The effect of rigid inclusions on the densification during isothermal sintering of glass matrix composites was investigated. Mixtures containing borosilicate glass powder and 0, 5, 10 and 25 vol. % alumina (Al 2O3) particles were prepared and powder compacts isostatically pressed at 200 MPa have been used. The sintering behaviour of the samples heated at 800°C during various times was investigated through density measurement, axial and radial shrinkage measurements. The microstructure was analysed by SEM and the crystalline phases present in the sintered composites were identified by XRD. The relative density of the isothermally treated borosilicate glass-Al2O3 composites decreased significantly with the increase in Al2O3 content because the presence of rigid inclusions retarded the densification of the compacts. The borosilicate glass exhibited anisotropic shrinkage behaviour, showing a radial shrinkage higher than the axial shrinkage and isotropic shrinkage was favoured by Al2O3 additions. Sintered glass showed a dense microstructure with some spherical closed pores. The microstructure of composites with 5 vol. % Al2O3 revealed that most of the pores were filled by capillary flow of the glass. The microstructure of composites with higher Al2O3 additions showed dense areas together with interconnected pores, which appeared at the sites of large glass particles in the green compacts.

n/a

n/a

n/a

n/a

Cross-linked polyethylene (XLPE) peelings from aged power cables from three different sources were studied using a combined procedure of isothermal and thermo-stimulated current measurements. Different parameters, such as electric field, temperature, charging/discharging times, can be selected in order to make an analysis of the space charge characteristics (such as, relaxation times and activation energies). Three different cables peelings were analyzed: A - electrically aged in the laboratory at high temperature, B - service aged for 18 years and C - thermally aged in the laboratory at high temperature. The results were compared for the different types of samples and also with previous results on laboratory aged and produced films of low-density polyethylene (LDPE) and XLPE.

n/a

Electrical properties of natural cork, commercial cork agglomerates (for floor and wall coverings) and a recently developed composite of cork/TetraPak (R) were studied. Measurements of isothermal charge and discharge currents were made for natural cork samples in different directions (axial, radial and tangential cuts). The isothermal current characteristics and the samples conductivity were investigated under different conditions (electric field, temperature and environmental conditions: in air at ambient relative humidity (RH), dry air and vacuum), also the samples could be or not conditioned (dried in vacuum or in a P2O5 atmosphere at room temperature). From these results the influence of water on the electrical properties of natural cork could be seen. In order to compare the three different cork materials a preliminary study was made. Isothermal charge and discharge currents and conductivity after 1h charging were measured and compared for different electric fields and temperature in air at ambient RH.

n/a

n/a

n/a

n/a

n/a

n/a

The thermoreactivity of a zinc acetate non-alkoxide solution used for the preparation of ZnO-based thin films was investigated in the temperature range 20-600°C by TG-DTA, XRD and SEM data. We found that the formation in air of ZnO crystallites from the sol-gel precursor occurs above 150°C simultaneously with the decomposition of an intermediary compound, most probably carbonate hydroxide (sciante and/or hydrozincite). At 200°C, the crystalline structure is well defined in terms of ZnO hexagonal lattice parameters, although residual organic compounds and water were not yet fully removed and an amorphous phase coexists. A kinetic investigation on the thermal decomposition of sol-gel precursor from DTA data using Kissinger differential equation is also presented. Apparent activation energy values of about. 100 kJ mol-1 corresponding to the non-isothermal decomposition of solid precursors in the temperature range 170-250°C have been found.

Wavelengths and oscillator strengths for all dipole-allowed fine-structure transitions in Zr III have been calculated within the Multi-Configuration Dirac-Fock method with QED corrections. These transitions are included in the spectrum of some chemically peculiar stars, like the B-type star Lupi observed by the Hubble space telescope. The results are compared to existing experimental and semi-empirical data.

Wavelengths and oscillator strengths for all dipole-allowed fine-structure transitions in Zr III have been calculated within the Multi-Configuration Dirac-Fock method with QED corrections. These transitions are included in the spectrum of some chemically peculiar stars, like the B-type star Lupi observed by the Hubble space telescope. The results are compared to existing experimental and semi-empirical data. Corr

n/a

n/a

This paper describes the evaluation of different refractory compounds – SiO2, ZrO2 and Y2O3 –as face coats of investment casting shells for c-TiAl. The effect of the different refractories on the metal–mould interaction is studied in different aspects. Experimental results include characterisation of the constituents present at the metal/ mould interface, the segregation profiles of residual elements, namely oxygen, from the interface to the inner part of the samples, the extension and microhardness of the samples external hard case and the samples surface finishing.

Denitrification, or dissimilative nitrate reduction, is an anaerobic process used by some bacteria for energy generation. This process is important in many aspects, but its environmental implications have been given particular relevance. Nitrate accumulation and release of nitrous oxide in the atmosphere due to excess use of fertilizers in agriculture are examples of two environmental problems where denitrification plays a central role. The reduction of nitrate to nitrogen gas is accomplished by four different types of metalloenzymes in four simple steps: nitrate is reduced to nitrite, then to nitric oxide, followed by the reduction to nitrous oxide and by a final reduction to dinitrogen. In this manuscript we present a concise updated review of the bioinorganic aspects of denitrification. (c) 2006 Elsevier Inc. All rights reserved.