Regina Monteiro

Citation:

Lima, M. M. R. A., and R. C. C. Monteiro. "Shrinkage behaviour of borosilicate glass-Al2O3 composites during isothermal sintering." Materials Science Forum. 514-516 (2006): 648-652.

Abstract:

The effect of rigid inclusions on the densification during isothermal sintering of glass matrix composites was investigated. Mixtures containing borosilicate glass powder and 0, 5, 10 and 25 vol. % alumina (Al 2O3) particles were prepared and powder compacts isostatically pressed at 200 MPa have been used. The sintering behaviour of the samples heated at 800°C during various times was investigated through density measurement, axial and radial shrinkage measurements. The microstructure was analysed by SEM and the crystalline phases present in the sintered composites were identified by XRD. The relative density of the isothermally treated borosilicate glass-Al2O3 composites decreased significantly with the increase in Al2O3 content because the presence of rigid inclusions retarded the densification of the compacts. The borosilicate glass exhibited anisotropic shrinkage behaviour, showing a radial shrinkage higher than the axial shrinkage and isotropic shrinkage was favoured by Al2O3 additions. Sintered glass showed a dense microstructure with some spherical closed pores. The microstructure of composites with 5 vol. % Al2O3 revealed that most of the pores were filled by capillary flow of the glass. The microstructure of composites with higher Al2O3 additions showed dense areas together with interconnected pores, which appeared at the sites of large glass particles in the green compacts.

Notes:

cited By 0

Related External Link