Cork is a natural cellular and electrically insulating material which may have the capacity to store electric charges on or in its cell walls. Since natural cork has many voids, it is difficult to obtain uniform samples with the required dimensions. Therefore, a more uniform material, namely commercial cork agglomerate, usually used for floor and wall coverings, is employed in the present study. Since we know from our previous work that the electrical properties of cork are drastically affected by absorbed and adsorbed water, samples were protected by means of different polymer coatings (applied by spin-coating or soaking). Corona charging and isothermal charging and discharging currents were used to study the electrical trapping and detrapping capabilities of the samples. A comparison of the results leads to the conclusion that the most promising method for storing electric charges in this cellular material consists of drying and coating or soaking with a hydrophobic, electrically insulating polymer such as polytetraflouroethylene (Teflon (R)). (c) 2007 Elsevier B.V. All rights reserved.

Cross-linked polyethylene (XLPE) is currently widely used as an insulating material for power cables due to its good physical properties, however when in use it undergoes an electrical ageing process. Its ability to trap electric charge can give rise to space charge accumulation in the bulk of the polymer and produce localised electric stresses that can lead to cable failure, since the electric field will be increased above the design stress in some regions favouring the initiation of degradation there. In this work the PEA (pulsed electro-acoustic) method was used to compare the charge dynamics in three samples (XLPE cable peelings) aged in different ways (electrothermally in the laboratory, field aged in service and thermally aged in the laboratory). Very different transient behavior was found depending upon the ageing history. This is related to differences in the migration of chemical species in the insulation layer, which are known to act as charge traps. All materials showed heterocharge peaks when the space charge reached stability, the magnitude of which seems to be related to the severity of the ageing. (c) 2007 Elsevier B.V. All rights reserved.

Cross-linked polyethylene (XLPE) is currently widely used as an insulating material for power cables due to its good physical properties, however when in use it undergoes an electrical ageing process. Its ability to trap electric charge can give rise to space charge accumulation in the bulk of the polymer and produce localised electric stresses that can lead to cable failure, since the electric field will be increased above the design stress in some regions favouring the initiation of degradation there. In this work the PEA (pulsed electro-acoustic) method was used to compare the charge dynamics in three samples (XLPE cable peelings) aged in different ways (electrothermally in the laboratory, field aged in service and thermally aged in the laboratory). Very different transient behavior was found depending upon the ageing history. This is related to differences in the migration of chemical species in the insulation layer, which are known to act as charge traps. All materials showed heterocharge peaks when the space charge reached stability, the magnitude of which seems to be related to the severity of the ageing.

There is a sustained interest both from theoretical and from practical points of view to understand the isothermal charging and the isothermal discharging currents in dielectrics. The measured currents are analyzed either in terms of polarization mechanisms or in terms of charge injection/extraction at the metal-dielectric interface and the conduction current through the dielectric material. As long as we do not know the nature of the origin of the current, it is not clear what information we can get by analyzing the experimental data. We propose to measure the open-circuit isothermal charging and discharging currents just to overpass the difficulties related to the analysis of the conduction mechanisms in dielectric materials. We demonstrate that besides a polarization current, there is a current related with charge injection or extraction at the metal-dielectric contact and a reverse current related to the charge trapped into the superficial trap states of the dielectric and that can jump at the interface in a reverse way. An analytical expression for the current is proposed. By fitting the experimental data to this analytical equation, two important parameters can be determined: (i) the highest value of the relaxation time for the polarization mechanisms still involved into the transient current and (ii) the height of the potential barrier W-0 at the metal-dielectric interface at the initial time when the step voltage is applied. The value obtained for Al-polyethylene terephthalate interface is (0.43 +/- 0.02) eV. For a charging voltage of 220 V there are 6x10(14) trapped electrons/m(2). (c) 2008 American Institute of Physics.

Lately the electrical and dielectric properties of cork and some cork-based materials (commercial and non-commercial) have been studied in order to understand their ability to store electrical charge. The main problem found so far is related to the water content in cork, only of a few % weight. but large enough to influence greatly the conductivity of cork and, consequently, the charge storage capability. To overcome this problem cork has been combined with hydrophobic materials. In this work a commercial wax (paraffin wax) was used to produce a cork/paraffin composite by hot pressing. After milled and mixed natural cork. TetraPak (R) containers waste and paraffin were pressed to make plaques of a new composite. Different concentrations of cork. TetraPak (R) and paraffin, different granules sire, different temperature and pressure were used to produce the samples. The electrical properties of the new composite were measured by the isothermal charging and discharging current method and the results compared to previously ones obtained for natural cork and other derivative products. The new composite has shown to have lower conductivity than the commercial agglomerate. which makes it a better material for charge storage.

Lately the electrical and dielectric properties of cork and some cork-based materials (commercial and non-commercial) have been studied in order to understand their ability to store electrical charge. The main problem found so far is related to the water content in cork, only of a few % weight. but large enough to influence greatly the conductivity of cork and, consequently, the charge storage capability. To overcome this problem cork has been combined with hydrophobic materials. In this work a commercial wax (paraffin wax) was used to produce a cork/paraffin composite by hot pressing. After milled and mixed natural cork. TetraPak (R) containers waste and paraffin were pressed to make plaques of a new composite. Different concentrations of cork. TetraPak (R) and paraffin, different granules sire, different temperature and pressure were used to produce the samples. The electrical properties of the new composite were measured by the isothermal charging and discharging current method and the results compared to previously ones obtained for natural cork and other derivative products. The new composite has shown to have lower conductivity than the commercial agglomerate. which makes it a better material for charge storage.

Lately the electrical and dielectric properties of cork and some cork-based materials (commercial and non-commercial) have been studied in order to understand their ability to store electrical charge. The main problem found so far is related to the water content in cork, only of a few % weight. but large enough to influence greatly the conductivity of cork and, consequently, the charge storage capability. To overcome this problem cork has been combined with hydrophobic materials. In this work a commercial wax (paraffin wax) was used to produce a cork/paraffin composite by hot pressing. After milled and mixed natural cork. TetraPak (R) containers waste and paraffin were pressed to make plaques of a new composite. Different concentrations of cork. TetraPak (R) and paraffin, different granules sire, different temperature and pressure were used to produce the samples. The electrical properties of the new composite were measured by the isothermal charging and discharging current method and the results compared to previously ones obtained for natural cork and other derivative products. The new composite has shown to have lower conductivity than the commercial agglomerate. which makes it a better material for charge storage.

The thermally stimulated discharge current (TSDC.) method is a very sensitive and a very selective technique to analyze dipole disorientation and the movement of de-trapped space charge (SC). We have proposed a variant of the TSDC method, namely the final thermally stimulated discharge current (FTSDC) technique. flee experimental conditions can be selected so that the FTSDC is mainly determined by the SC de-trapping. The temperatures of the maximum intensity of the fractional polarization peaks obtained at low temperature, in the range of the local (secondary) relaxation, are in general about 10 to 20 K above the poling temperature. Measurements of the FTSDC in a wide temperature range demonstrate the existence of an apparent peak at a temperature T-ma shifted with about 10 to 30 K above the charging temperature T-c. The shift of T-ma with respect to T-c depends on the experimental conditions. The peak width at the half maximum intensity decreases as T-c increases and the thermal apparent activation energy increases. The variations are not monotonous revealing the temperature range where the molecular motion is stronger and consequently the charge trapping and de-trapping processes are affected. Our results demonstrate that there is a strong similarity between the elementary peaks obtained by the two methods, and the current is mainly determined by SC de-trapping. Even the best elementary peaks are not fitted very well by the analytical equation, indicating that the hypothesis behind this equation have to be reconsidered.

The thermally stimulated discharge current (TSDC.) method is a very sensitive and a very selective technique to analyze dipole disorientation and the movement of de-trapped space charge (SC). We have proposed a variant of the TSDC method, namely the final thermally stimulated discharge current (FTSDC) technique. flee experimental conditions can be selected so that the FTSDC is mainly determined by the SC de-trapping. The temperatures of the maximum intensity of the fractional polarization peaks obtained at low temperature, in the range of the local (secondary) relaxation, are in general about 10 to 20 K above the poling temperature. Measurements of the FTSDC in a wide temperature range demonstrate the existence of an apparent peak at a temperature T-ma shifted with about 10 to 30 K above the charging temperature T-c. The shift of T-ma with respect to T-c depends on the experimental conditions. The peak width at the half maximum intensity decreases as T-c increases and the thermal apparent activation energy increases. The variations are not monotonous revealing the temperature range where the molecular motion is stronger and consequently the charge trapping and de-trapping processes are affected. Our results demonstrate that there is a strong similarity between the elementary peaks obtained by the two methods, and the current is mainly determined by SC de-trapping. Even the best elementary peaks are not fitted very well by the analytical equation, indicating that the hypothesis behind this equation have to be reconsidered.

The measured isothermal charging and discharging currents are analyzed either in terms of polarization mechanisms or in terms of charge injection/extraction at the metal-dielectric interface and the conduction current through the dielectric material. We propose to measure the open-circuit isothermal charging and discharging currents just to overpass the difficulties related to the analysis of the conduction mechanisms through the dielectric materials. Besides a polarization current, there is a current related with charge injection or extraction at the metal-dielectric contact and a reverse current related to the charge trapped into the superficial trap states of the dielectric and that can jump at the interface in a reverse way. By fitting the experimental data, two important parameters can be determined (i) the highest value of the relaxation time for the polarization mechanisms still involved into the transient current and (ii) the height W-0 of the potential barrier at the metal-dielectric interface immediately after the step voltage is applied. Only the initial part of the measured isothermal charging or discharging current can be used to obtain information about the polarization processes. By transforming the time-domain data into the frequency domain, a maximum for the imaginary part of the dielectric permittivity is obtained, in good agreement with the data obtained from AC dielectric measurements and the finally thermally stimulated discharge current measurements. (C) 2009 Elsevier B.V. All rights reserved.

Opposite results concerning the sign of the parasitic charge accumulated at the metal dielectric contact in RF microelectromechanical systems (MEMS) capacitive switches are found in the literature. The mechanism concerning charge injection/extraction at the metal-dielectric contact and its influence on the pull-in voltage needs to be further clarified. A model-switch, for which only one dimension is in the microns range, is used to study the behaviour of a capacitive RF MEMS switch. The aim is to analyze how the electric charge is injected/extracted into or from the dielectric material under the applied field and to obtain realistic data to understand how this parasitic charge influences the pull-in voltage V-pi and the pull-off voltage V-po. A triangle voltage is employed to measure V-pi and V-po by measuring the isothermal charging/discharging currents. Our results demonstrate that V-pi is strongly dependent on the injected/extracted charge on the free surface of the dielectric. The charge injected/extracted at the bottom side of the dielectric has no influence on the actuation voltage. The charge injected/extracted on the free surface of the dielectric determines an increase of the modulus of V-pi and, eventually, the switch can fail to actuate. An estimation of the charge stored into the material was obtained (i) by measuring the charging current and the discharging current and (ii) from the value of the V-pi. The parasitic charge necessary to keep the bridge stick to the insulator is 5.3 x 10(-4) cm(-2) for our experimental conditions. The modification of the V-pi determined by the stored charge in the dielectric is analyzed. An increase of the relative dielectric permittivity by a factor of 2 produces a decrease of the actuation voltage of 10%. A variation of 30% in the elastic constant determines a variation of about 20% in the V-pi. A voltage threshold for charge injection/extraction was not observed.

Cork is a cellular biomaterial that has unique characteristics that make it suitable for many types of applications. Since it is also an electrical insulator, the study of its electrical and dielectric properties can lead to new interesting applications. The moisture present in cork and derivatives has a very important role on the dielectric properties. In this work a composite made of both recycled cork and TetraPak (R) used containers was studied and compared with other cork products. The dielectric relaxation spectra of natural cork (as received), commercial cork agglomerate and of a composite cork/Tetrapak (R) was investigated in the temperature range of -50 to 120 degrees C and in the frequency range of 10(-1) Hz-2 MHz. For some samples of the composite a small amount of paraffin was added. The highest values for the imaginary part of the dielectric permittivity were found for the commercial material and the composite without paraffin. The lowest was found for the cork/TetraPak (R)/paraffin composite. The influence of humidity content was investigated for the composite with wax. Natural cork shows a peak around 80 degrees C (not seen in the derivative materials). The commercial agglomerate and the cork/TetraPak (R)/paraffin composite show a peak around 40-50 degrees C. In the composite this peak becomes smaller as humidity is removed. (C) 2009 Elsevier B.V. All rights reserved.

For the characterization of the new materials and for a better understanding of the connection between structure and properties it is necessary to use more and more sensible methods to study molecular movement at nanometric scale. This paper presents the experimental basis for a new electrical method to study the fine molecular movements at nanometric scale in dielectric materials. The method will be applied for polar and non-polar materials characterization. Traditionally, the electrical methods used to study the molecular movements are based on the movements of the dipoles that are parts of the molecules. We have proposed recently a combined protocol to analyze charge injection/extraction, transport, trapping and detrapping in low mobility materials. The experimental results demonstrate that the method can be used to obtain a complex thermogram which contains information about all molecular movements, even at nanoscopic level. Actually during the charging process we are decorating the structure with space charge and during the subsequent heating we are observing an apparent peak and the genuine peaks that are related to charge de-trapping determined by the molecular movement. The method is very sensitive, very selective and allows to determinate the parameters for local and collective molecular movements, including the temperature dependence of the activation energy and the relaxation time.

The isothermal charging current and the isothermal discharging current in low mobility materials are analyzed either in terms of polarization mechanisms or in terms of charge injection/extraction at the metal-dielectric interface and the conduction current through the dielectric material. We propose to measure the open-circuit isothermal charging and discharging currents just to overpass the difficulties related to the analysis of the conduction mechanisms in dielectric materials. We demonstrate that besides a polarization current there is a current related to charge injection or extraction at the metal-dielectric interface and a reverse current related to the charge trapped into the shallow superficial or near superficial states of the dielectric and which can move at the interface in the opposite way that occurring during injection. Two important parameters can be determined (i) the highest value of the relaxation time for the polarization mechanisms which are involved into the transient current and (ii) the height of the potential barrier W-0 at the metal-dielectric interface. The experimental data demonstrate that there is no threshold field for electron injection/extraction at a metal-dielectric interface.

The Thermally Stimulated Discharge Current (TSDC) method is a very sensitive technique to analyze the movement of dipoles and of space charge (SC). To increase the selectivity of the method we have proposed a variant of the TSDC method, namely the final thermally stimulated discharge current (FTSDC) technique. The experimental conditions can be selected so that the FTSDC is mainly determined by SC de-trapping. The aim of this paper is to analyze if the elementary peaks obtained by using the two methods can be assumed as elementary Debye peaks and to determine the best experimental conditions to obtain a narrow experimental peak which means to increase the selectivity of the method.