Aqueous tape casting of low-k cordierite substrate: The influence of glass content
- Citation:
- Mei, S.a, Yang Ferreira Martins J. a J. M. "Aqueous tape casting of low-k cordierite substrate: The influence of glass content." Materials Science Forum. 455-456 (2004): 168-171.
Abstract:
Thick films of cordierite-based glass ceramics were prepared by aqueous tape casting from suspensions containing 80-wt% solids. The weight proportions of cordierite/glass ranged from 70/30 to 30/70 in order to investigate the effect of glass content on the rheological behaviour and on the microstructures and properties of the green tapes. Suspensions with 50 to 60-wt% glass content exhibited the lowest viscosity values among all the slurries investigated, while the green tape containing 30-wt% glass presented homogenous microstructures at both top and bottom surfaces, contrarily to the observations for the other compositions. The green densities increased with glass content. The sintered tapes (1150°C, 2h) containing 50 to 60-wt% glass exhibited the lowest values for the dielectric constant (∼5.2) and dielectric loss (∼0.002) at 1MHz.
Notes:
cited By 1
Recent Publications