Abstract Photonic front-coatings with self-cleaning properties are presented as means to enhance the efficiency and outdoor performance of thin-film solar cells, via optical enhancement while simultaneously minimizing soiling-related losses. This is achieved by structuring parylene-C transparent encapsulants using a low-cost and highly-scalable colloidal-lithography methodology. As a result, superhydrophobic surfaces with broadband light-trapping properties are developed. The optimized parylene coatings show remarkably high water contact angles of up to 165.6° and extremely low adhesion, allowing effective surface self-cleaning. The controlled nano/micro-structuring of the surface features also generates strong anti-reflection and light scattering effects, corroborated by numeric electromagnetic modeling, which lead to pronounced photocurrent enhancement along the UV?vis?IR range. The impact of these photonic-structured encapsulants is demonstrated on nanocrystalline silicon solar cells, that show short-circuit current density gains of up to 23.6%, relative to planar reference cells. Furthermore, the improvement of the devices' angular response enables an enhancement of up to 35.2% in the average daily power generation.

Abstract The present work shows the effect of magnesium doping on structural, optoelectrical and electrical properties of Cu2O thin films prepared by spray pyrolysis. The variation in the concentration of Mg shows significant impact on the final thin film properties, whereas the film doped with 0.5 at{%} of Mg exhibited major property improvements in comparison with the undoped thin film and among the other concentrations tested. This condition was further applied for the deposition of an absorber layer in a heterojunction solar cell array with a gradient in thicknesses of active layers to investigate the impact of changing thicknesses on the PV parameters of the solar cell. TiO2 was used as a window layer and the 0.5 at{%} Cu2O doped film as an absorber layer. The produced heterojunction solar cell array was further exposed to a rapid thermal annealing treatment. The I–V measurements show an open circuit voltage of up to 365 mV and a short circuit current density, which is dependent on absorber layer thickness, and reaches to a maximum value of 0.9 mA/cm2.

Thin-films of copper oxide Cu O were produced by thermal oxidation of metallic copper (Cu) at different tempera- tures (150–450 C). The films produced at temperatures of 200, 250 and 300 C showed high Hall motilities of 2.2, 1.9 and 1.6 cm V s , respectively. Single Cu O phases were obtained at 200 Cand its conversion toCuO starts at 250 C. For lower thick- nesses 40 nm, the films oxidized at 250 Cshowed a complete conversion to CuO phase. Successful thin-film transistors (TFTs) were produce by thermal oxidation of a 20 nm Cu film, obtaining p-type Cu O (at 200 C) and CuO (at 250 C) with On/Off ratios of 6 10 and 1 10 , respectively.