Lapa, N. a, R. a Barbosa, S. a Camacho, R. C. C. b Monteiro, M. H. V. c Fernandes, and J. S. a Oliveira. "
Leaching behaviour of a glass produced from a MSWI bottom ash."
Materials Science Forum. 514-516 (2006): 1736-1741.
AbstractThis paper is mainly focused on the characterisation of a glass material (GM) obtained from the thermal treatment of a bottom ash (BA) produced at the Municipal Solid Waste (MSW) incineration plant of Valorsul. By melting the BA at 1400°C during 2 hours, and without using any chemical additives, a homogeneous black-coloured glass was obtained. The thermal and mechanical properties of this glass were characterised. The thermal expansion coefficient, measured by dilatometry, was 9-10 × 10-6 per °C and the modulus of rupture, determined by four-point bending test, was 75±6 MPa, which are similar values to those exhibited by commercial soda-lime-silica glasses used in structural applications. The chemical and the ecotoxicological leaching behaviour of the GM were also analysed. The GM was submitted to a leaching procedure composed of 15 sequential extraction cycles. A liquid/solid (L/S) ratio of 2 1/kg was applied in each cycle. The leachates were filtered through a membrane of PTFE (porosity: 0.45 μm). The filtered leachates were characterised for different chemical parameters and for an ecotoxicological indicator (bacterium Vibrio fischeri). The GM was also submitted to a microwave acidic digestion for the assessment of the total metal content. The crude BA was also submitted to the same experimental procedures. The GM showed levels of chemical emission and ecotoxicity for V. fischeri much lower than those determined for the crude BA. Similar characterisation studies will be pursued with the glass-ceramics produced by adequate thermal treatment of the glass, in order to investigate the effect of the crystallization on the final properties.
Lima, M. M. R. A., F. M. Braz Fernandes, and R. C. C. Monteiro. "
Study of the crystallization of a borosilicate glass."
Key Engineering Materials. 230-232 (2002): 157-160.
AbstractThe crystallization of a commercial borosilicate glass powder has been studied in the temperature range 750-900°C. Crystal growth was investigated by high temperature XRD and cristobalite precipitation was identified. Glass devitrification exhibited a characteristic incubation period that decreased with increasing temperature: 25-30 min at 750°C, 9-12 min at 775°C, 5-10 min at 810°C, and 0-5 min at 840°C. Cristobalite is an unfavorable transformation product in terms of thermal expansion behavior. The precipitation of cristobalite in sintered glass compacts was confirmed by dilatometric analysis, where the increase in thermal expansion coefficient due to the presence of cristobalite and its transition from the tetragonal to the cubic phase were verified. Correlation between the XRD results and the dilatometric data from sintered glass compacts showed the partial dissolution of cristobalite when the glass was heated at the highest temperatures.