{Solution processing has been recently considered as an option when trying to reduce the costs associated with deposition under vacuum. In this context, most of the research efforts have been centered in the development of the semiconductors processes nevertheless the development of the most suitable dielectrics for oxide based transistors is as relevant as the semiconductor layer itself. In this work we explore the solution combustion synthesis and report on a completely new and green route for the preparation of amorphous aluminum oxide thin films; introducing water as solvent. Optimized dielectric layers were obtained for a water based precursor solution with 0.1 M concentration and demonstrated high capacitance, 625 nF cm(-2) at 10 kHz, and a permittivity of 7.1. These thin films were successfully applied as gate dielectric in solution processed gallium-zinc-tin oxide (GZTO) thin film transistors (TFTs) yielding good electrical performance such as subthreshold slope of about 0.3 V dec(-1) and mobility above 1.3 cm(2) V-1 s(-1).}

{pH is a vital physiological parameter that can be used for disease diagnosis and treatment as well as in monitoring other biological processes. Metal/metal oxide based pH sensors have several advantages regarding their reliability, miniaturization, and cost-effectiveness, which are critical characteristics for in vivo applications. In this work, WO3 nanoparticles were electrodeposited on flexible substrates over metal electrodes with a sensing area of 1 mm(2). These sensors show a sensitivity of -56.7 +/- 1.3 mV/pH, in a wide pH range of 9 to 5. A proof of concept is also demonstrated using a flexible reference electrode in solid electrolyte with a curved surface. A good balance between the performance parameters (sensitivity), the production costs, and simplicity of the sensors was accomplished, as required for wearable biomedical devices.}

{We use resonant photoemission spectroscopy (resPES) to study the electronic properties of amorphous ZnO (a-ZnO) layers. We report on the core levels, the valence band (VB) PES data, and the X-ray absorption (XAS) data which we use for the conduction band (CB) density of states. From these results we are able to derive the partial density of states (pDOS) of O2p and Zn4s4p states in the VB and CB, respectively as well as a band scheme. At the O1s resonance we observe a band of localized defect states which is located between the Fermi energy and the CBM. At the Zn2p edge the XAS data indicate that localized Zn4s4p states are involved in the DOS starting already at the Fermi energy. (C) 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim}