Rodrigo Martins

In this work metal-insulator-semiconductor (MIS) photodiodes with a structure: Cr/a-Si:H(n+)/a-Si:H(i)/oxide/Au were studied, where the main objective was to determine the influence of the oxide layer on the performance of the devices. The results achieved show that their performance is a function of both oxide thickness and oxide density. The a-Si:H oxidation method used was the immersion in H2O2 solution. By knowledge of the oxide growth process it was possible to fabricate photodiodes exhibiting an open circuit voltage of 0.65V and short circuit current density under AM1.5 illumination of 11mA/cm2, with a response times less than 1μs for load resistance <400Ω, and a signal to noise ratio of 1×107. © 2003 Elsevier B.V. All rights reserved.

This work presents a study performed on the deposition of pm-Si:H by plasma enhanced chemical vapor deposition using excitation frequencies of 13.56 and 27.12 MHz, where the interest of increasing the excitation frequency relies on higher plasma dissociation and reduced energy of ion bombardment, thus allowing the deposition of superior grade material at higher growth rates. The plasma impedance, which allows the monitoring of particle formation in the plasma, was correlated to the film properties, characterized by spectroscopic ellipsometry and hydrogen exodiffusion experiments. The set of data obtained show that by using the 27.12-MHz excitation frequency the hydrogen dilution and the r.f. power density needed to produce pm-Si:H can be reduced. Growth rates above 3.1 Å/s were obtained, the films being more dense and chemically more stable than those obtained with the standard 13.56 MHz. © 2003 Elsevier B.V. All rights reserved.

This work presents a study on the effect of an interfacial silicon oxide layer placed between Au and a-Si:H MIS (metal-insulator-semiconductor) photodiodes in their performances, by stopping the Au diffusion towards the a-Si:H. The results show that the Au diffuses very easily to the oxide free a-Si:H surface, even at room temperature, degrading the photodiode performance. On the other hand, the MIS photodiodes with the interfacial oxide show an improvement of their characteristics after annealing, function of its thickness, and degree of film's compactness. This effect is associated with the presence of oxide of thicknesses ≥5 Å at the Au/a-Si:H interface that prevents the Au diffusion and improves the photodiode characteristics, which does not happen when the interfacial oxide is absent. © 2004 Elsevier B.V. All rights reserved.

This work presents a study performed on several Au contacts deposited by evaporation on oxide free and oxidised (5-20Å of oxide) a-Si:H surfaces. The characterisation of the films was performed on as deposited, aged and annealed at 150°C structures. SIMS and RBS measurements show that the Au diffuses very easily on oxide free a-Si:H surfaces, even at room temperature, resulting in the formation of an oxide at the device surface that acquires a blue colour instead of the gold colour of the contacts. This was also visible in the SEM pictures of the cross section of the structures produced and on the changes of the surface morphology observed by AFM measurements. On the other hand, when the Au is deposited on oxidised a-Si:H surfaces, the results show that the oxide prevents the Au from diffusing and the nature of the contact is preserved. That is, better rectifying and stability performances are obtained in MIS like structures than in Schottky structures.

It is experimentally known that the linearity and sensitivity of the position sensitive detectors (PSD) are dependent on the resistance of the collecting layer and of the load resistance, mainly if the detection is based on the measurement of the photo-lateral voltage. To determine the value of the load resistance to be used in metal - insulator - semiconductor (MIS) PSDs structures that lead to the maximum value of sensitivity and linearity, we propose an electrical model through which it is able to simulate the proper sensor response and how the load resistance influence the results obtained. This model is valid for PSDs where the resistance of the collecting resistive layer is quite low (≤ 500 Ω), leading to a low output impedance. Under these conditions we conclude that the value of the load resistance should be of about 1 kΩ in order to achieve a good compromise between the linearity and the sensitivity of the PSD. This result is in agreement with the set of experiments performed. © 2005 Materials Research Society.

In this work we present results of a study performed on metal-insulator-semiconductor (MIS) diodes with the following structure: substrate (glass)/Cr (2000 Å)/a-Si:H n+(400 Å)/a-Si:H i (5500 Å)/oxide (0-40 Å)/Au (100 Å) to determine the influence of the oxide passivation layer grown by different techniques on the electrical performance of MIS devices. The results achieved show that the diodes with oxides grown using hydrogen peroxide present higher rectification factor (2×106) and signal to noise (S/N) ratio (1×10 7 at -1 V) than the diodes with oxides obtained by the evaporation of SiO2, or by the chemical deposition of SiO2 by plasma of hexamethyldisiloxane. However, in the case of deposited oxides, the breakdown voltage is higher, 30 V instead of 3-10 V for grown oxides. The ideal oxide thickness, determined by spectroscopic ellipsometry, is dependent on the method used to grow the oxide layer and is in the range between 6 and 20 Å. The reason for this variation is related to the degree of compactation of the oxide produced, which is not relevant for applications of the diodes in the range of ±1 V, but is relevant when high breakdown voltages are required. © 2003 Elsevier B.V. All rights reserved.

In this study, amorphous indium-tungsten oxide (IWO) semiconductor thin films were prepared by an eco-friendly spin-coating process using ethanol and water as solvents. The electrical properties of IWO thin-film transistors (TFTs), together with the structural and morphological characteristics of IWO thin films, were systematically investigated as functions of tungsten concentration and annealing temperature. The optimized IWO channel layer was then integrated on an aqueous aluminum oxide (AlOx) gate dielectric. It is observed that the solution-processed IWO/AlOx TFT presents high stability and improved characteristics, such as an on/off current ratio of 5 × 107, a field-effect mobility of 15.3 cm2 V-1 s-1, a small subthreshold slope of 68 mV dec-1, and a threshold voltage shift of 0.15 V under bias stress for 2 h. The IWO/AlOx TFT could be operated at a low voltage of 2 V, which was 15 times lower than that of conventional SiO2-based devices. The solution-processed IWO thin films synthesized in a green route would be promising candidates for large-area and high-performance low-cost devices. © The Royal Society of Chemistry 2016.

This work shows the effect of the annealing temperature and atmosphere on the properties of r.f. magnetron sputtered indium-zinc oxide (IZO) thin-films of two types: one a conductive film (as-deposited, room temperature) that exhibits a resistivity of 3.5 × 10- 4 Ω cm; the other, a semiconductor film with a resistivity ∼ 102 Ω cm. The annealing temperatures were changed between 125 and 500 °C. Crystallization of the more conductive films was already noticeable at temperatures around 400 °C. Three different annealing atmospheres were used - vacuum, air and oxygen. For the conductive films, only the oxygen atmosphere was critical, leading to an increase of the electrical resistivity of more than one order of magnitude, for temperatures of 250 °C and above. Concerning the semiconductor films, both temperature and atmosphere had a strong effect on the film's properties, and the resistivity of the annealed films was always considerably smaller than the as-deposited films. Finally, some results of the application of these films to transparent TFTs are shown. © 2007 Elsevier B.V. All rights reserved.

The influence of oxygen content, radio-frequency (rf) sputtering power, and postdeposition annealing on the electrical properties of gallium-indium-zinc oxide (GIZO) thin-film transistors (TFTs) is analyzed. Little to no oxygen content in the sputtering chamber is crucial to obtain high-performance devices, even before annealing. In contrast, a high oxygen content and rf power lead, respectively, to unstable/poor performing and depletion mode TFTs before annealing, and mainly for these "nonideal" conditions, annealing proves to be effective to improve device performance/stability and to decrease the performance discrepancy among TFTs processed under different oxygen and rf power conditions. Best TFTs present a field-effect mobility of 46 cm2 / V s, subthreshold swing of 0.26 V/dec, threshold voltage of 0.70 V, and an on/off ratio 108 - 109. These results are a consequence of the optimized processing and of the usage of proper GIZO target composition, 1:2:1 mol. © 2008 The Electrochemical Society.

Insensitivity to light irradiation is desirable for conventional applications of thin-film transistors, i.e., the active matrices of displays. However, if one produces a device presenting controlled sensitivity to light, many other applications can benefit or can even be created. In this work it is shown the influence of the photon energy on the optoelectronic properties presented by n-type bottom-gate thin-film transistors based on indium zinc oxide. In the dark, the devices present very good electrical properties, working in the enhancement mode, exhibiting on-off ratios higher than 107 and channel mobility above 30 cm2/V s. Remarkable results were achieved when the devices were exposed to light radiation, the most striking one is the possibility to switch between enhancement (in the dark) and depletion (illuminated) modes, with different threshold voltages and on/off ratios, function of the light power density and wavelength used. This type of behavior permits to design circuits where one can have the same transistor working either in the enhancement or depletion modes, function of the light beam and intensity impinging on it, highly important for short wavelength detector applications. © 2006 Elsevier B.V. All rights reserved.

The aim of the present work was to study the optical properties of amorphous hydrogenated silicon films produced by capacitive and inductive r.f. glow discharge in a 3%SiH4-Ar gas mixture. The effect of the application of static electric and magnetic fields during the film formation on the photoconductivity, photoactivation energy, recombination mechanisms and optical gap was thoroughly investigated. Films prepared in a capacitively or inductively coupled discharge show bias-dependent photoconductivities, which reach about 10-4 Ω-1 cm-1 for an inductive discharge with a negative bias and about 10-5 Ω-1 cm-1 for a capacitive discharge with a positive bias. The optical gap is of the order of 1.55 eV for capacitive films and is bias dependent for inductive films (1.45-1.85 eV). A superimposed magnetic field (of about 1 kG) increases the photoconductivity by one order of magnitude for both deposition methods. The optical gap is field dependent for inductive films (1.6-1.8 eV) and is about 1.6 eV for capacitive films. The main recombination mechanism at a moderate photon flux (less than 1014 cm-2 s-1) is monomolecular for all deposition conditions. The photoactivation energy lies between 0.1 and 0.2 eV for capacitive films and is about 0.1 eV for inductive films. It was also found that, by using suitable crossed electric and magnetic fields, it was possible to control the density and nature of the defect states in the films. These are correlated with the type of hydrogenated silicon species and with the amount of hydrogen incorporated into the films, which markedly influence the film properties. © 1982.

Microcrystalline phosphorus-doped hydrogenated silicon alloy films were deposited in a remote plasma CVD (chemical vapor deposition) system. The film properties were studied as a function of RF power density and hydrogen concentration in the reaction gas mixture. The properties of the deposited films are extremely sensitive to the RF power density in the studied range of 250 mW/cm2 to 625 mW/cm2. Very low values of electrical resistivity were obtained. For an RF power density of 500 mW/cm2, ρ = 3 × 10-2 Ω-cm, while ρ = 1.9 × 103 Ω-cm for 625 mW/cm2, indicating the predominance of the amorphous tissue over the microcrystalline phase. High doping efficiencies which can be correlated to large grain size are indicated by the very low values of the activation energy as low as 30 meV for 500 mW/cm2, that were obtained.

Indium molybdenum oxide (IMO) thin films were radio-frequency (RF) sputtered at room temperature (RT) and studied as a function of base pressure (BP). The crystallinity of the films is decreased with the increase in BP. A maximum mobility (μ) of 49.6 cm 2 V -1 s -1 was obtained from the IMO films deposited at RT without any post-annealing treatment. The electronic behaviour of the deposited films was investigated by temperature-dependent (100-550 K) Hall measurements. Study on the scattering mechanisms based on the experimental data and theoretical models show that the ionized scattering centres are dominating. The films possess wide work function (4.91 eV) and high transmittance (> 70%) over visible and near infrared (NIR) range. The obtained results, especially the high work function and NIR transmittance, are very promising particularly in applications such as optical detectors and solar cells. Copyright © EPLA, 2012.

Thin films of molybdenum doped indium oxide (IMO) were deposited on glass at room temperature using an in-built three-source RF magnetron sputtering. The films were studied as a function of oxygen volume percentage (O2 vol. %; ranging from 0.0 to 17.5%) in the sputtering chamber. The as-deposited amorphous films were crystallized on post-annealing. The as-deposited films are low conducting and Hall coefficients were undetectable; whereas post-annealed films possess fairly high conductivity. The lowest transmittance (11.96% at 600 nm) observed from the films deposited without oxygen increased to a maximum of 88.01% (3.5 O2 vol. %); whereas this transmittance was decreased with the increasing O2 vol. % to as low as 81.04% (15.6 O2 vol. %); a maximum of 89.80% was obtained from the films annealed at 500 °C in open air (3.5 O2 vol. %). The optical band gap of 3.80 eV obtained from the films deposited without oxygen increased with increasing O2 vol. % to as high as 3.91 eV (17.5 O2 vol. %). A maximum of 3.92 eV was obtained from the films annealed at 300 °C in N2:H2 gas atmosphere (17.5 O2 vol. %). © 2008 Elsevier Ltd. All rights reserved.

Indium molybdenum oxide thin films radio-frequency sputtered at room temperature on glass were studied as a function of oxygen volume percentage. The as-deposited films were post-annealed in the temperature range of 300-500 °C in oxidizing (open air) and reducing (N2:H2 gas) atmospheres for 1 h. The as-deposited amorphous films become crystalline on post-annealing irrespective of the annealing conditions. In most cases, the (2 2 2) diffraction line is emerged as the high intensive peak. The films annealed at ≥400 °C in N2:H2 show a carrier concentration >1020 cm-3. The better electrical properties are obtained for the films post-annealed at 300 °C. The optical transmittance of the as-deposited films varies between 10% and 85% depending on the deposition and annealing conditions. Atomic force microscope analysis reveal that the films annealed at 300 °C are composed of closely packed crystallites (size of which varies between 5 nm and 150 nm) whose size varies noticeably when the annealing temperature is raised to 400 °C. On the other hand, the surface of the films annealed at 500 °C becomes rougher, with the RMS roughness varying between 2.00 nm and 16.97 nm. The surface of the films deposited in the presence of oxygen shows metal like features when annealed at ≥400 °C in N2:H2 that is attributed to the segregation of indium. Further, the segregation of In is substantiated from the scanning electron microscope analysis of these samples. © 2008 Elsevier B.V. All rights reserved.

Indium molybdenum oxide thin films were RF sputtered at room temperature on glass substrates with a reference base pressure of 7.5 × 10- 4 Pa. The electrical and optical properties of the films were studied as a function of oxygen partial pressures (OPP) ranging from 1.5 × 10- 3 Pa to 3.5 × 10- 3 Pa. The obtained data show that the bulk resistivity of the films increased by about 4 orders of magnitude (from 7.9 × 10- 3 to 7.6 × 101 Ω-cm) when the OPP increased from 1.5 × 10-3 to 3.5 × 10- 3 Pa, and the carrier concentration decreased by about 4 orders (from 1.77 × 1020 to 2.31 × 1016 cm- 3). On the other hand, the average visible transmittance of 30.54% of the films (brown colour; OPP = 1.5 × 10- 3 Pa) was increased with increasing OPP to a maximum of 80.47% (OPP = 3.5 × 10- 3 Pa). The optical band gap calculated from the absorption edge of the transmittance spectra ranges from 3.77 to 3.88 eV. Further, the optical and electrical properties of the films differ from those deposited at similar conditions but with a base pressure lower than 7.5 × 10- 4 Pa. © 2007 Elsevier B.V. All rights reserved.

Nanocrystalline hydrogenated silicon (nc-Si:H) thin films are generally accepted to be a two phase material-Si crystalline and Si:H amorphous. This work reports the use of impedance spectroscopy to determine the amorphous and crystalline electrical conductivity of a/nc-Si:H films obtained by hot wire chemical vapour deposition. Different relaxation time or time constants are detected, if the film is composed by inhomogeneous material, by measuring ac impedance in a wide range of frequencies. Relating the conduction mechanism of the film to a series of two RC circuits constituted by a resistance and a capacitor in parallel, we may determine distinct ac conductivities and correlate that to the crystalline, amorphous and interface components. The amorphous films analysed exhibit one ac conductivity component while for nanocrystalline films two ac conductivity components are observed. The average value of ac conductivities is in agreement with that of dc conductivity. © 2006.

In this work, we show the possibility to use undoped porous silicon (PS) thin films produced by hot wire chemical vapour deposition technique (HW-CVD) as ethanol detector. Silicon thins films produced by HW-CVD technique, under certain deposition conditions, have a porous structure [Vacuum 52 (1999) 147]. Therefore, in the presence of an alcohol, the OH group is adsorbed by the uncompensated bonds behaving as donor-like carriers leading to an increase in the current flowing through the material. This current enhancement is bias dependent in glass/ITO/i-a-Si:H/Al sensor and increases as the ethanol vapour pressure increases from 10-1mbar to atmospheric pressure. The response time of the current of the sensor and its recovery time are in the range of 10-50s at room temperature. Ethanol quantities above 50ppm can be detected. © Published by Elsevier B.V.

Thin films of copper oxide were obtained through thermal oxidation (100-450 °C) of evaporated metallic copper (Cu) films on glass substrates. The X-ray diffraction (XRD) studies confirmed the cubic Cu phase of the as-deposited films. The films annealed at 100 °C showed mixed Cu-Cu2O phase, whereas those annealed between 200 and 300 °C showed a single cubic Cu2O phase. A single monoclinic CuO phase was obtained from the films annealed between 350 and 450 °C. The positive sign of the Hall coefficient confirmed the p-type conductivity in the films with Cu2O phase. However, a relatively poor crystallinity of these films limited the p-type characteristics. The films with Cu and CuO phases show n-type conductivity. The surface of the as-deposited is smooth (RMS roughness of 1.47 nm) and comprised of uniformly distributed grains (AFM and SEM analysis). The post-annealing is found to be effective on the distribution of grains and their sizes. The poor transmittance of the as-deposited films (<1%) is increased to a maximum of ∼80% (800 nm) on annealing at 200 °C. The direct allowed band gap is varied between 2.03 and 3.02 eV. © 2008 Elsevier B.V. All rights reserved.

Copper oxide thin films were obtained by annealing (temperature ranging between 100 and 450 °C) the metallic Cu films deposited on glass substrates by e-beam evaporation. XRD studies confirmed that the cubic Cu phase of the asdeposited films changes into single cubic Cu 2Ophase and single monoclinic CuO phase, depending on the annealing conditions. The crystallite size is varied betweeñ12 and 31 nm. The lattice parameters of cubic Cu and Cu 2Ophases are estimated tõ3.60 and ̃4.26 Å , respectively. The films with Cu 2O phase showed p-type characteristics. The conductivity is decreased linearly with the decreasing temperature (1/T), which has confirmed the semiconductor nature of the deposited films. The calculated activation energy is varied between 0.10 and 0.16 eV. The surface microstructure is changed depending on the variation in the annealing temperature. The poor transmittance of the asdeposited films (<1%) is increased to a maximum of ̃80% (800 nm) on annealing at 200 °C. The estimated direct allowed band gap is varied between 1.73 and 2.89 eV. © 2009 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

In this paper we present the effect of the insertion of a non-doped nanocrystalline zinc oxide/buffer layer on the electrical, optical and structural properties of indium tin oxide produced at room temperature by radio frequency plasma enhanced reactive thermal evaporation on polymeric substrates. The electrical resistivity of the ITO films is reduced by more than two orders of magnitude (4.5×10-1 to 2.9×10-3 Ωcm). From the Hall effect measurements it is observed that the large decrease associated to the electrical resistivity, is due to the increase associated to the Hall mobility. Concerning the optical properties no effect was observed, being the transmittance in the visible and near the infra red region always higher than 80%.

In this paper we report results concerning the effect of the TCO interface on hydrogenated amorphous silicon (a-Si:H) p-i-n homojunction solar cells. Its correlation with dark current density-voltage (J-V) characteristics and spectral response, before and after while light-soaking degradation, is analysed. From this study, we conclude that the properties and stability of these devices are not only influenced by the a-Si:H film properties, but also by the properties of the transparent conductive electrode and its interface with the a-Si:H layer.

When thinking on low cost and sustainable electronic systems, paper can be considered as an interesting option to be used as substrate but also as a component of such systems. In this work we have tailored paper samples that were used simultaneously as physical support and dielectric in oxide based paper field effect transistors (FETs). It was observed that the gate leakage current in these devices depends directly from fibril's dimension and arrangement, being lower for micro/nano fibrillated cellulose paper. Moreover, extra ionic charge added to the paper during its production results in the improvement of FETs' electrical properties, with saturation mobility of 16 cm 2V -1s -1 and on/off current ratio close to 105. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Indium oxide thin films deposited by spray pyrolysis were irradiated by 100 MeV O7+ ions with different fluences of 5 × 1011, 1 × 1012 and 1 × 1013 ions/cm2. X-ray diffraction analysis confirmed the structure of indium oxide with cubic bixbyite. The strongest (2 2 2) orientation observed from the as-deposited films was shifted to (4 0 0) after irradiation. Furthermore, the intensity of the (4 0 0) orientation was decreased with increasing fluence together with an increase in (2 2 2) intensity. Films irradiated with maximum fluence exhibited an amorphous component. The mobility of the as-deposited indium oxide films was decreased from ∼78.9 to 43.0 cm2/V s, following irradiation. Films irradiated with a fluence of 5 × 1011 ions/cm2 showed a better combination of electrical properties, with a resistivity of 4.57 × 10-3 Ω cm, carrier concentration of 2.2 × 1019 cm-3 and mobility of 61.0 cm2/V s. The average transmittance obtained from the as-deposited films decreased from ∼81% to 72%, when irradiated with a fluence of 5 × 1011 ions/cm2. The surface microstructures confirmed that the irregularly shaped grains seen on the surface of the as-deposited films is modified as "radish-like" morphology when irradiated with a fluence of 5 × 1011 ions/cm2. © 2011 Elsevier B.V. All rights reserved.