The crystallization kinetics of a glass with a molar composition 40BaO-20ZnO-30B2O3-10SiO2 was investigated. The kinetic parameters, activation energy for crystallization (Ec) and Avrami exponent (n), were evaluated under non-isothermal conditions using the results obtained by differential thermal analysis (DTA) performed at different heating rates. DTA curves exhibited two overlapping exothermic peaks associated with the crystallization of the glass. Barium borate (BaB4O 7) was the first crystalline phase to be formed and it was followed by the formation of barium zinc silicate (BaZnSiO4), as identified by XRD. For the first exothermic peak, when the fraction of crystallization (χ) increased from 0.1 to 0.9, the local activation energy (E c(χ)) decreased from 700 to 500 kJ/mol, while for the second exothermic peak, Ec(χ) slightly increased from 490 to 570 kJ/mol. For the range of 0.1 < χ < 0.9, the local Avrami exponent (n(χ)) increased from ∼1 to 1.4 for the first exothermic peak and it decreased from ∼1.7 to 1.4 for the second exothermic peak. Observation by SEM of the microstructure of sintered glass samples revealed that crystallization started at the surface of glass particles, with growth of lamellar crystallites, that together with some quasi-spherical nano-sized crystallites progressed towards the inside of the glass at the highest sintering temperatures. The change of the local activation energy with the fraction of crystallization suggested that a multi-step kinetic reaction took place during sintering and crystallization of the glass. © 2013 Elsevier B.V. All rights reserved.

... Title Elemental characterization of plants and soils in Panasqueira tungsten mining region Journal Journal of Soils and Sediments Volume 14, Issue 4 , pp 778-784 Cover Date 2014-04-01 DOI 10.1007 / s11368 - 013 - 0788 - x Print ISSN 1439-0108 Online ISSN 1614-7480 ...

... Title Elemental characterization of plants and soils in Panasqueira tungsten mining region Journal Journal of Soils and Sediments Volume 14, Issue 4 , pp 778-784 Cover Date 2014-04-01 DOI 10.1007 / s11368 - 013 - 0788 - x Print ISSN 1439-0108 Online ISSN 1614-7480 ...

With a 4f6 electronic configuration, europium ions in the trivalent charge state are known to be efficient activators in wide band gap matrices. Embedded in the aluminophosphate (Li2O-BaO-Al 2O3-La2O3-P2O 5) glasses the optically activated Eu3+ ions lead to intense room temperature orange/red luminescence with 16-23 Cd/m2 by using ultraviolet pumping. The as-prepared and heat treated europium doped glasses for temperatures below and above Tg were studied by room temperature Raman spectroscopy, absorption, photoluminescence excitation, temperature dependent and time dependent photoluminescence. When the samples are excited by 325 nm wavelength photons, an enhancement of the red luminescence intensity by ca. one order of magnitude was found to occur for temperatures between 14 K and 350 K, for all the doped glasses. On the other hand, by using resonant excitation on the 5L6 Eu3+ excited state (λexc 390 nm) the ion emission intensity was found to be nearly constant for temperatures up to 500 K. For higher temperatures a steeper decrease of the luminescence intensity occurs due to non-radiative competitive channels described by activation energies of ca. 235 meV and 450 meV by using 325 and 390 nm wavelength photons as excitation, respectively. The lifetime of the 5D0 level in these glasses is ca. 2.93 ms. A discussion of the thermal population and de-excitation mechanisms is performed. © 2013 Elsevier B.V.