n/a

This paper is mainly focused on the characterisation of a glass material (GM) obtained from the thermal treatment of a bottom ash (BA) produced at the Municipal Solid Waste (MSW) incineration plant of Valorsul. By melting the BA at 1400ºC during 2 hours, and without using any chemical additives, a homogeneous black-coloured glass was obtained. The thermal and mechanical properties of this glass were characterised. The thermal expansion coefficient, measured by dilatometry, was 9-10 x 10-6 per ºC and the modulus of rupture, determined by four-point bending test, was 75±6 MPa, which are similar values to those exhibited by commercial soda-lime-silica glasses used in structural applications. The chemical and the ecotoxicological leaching behaviour of the GM were also analysed. The GM was submitted to a leaching procedure composed of 15 sequential extraction cycles. A liquid/solid (L/S) ratio of 2 l/kg was applied in each cycle. The leachates were filtered through a membrane of PTFE (porosity: 0.45 8m). The filtered leachates were characterised for different chemical parameters and for an ecotoxicological indicator (bacterium Vibrio fischeri). The GM was also submitted to a microwave acidic digestion for the assessment of the total metal content. The crude BA was also submitted to the same experimental procedures. The GM showed levels of chemical emission and ecotoxicity for V. fischeri much lower than those determined for the crude BA. Similar characterisation studies will be pursued with the glass-ceramics produced by adequate thermal treatment of the glass, in order to investigate the effect of the crystallization on the final properties.

n/a

n/a

A uniform shiny black-coloured glass was obtained using bottom ash produced by a Portuguese municipal solid waste incinerator (MSWI). The bottom ash was the single batch material used in the formation of the glass, which was obtained by vitrification of the solid waste at 1400 °C for 2 h. Under these conditions, a homogeneous melt with an appropriate viscosity to be shaped was obtained, indicating the suitability of this waste material to be employed in the development of vitreous products. The characterization of the resulting glass was performed in order to assess its structural, physical, mechanical, thermal and chemical features. The glass had a density of 2.69 g cm -3, a hardness of 5.5 GPa, a fracture strength of 75 MPa, a thermal expansion coefficient of 9.5 × 10-6 °C-1 and it exhibited a very good chemical stability. In summary, the MSWI bottom ash glass has good mechanical and chemical properties and may, therefore, be used in several applications, particularly as a construction material. © 2005 Elsevier B.V. All rights reserved.

This paper presents the effect of post-heating temperature and atmosphere on the electrical and optical properties of ZnO:Al thin films prepared by the sol-gel method. The electrical properties of the n-type semiconductor thin films showed that for the final films, the values of carrier concentration ranged between 2.76 and 9.96 × 1019 cm- 3, the Hall mobility values between 7 and 34.1 cm2/V s and the resistivity values between 2.9 × 10- 3 and 5.0 × 10- 2 Ω cm, depending on the processing conditions. For the thin film doped with 2 wt.% Al, preheated at 400 °C and post-heated for 1 h in air at 600 °C, a resistivity of 2.9 × 10- 3 Ω cm has been reached after annealing under a reducing atmosphere of forming gas. The optical transmittance spectra of the only post-heated films and of the post-heated and annealed films showed a good transmittance (75-90%) within the visible wavelength region and some small effects of Al-doping concentration and annealing treatment in forming gas. © 2005 Elsevier B.V. All rights reserved.