEM analysis indicated a decrease of the amount of crystalline phases with the increase in the annealing temperature. © 2009 Elsevier B.V. All rights reserved.

Various metal oxide-silica nanocomposite films have been recently proposed as gas-sensitive materials. This paper presents results on cobalt oxide-SiO2 mesoporous nanocomposite thin films templated by a cationic surfactant. The films were deposited on glass substrate by dip-coating process, using [Co(CH3COO)2]·4H2O and tetraethoxysilane (TEOS) as starting materials. The effect of withdrawal speed, number of layers and thermal treatment on the crystalline structure, morphology, Co-doping states, optical, electrical and gas sensing properties of the thin films has been investigated using X-ray diffraction, atomic force microscopy, X-ray photoelectron spectroscopy, optical transmittance and room temperature photoreduction-oxidation data. © 2007 Elsevier B.V. All rights reserved.

Barium zinc borosilicate glasses with a molar composition xBaO-(60-x)ZnO-30B 2O 3-10SiO 2, where x ranged from 0 to 60 mol%, were prepared using melt-quenching method. The effect of BaO substitution for ZnO on the sintering, crystallization, and dielectric characteristics has been investigated. The behavior of the studied barium zinc borosilicate glasses was mainly determined by the relative amount of the structural modifier oxides (BaO and ZnO) and the ionic size, and field strength of the modifying cations (Ba 2+, Zn 2+). Increased amounts of BaO decreased both glass transition temperature and crystallization temperature, while increasing the relative dielectric constant. Sintering occurred before crystallization for glasses where substitution of BaO for ZnO was up to 30 mol%, but for higher substitution levels, crystallization occurred during the sintering process hindering densification. © 2012 The American Ceramic Society.

The effect of rigid inclusions on the densification during isothermal sintering of glass matrix composites was investigated. Mixtures containing borosilicate glass powder and 0, 5, 10 and 25 vol. % alumina (Al 2O3) particles were prepared and powder compacts isostatically pressed at 200 MPa have been used. The sintering behaviour of the samples heated at 800°C during various times was investigated through density measurement, axial and radial shrinkage measurements. The microstructure was analysed by SEM and the crystalline phases present in the sintered composites were identified by XRD. The relative density of the isothermally treated borosilicate glass-Al2O3 composites decreased significantly with the increase in Al2O3 content because the presence of rigid inclusions retarded the densification of the compacts. The borosilicate glass exhibited anisotropic shrinkage behaviour, showing a radial shrinkage higher than the axial shrinkage and isotropic shrinkage was favoured by Al2O3 additions. Sintered glass showed a dense microstructure with some spherical closed pores. The microstructure of composites with 5 vol. % Al2O3 revealed that most of the pores were filled by capillary flow of the glass. The microstructure of composites with higher Al2O3 additions showed dense areas together with interconnected pores, which appeared at the sites of large glass particles in the green compacts.