Ana Rita C. Duarte

Electrospun structures were proposed as scaffolds owing to their morphological and structural similarities with the extracellular matrix found in many native tissues. These fibrous structures were also proposed as drug release systems by exploiting the direct dependence of the release rate of a drug on the surface area. An osteogenic differentiation factor, dexamethasone (DEX), was incorporated into electrospun polycaprolactone (PCL) nanofibers at different concentrations (5, 10, 15 and 20 wt.{%} polymer), in a single-step process. The DEX incorporated into the polymeric carrier is in amorphous state, as det ermined by DSC, and does not influence the typical nanofibers morphology. In vitro drug release studies demonstrated that the dexamethasone release was sustained over a period of 15 days. The bioactivity of the released dexamethasone was assessed by cultivating human bone marrow mesenchymal stem cells (hBMSCs) on 15 wt.{%} DEX-loaded PCL NFMs, under dexamethasone-absent osteogenic differentiation medium formulation. An increased concentration of alkaline phosphatase and deposition of a mineralized matrix was observed. Phenotypic and genotypic expression of osteoblastic-specific markers corroborates the osteogenic activity of the loaded growth/differentiation factor. Overall data suggests that the electrospun biodegradable nanofibers can be used as carriers for the sustained release of growth/differentiation factors relevant for bone tissue engineering strategies. © 2010 Elsevier Ltd.

A marine derived polysaccharide, ulvan, extracted from green algae, was combined with poly-d, l-lactic acid (PDLLA) in order to produce a novel scaffold for bone tissue engineering applications. Three dimensional (3D) scaffolds of PDLLA loaded with ulvan particles were originally prepared by subcritical fluid sintering with carbon dioxide at 40°C and 50 bar. Prepared matrixes were characterized in order to validate their suitability to be used as scaffolds for bone tissue regeneration. Characterization included micro-computed tomography, mechanical compression testing, water uptake and degradation testing, and cytotoxicity assays. In addition, ulvan particles loaded with dexamethasone, were also dispersed within the PDLLA matrix and the respective release profile from the samples was evaluated. Prepared PDLLA scaffolds enriched with ulvan particles demonstrated appropriate physicochemical and cytocompatible features to be used for the envisaged applications. On the other hand, the release of dexamethasone from ulvan particles embedded within the PDLLA matrix revealed that the designed systems can be potentially suitable for localized drug delivery. These results further contribute to the establishment of ulvan as a potential novel biomaterial. © 2012 Elsevier B.V. All rights reserved.

Supercritical fluid technology has proven to be useful for many pharmaceutical applications and is now emerging as an alternative to conventional processes for the preparation of 3D structures and injectable particles suitable to be used in regenerative medicine. A current overview of the basic principles underlying supercritical fluid technology, the state of the art and future potential of this technology are presented.

Phase equilibrium measurements of single and mixed organic clathrate hydrates with hydrogen were determined within a pressure range of 2.0-14.0. MPa. The organic compounds studied were furan, 2,5-dihydrofuran, tetrahydropyran, 1,3-dioxolane and cyclopentane. These organic compounds are known to form structure II clathrate hydrates with water. It was found that the addition of hydrogen to form a mixed clathrate hydrate increases the stability compared to the single organic clathrate hydrates. Moreover, the mixed clathrate hydrate also has a much higher stability compared to a pure hydrogen structure II clathrate hydrate. Therefore, the organic compounds act as promoter materials. The stabilities of the single and mixed organic clathrate hydrates with hydrogen showed the following trend in increasing order: 1,3-dioxolane {\textless} 2,5-dihydrofuran {\textless} tetrahydropyran {\textless} furan {\textless} cyclopentane, indicating that both size and geometry of the organic compound determine the stability of the clathrate hydrates. © 2011 Elsevier B.V.

The possibility to fabricate marine collagen porous structures crosslinked with genipin under high pressure carbon dioxide is investigated. Collagen from shark skin is used to prepare pre-scaffolds by freeze-drying. The poor stability of the structures and low mechanical properties require crosslinking of the structures. Under dense CO 2 atmosphere, crosslinking of collagen pre-scaffolds is allowed for 16 h. Additionally, the hydrogels are foamed and the scaffolds obtained present a highly porous structure. In vitro cell culture tests performed with a chondrocyte-like cell line show good cell adherence and proliferation, which is a strong indication of the potential of these scaffolds to be used in tissue cartilage tissue engineering. The development of an optimized processing technique for the preparation of stable structures from marine origin collagen is described. The samples are processed under a dense carbon dioxide atmosphere that promotes crosslinking and enhances the morphology of the 3D architectures obtained. © 2013 WILEY-VCH Verlag GmbH {&} Co. KGaA, Weinheim.

The possibility of preparation of ophthalmic drug delivery systems using compressed anti-solvent technology was evaluated. Eudragit RS 100 and RL 100 were used as drug carriers, acetazolamide was the model drug processed. Compressed anti-solvent experiments were carried out as a semi-continuous or a batch operation from a liquid solution of polymer(s) + solute dissolved in acetone. Both techniques allowed the recovery of composite particles, but the semi-continuous operation yielded smaller and less aggregated populations than the batch operation. The release behaviour of acetazolamide from the prepared microparticles was studied and most products exhibited a slower release than the single drug. Moreover, the release could be controlled to some extent by varying the ratio of the two Eudragit used in the formulation and by selecting one or the other anti-solvent technique. Simple diffusion models satisfactorily described the release profiles. Composites specifically produced by semi-continuous technique have a drug release rate controlled by a diffusion mechanism, whereas for composites produced by the batch operation, the polymer swelling also contributes to the overall transport mechanism. © 2006 Elsevier B.V. All rights reserved.

The possibility of preparation of ophthalmic drug delivery systems using compressed anti-solvent technology was evaluated. Eudragit RS 100 and RL 100 were used as drug carriers, acetazolamide was the model drug processed. Compressed anti-solvent experiments were carried out as a semi-continuous or a batch operation from a liquid solution of polymer(s) + solute dissolved in acetone. Both techniques allowed the recovery of composite particles, but the semi-continuous operation yielded smaller and less aggregated populations than the batch operation. The release behaviour of acetazolamide from the prepared microparticles was studied and most products exhibited a slower release than the single drug. Moreover, the release could be controlled to some extent by varying the ratio of the two Eudragit used in the formulation and by selecting one or the other anti-solvent technique. Simple diffusion models satisfactorily described the release profiles. Composites specifically produced by semi-continuous technique have a drug release rate controlled by a diffusion mechanism, whereas for composites produced by the batch operation, the polymer swelling also contributes to the overall transport mechanism. © 2006 Elsevier B.V. All rights reserved.

© 2017 Elsevier B.V. Porous polymeric materials are studied in tissue engineering, because they can act as support for cell proliferation and as drug delivery vehicles for regeneration of tissues. Hydrogel foaming with supercritical CO 2 is a suitable alternative for the creation of these structures, since it avoids the use of organic solvents and high temperature in the processing. In this work, $\beta$-glucans were used as raw materials to create hydrogels due to their easily gelation and biological properties. The enhancement of porosity was generated by a fast decompression after keeping the hydrogels in contact with CO 2 . The effect of the processing conditions and type of $\beta$-glucan in the final properties was assessed regarding morphological and mechanical properties. Finally, the ability of these materials to sustainably deliver dexamethasone was evaluated. The scaffolds had good morphology and provided a controlled release, thus being suitable to be used as scaffolds and drug delivery vehicles.

Supercritical fluid impregnation was tested to prepare a new scaffold loaded with a bioactive compound. Dexamethasone is used in osteogenic media to direct the differentiation of stem cells towards the osteogenic lineage. Dexamethasone was impregnated in chitosan scaffolds at different operating conditions, in order to optimize the impregnation process. Pressure and temperature affect the carbon dioxide density and influence the swelling of the polymer and the drug solubility in the fluid phase, therefore these are two important parameters that were studied in this work. Chitosan sponges prepared by freeze drying were impregnated with the active compound at pressures from 8.0 up to 14.0 MPa and temperatures from 35 up to 55 °C. The effect of the impregnation contact time (3 h and 6 h) was also evaluated. From the experiments performed we can conclude that the yield of impregnation is lower when increasing pressure and temperature. The contact time will mainly influence the amount of drug impregnated in the scaffold and for higher contact times the impregnation yield is also higher. Scanning electron microscopy shows particles of dexamethasone in the bulk of the scaffold, which confirms the feasibility of the supercritical fluid impregnation technology for the preparation of delivery devices. The loading capacity of the scaffolds was determined by spectroscopic analysis and the highest loading was achieved for the experiments performed at 8.0 MPa and 35 °C. Furthermore, in vitro drug release studies were carried out and the results show that dexamethasone was sustainably released. Supercritical fluid impregnation proved to be feasible for the preparation of a drug delivery system for bone tissue engineering purposes. © 2008 Elsevier Ltd. All rights reserved.

Ethylcellulose/methylcellulose blends were produced using different precipitation techniques and impregnated with naproxen, a non-steroidal anti-inflammatory drug (NSAID). Solvent-evaporation technique was used not only for the preparation of ethylcellulose/methylcellulose microspheres but also to encapsulate naproxen. Supercritical fluid (SCF) impregnation was also performed to prepare naproxen loaded microspheres. The microspheres, impregnated by the SCF technique, were prepared both by solvent-evaporation and by a supercritical antisolvent (SAS) process. In vitro release profiles at pH 7.4 and 1.2, of naproxen-loaded microspheres were evaluated and the results were modelled Fick's law of diffusion and Power law. Miscrospheres prepared by supercritical antisolvent have a higher loading capacity and present a slower release profile. The systems studied present a release mechanism controlled by drug diffusion which complies Fick's law of diffusion. © 2005 Elsevier B.V. All rights reserved.

The supercritical antisolvent (SAS) technique was used to prepare ethyl cellulose/methyl cellulose blends, two biocompatible polymers commonly used as drug carriers in controlled delivery systems. Ethyl cellulose is widely used as a drug carrier. The drug release of the delivery devices can be controlled to some extent by addition of a water-soluble or water swellable polymer, such as methyl cellulose. This leads to the solubility enhancement of poorly water-soluble molecules. SAS experiments were carried out at different operational conditions and microspheres with mean diameters ranging from 5 to 30 $μ$m were obtained. The effect of CO2 and liquid flow, temperature and pressure on particle size and particle size distribution was evaluated. The microspheres were precipitated from a mixture of dichloromethane (DCM) and dimethylsulfoxide (DMSO) (4:1 ratio). The best process conditions for this mixture were according to our study 40°C and 80 bar. © 2006 Elsevier B.V. All rights reserved.

Aerogels are a special class of ultra-light porous materials with growing interest in biomedical applications due to their open pore structure and high surface area. However, they usually lack macroporosity, while mesoporosity is typically high. In this work, carbon dioxide induced gelation followed by expansion of the dissolved CO{\textless}inf{\textgreater}2{\textless}/inf{\textgreater} was performed to produce hybrid calcium-crosslinked alginate-starch hydrogels with dual meso- and macroporosity. The hydrogels were subjected to solvent exchange and supercritical drying to obtain aerogels. Significant increase in macroporosity from 2 to 25{%} was achieved by increasing expansion rate from 0.1 to 30 bar/min with retaining mesoporosity (BET surface and BJH pore volume in the range 183-544m{\textless}sup{\textgreater}2{\textless}/sup{\textgreater}/g and 2.0-6.8cm{\textless}sup{\textgreater}3{\textless}/sup{\textgreater}/g, respectively). In vitro bioactivity studies showed that the alginate-starch aerogels are bioactive, i.e. they form hydroxyapatite crystals when immersed in a simulated body fluid solution. Bioactivity is attributed to the presence of calcium in the matrix. The assessment of the biological performance showed that the aerogels do not present a cytotoxic effect and the cells are able to colonize and grow on their surface. Results presented in this work provide a good indication of the potential of the alginate-starch aerogels in biomedical applications, particularly for bone regeneration.

The aim of this study was to evaluate the possibility of preparing starch-based porous matrixes using supercritical fluid technology. Supercritical immersion precipitation technique was used to prepare scaffolds of a polymeric blend of starch and poly(l-lactic acid) for tissue engineering purposes.Immersion precipitation experiments were carried out at different operational conditions and highly porous and interconnected scaffolds were obtained. Two organic solvents, dichloromethane and chloroform were tested, and from the results obtained chloroform was the more favourable for the process. The effect of polymer solution concentration (5 up to 20 wt{%}), temperature (35 up to 55 °C) and pressure (100 up to 200 bar) in the SPLA (50:50 wt{%}) membrane morphology, porosity and interconnectivity was evaluated. All the conditions tested were in the region of total miscibility between the organic solvent and carbon dioxide. Additionally, a blend with a different starch-poly(l-lactic acid) ratio (30:70 wt{%}) was tested. Bicontinuous structures were formed indicating that the L-L demixing process that governs the phase inversion is the spinodal decomposition. © 2008 Elsevier B.V. All rights reserved.

The aim of this study was to develop a new process for the production of bioactive 3D scaffolds using a clean and environmentally friendly technology. The possibility of preparing composite scaffolds of Bioglass?? and a polymeric blend of starch and poly(l-lactic acid) (SPLA50) was evaluated. Supercritical phase-inversion technique was used to prepare inorganic particles loaded starch-based porous composite matrixes in a one-step process for bone tissue engineering purposes. Due to their osteoconductive properties some glasses and ceramics are interesting materials to be used for bone tissue engineering purposes; however their poor mechanical properties create the need of a polymeric support where the inorganic fraction can be dispersed. Samples impregnated with different concentrations of Bioglass?? (10 and 15{%} wt/wt polymer) were prepared at 200??bar and 55????C. The presence of Bioglass?? did not affect the porosity or interconnectivity of the polymeric matrixes. Dynamic mechanical analysis has proven that the modulus of the SPLA50 scaffolds increases when glass particles are impregnated within the matrix. In vitro bioactivity studies were carried out using simulated body fluid and the results show that a calcium-phosphate layer started to be formed after only 1??day of immersion. Chemical analysis of the apatite layer formed on the surface of the scaffold was performed by different techniques, namely EDS and FTIR spectroscopy and X-ray diffraction (XRD). The ion concentration in the simulated body fluid was also carried out by ICP analysis. Results suggest that a bone-like apatite layer was formed. This study reports the feasibility of using supercritical fluid technology to process, in one step, a porous matrix loaded with a bioactive material for tissue engineering purposes. ?? 2009 Elsevier B.V. All rights reserved.

Fast-dissolving delivery systems (FDDS) have received increasing attention in the last years. Oral drug delivery is still the preferred route for the administration of pharmaceutical ingredients. Nevertheless, some patients, e.g. children or elderly people, have difficulties in swallowing solid tablets. In this work, gelatin membranes were produced by electrospinning, containing an encapsulated therapeutic deep-eutectic solvent (THEDES) composed by choline chloride/mandelic acid, in a 1:2 molar ratio. A gelatin solution (30{%} w/v) with 2{%} (v/v) of THEDES was used to produce electrospun fibers and the experimental parameters were optimized. Due to the high surface area of polymer fibers, this type of construct has wide applicability. With no cytotoxicity effect, and showing a fast-dissolving release profile in PBS, the gelatin fibers with encapsulated THEDES seem to have promising applications in the development of new drug delivery systems.

Equilibrium solubility of acetazolamide, a carbonic-anhydrase inhibitor, in supercritical carbon dioxide in the presence of a cosolvent was measured by a static analytical method for three mole fractions of ethanol (5, 7.5, and 10) {%} at 313.0 K from (13.0 to 21.0) MPa and at 323.0 K from (13.0 to 21.0) MPa for a mole fraction of 5{%} ethanol The presence of a cosolvent (ethanol) was essential for the solubilization of the bioactive compound in supercritical carbon dioxide. The results obtained are useful for the design of supercritical processes with this drug. Experimental solubility data were correlated with two enhanced density-based models (Chrastil, I. Solubility of Solids in Supercritical Gases. J. Phys. Chem. 1982, 86, 3016-3021; Santiago, J. M.; Teja, A. S. The solubility of solids in supercritical fluids. Fluid Phase Equilib. 1999, 158-160, 501-510).

Carbon dioxide solubility in a natural biodegradable polymer, namely poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) and the diffusion coefficients are reported. Equilibrium solubility of dense carbon dioxide in PHBV was studied by a gravimetric method in a temperature range from 308 to 313 K and a pressure range from 10.0 to 15.0 MPa. The copolymer presented Fickian behavior and Fick's diffusion model was applied to determine the amount of carbon dioxide present in the samples after a predermined exposure time as well as the diffusion coefficients. Diffusion coefficients for the sorption under supercritical (sc) conditions and desorption at ambient conditions were determined and compared. To evaluate the influence of the HV content in the amount of maximum sorption degree of the polymer, different samples of PHBV copolymers were tested and the sorption curves are here presented. © 2006 Elsevier B.V. All rights reserved.

Equilibrium solubility of flurbiprofen, a nonsteroidal antiinflammatory agent, in supercritical carbon dioxide was measured by a static analytical method in the pressure range from (8.0 to 25.0) MPa, at temperatures of (303.0, 313.0, and 323.0) K. The cosolvent effect of ethanol in the solubility of the bioactive compound in supercritical carbon dioxide was investigated at 18 MPa and 313 K. The results obtained have a potential application in supercritical processes for this drug. Experimental solubility data were correlated with an empirical density-based Chrastil model.

Mass sorption and diffusion coefficients in one acrylate biocompatible copolymer contacted with supercritical (sc) carbon dioxide are reported. Equilibrium solubility of dense carbon dioxide in poly(methylmethacrylate-co-ethylhexylacrylate-co-ethyleneglycoldimethacr ylate) (P(MMA-EHA-EGDMA)) was studied by a gravimetric method in a temperature range from 308 to 323 K and a pressure range from 10.0 to 20.0 MPa. The cross-linked copolymer presented Fickian behavior and Fick's diffusion model was applied to determine the amount of carbon dioxide present and the diffusion coefficients. Diffusion coefficients for the sorption under supercritical conditions and desorption at ambient conditions were determined and compared. Samples of P(MMA-EHA-EGDMA) with different thickness were used for comparison of the maximum sorption degree. Polymerization conditions were also varied in order to evaluate the influence of the molecular weight of the copolymer in the CO2 sorption process. To investigate the possibility of impregnating this acrylate copolymer with an anti-inflammatory drug, a preliminary experiment was performed. © 2005 Elsevier B.V. All rights reserved.

In this work, blends of starch and poly-$ε$-caprolactone (PCL) doped with different concentrations of 1-butyl-3-methylimidazolium acetate ([BMIM]Ac) or 1-butyl-3-methylimidazolium chloride ([BMIM] Cl) were studied. The blends were characterized by mechanical analysis, infra-red spectroscopy (FTIR), differential scanning calorimetry (DSC) and dielectric relaxation spectroscopy (DRS), evaluating the IL doping effect. The samples were subjected to supercritical carbon dioxide foaming and the morphology of the structures was assessed. DSC shows a single glass transition and melting endotherm for foamed and unfoamed samples, having no effect upon IL doping, and DRS shows increased molecular mobility for blends with higher IL concentrations, and some hindrance for lower ones. The conductivity for SPCL doped with 30{%} [BMIM] Cl, before and after foaming, is comparable to the conductivity of the IL but exhibits more stable conductivity values, opening doors for applications as self-supported conductive materials. © 2014 the Partner Organisations.

The micronization of poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) from organic solutions using supercritical antisolvent (SAS) technique has been successfully achieved. SAS experiments were carried out at different operational conditions and microspheres with mean diameters ranging from 3 to 9 $μ$m were obtained. The effect of CO2 and liquid flow, temperature and pressure on particle size and particle size distribution was evaluated. The microspheres were precipitated from a dichloromethane (DCM) solution. The best process conditions for this mixture were, according to our study, 40 °C, 100 bar, 1 mL min-1 liquid flow and 10 L min-1 carbon dioxide flow. Experiments with polymers containing different HV percentages were carried out. The powders obtained became more spherical as the HV content decreased. © 2006 Elsevier B.V. All rights reserved.

Supercritical fluid impregnation was tested to prepare a new ophthalmic drug delivery device. Poly(methylmethacrylate-co-ethylhexylacrylate-co-ethyleneglycoldimethacr ylate), P(MMA-EHA-EGDMA) has been proposed by Mariz [M. Mariz, Preparação de uma lente intra-ocular dotada de um sistema de libertação controlada de fármaco, Master Thesis, Universidade de Coimbra, 1999] as a promising matrix to be used for intraocular delivery of anti-inflammatory drugs used in eye surgery. This matrix was successfully impregnated with flurbiprofen, a non-steroidal anti-inflammatory agent. The success of the impregnation was evaluated by scanning electron microscopy (SEM) analysis and also by in vitro drug release studies. The effect of some operating parameters was evaluated, namely, pressure and contact time. The operating pressure will influence both the solubility of the drug in the supercritical fluid but also the sorption degree of the polymeric matrix in the presence of carbon dioxide. The solubility of the drug in carbon dioxide and the sorption degree are reported in previous studies. A comparison between the batch and the semi-continuous impregnation process is also presented. The supercritical fluid impregnation proved to be feasible for the preparation of a new ophthalmic drug delivery system. The drug release profiles suggest that the drug can be released up to three months, which is a major advantage for the prevention of the inflammatory response after ophthalmic surgery. © 2007 Elsevier B.V. All rights reserved.