Low-temperature sputtered mixtures of high-κ and high bandgap dielectrics for GIZO TFTs
- Citation:
- e Barquinha, P.a, Pereira Gonçalves Kuscer Kosec Vilà Olziersky Morante Martins Fortunato L. a G. a. "Low-temperature sputtered mixtures of high-κ and high bandgap dielectrics for GIZO TFTs." Journal of the Society for Information Display. 18 (2010): 762-772.
Abstract:
This paper discusses the properties of sputtered multicomponent amorphous dielectrics based on mixtures of high-κ and high-bandgap materials and their integration in oxide TFTs, with processing temperatures not exceeding 1 50° C. Even if Ta2O5 films are already amorphous, multicomponent materials such as Ta2O5-SiO2 and Ta2O5-Al2O3 allow an increase in the bandgap and the smoothness of the films, reducing their leakage current and improving (in the case of Ta2O5-SiO2)the dielectric/semiconductor interface properties when these dielectrics are integrated in TFTs. For HfO2- based dielectrics, the advantages of multicomponent materials are even clearer: while HfO2 films present a polycrystalline structure and a rough surface, HfO2-SiO2 films exhibit an amorphous structure and a very smooth surface. The integration of the multicomponent dielectrics in GIZO TFTs allows remarkable performance, comparable with that of GIZO TFTs using SiO2 deposited at 400°C by PECVD. For instance, with Ta2O5-SiO2 as the dielectric layer, field-effect mobility of 35 cm2/(V-sec), close to 0 V turn-on voltage, an on/off ratio higher than 106, a subthreshold slope of 0.24 V/dec, and a small/recoverable threshold voltage shifts under constant current (ID = 10 μ,A) stress during 24 hours are achieved. Initial results with multilayers of SiO2/HfO 2-SiO2/SiO2 are also shown, allowing a lower leakage current with lower thickness and excellent device performance. © Copyright 2010 Society for Information Display.
Notes:
cited By 28
Recent Publications