{Aluminophosphate glasses belonging to the Li2O-BaO-Al 2O3- La2O3-P2O 5 system doped with Tb3+ were prepared and investigated. Methods as Induced Coupled Plasma-Mass Spectrometry (ICP-MS), Induced Coupled Plasma-Atomic Emission Spectroscopy (ICP-AES) and X-ray diffraction (XRD) have been used to establish the elemental composition of these vitreous materials. The influence of the Tb3+ ions on the optical properties of the phosphate glasses has been investigated in relation with the structural characteristics of the vitreous matrix. The optical behavior has been studied by ultra-violet-visible (UV-Vis) spectroscopy, revealing electronic transitions specific for terbium ions. Fluorescence spectroscopy measurements have been performed by excitation in the UV and visible domains (377 nm and 488 nm) which resulted in the most significant fluorescence peaks in the Vis domain (540 and 547 nm). Structural information via vibration modes were provided by Fourier Transform Infrared (FTIR) absorption spectra in the 400-4000 cm-1 range. Absorption peaks specific for the vitreous phosphate matrix were put in evidence as P-O-P symmetrical and asymmetrical stretching vibration modes, P-O-P bend, PO2- symmetrical and asymmetrical stretching vibration modes

The work deals with optical and structural properties of aluminophosphate glasses from Li2O-BaO-Al2O3-La 2O3-P2O5 system containing Sm 3 + and Eu3 + ions. X-ray fluorescence (XRF) has been used to establish the elemental composition of these materials. The influence of Sm3 + and Eu3 + ions on the optical properties of these glasses has been investigated in relation with their structural characteristics. The optical behavior of these materials has been studied by ultra-violet-visible (UV-Vis) spectroscopy, revealing absorption maxima specific to the doping ions. Structural information via vibration modes was provided by Fourier Transform Infrared (FTIR) absorption spectra evidenced as POP symmetrical and asymmetrical stretching vibration modes, POP bend, PO 2- symmetrical and asymmetrical stretching vibration modes, PO stretching vibration mode and POH water absorbance. Raman spectra acquired by 514.5 nm laser excitation disclosed peaks specific to metaphosphate network. Information about the elemental compositional homogeneity of Sm 3 + and Eu3 +-containing glasses as well as about the defects of the doped-glasses is revealed by scanning electron microscopy/energy dispersive spectrometry (SEM/EDS). Fluorescence spectroscopy measurements put in evidence important fluorescence peaks found at 596 nm and 643 nm for Sm 3 + ions in phosphate matrix and 611 nm and 700 nm in the case of Eu3 +-doped glass. © 2013 Elsevier B.V.

Thin-films of copper oxide Cu O were produced by thermal oxidation of metallic copper (Cu) at different temperatures (150-450 C). The films produced at temperatures of 200, 250 and 300 C showed high Hall motilities of 2.2, 1.9 and 1.6 cm V s , respectively. Single Cu O phases were obtained at 200 C and its conversion to CuO starts at 250 C. For lower thicknesses 40 nm, the films oxidized at 250 C showed a complete conversion to CuO phase. Successful thin-film transistors (TFTs) were produce by thermal oxidation of a 20 nm Cu film, obtaining p-type Cu O (at 200 C) and CuO (at 250 C) with On/Off ratios of 6 10 and 1 10 , respectively. © 2005-2012 IEEE.

Electrospun fibers of poly[(9,9-dioctylfluorenyl-2,7-diyl)-co-bithiophene] (F8T2) with exceptional electro-optical performance are obtained. The I/T characteristics measured in fibers with 7-15 μm diameter and 1 mm length show a semiconductor behavior; their thermal activation energy is 0.5 eV and the dark conductivity at RT is 5 × 10-9 (Ω cm)-1. Besides exhibiting a photosensitivity of about 60 under white light illumination with a light power intensity of 25 mW · cm-2, the fibers also attain RT photoluminescence in the cyan, yellow, and red wavelength range under ultraviolet, blue, and green light excitation, respectively. Optical microscope images of F8T2 reveal homogeneous electrospun fibers, which are in good agreement with the uniformly radial fluorescence observed. The production of electrospun fibers from poly[(9,9-dioctylfluorenyl-2,7-diyl)-co-bithiophene] (F8T2) obtained without a carrier polymer is reported. The obtained fibers are shown to have properties suitable for organic fiber photovoltaic and sensors applications. Copyright © 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.