A laboratory-scale reactor system is built and operated to measure the kinetic of formation for single and mixed carbon dioxide-tetrahydrofuran hydrates. The T-cycle method, which is used to collect the kinetic data, is briefly discussed. For single carbon dioxide hydrate, the induction time decreases with the increase of the initial carbon dioxide pressure up to 2.96. MPa. Beyond this pressure, the induction time is becoming relatively constant with the increase of initial carbon dioxide pressure indicating that the liquid phase is completely supersaturated with carbon dioxide. Experimental results show that the inclusion of tetrahydrofuran reduces the induction time required for hydrate formation. These observations indicate hydrate nucleation process and onset growth are more readily to occur in the presence of tetrahydrofuran. In contrast, the presence of sodium chloride prolongs the induction time due to clustering of water molecules with the ions and the salting-out effects. It is also shown that the degree of subcooling required for hydrate formation is affected by the presence of tetrahydrofuran and sodium chloride in the hydrate forming system. The presence of tetrahydrofuran in the hydrate system significantly reduces the amount of carbon dioxide uptake. The apparent rate constant, k, for those systems are reported. © 2010.

n/a

n/a

The surfaces of cordierite and glass particles were modified by coating them with an alumina precursor using a precipitation process in the presence of urea. Scanning electron microscopy (SEM), high-resolution transmission electron microscopy, X-ray diffraction, electrophoresis, and rheological measurements were used to characterize the coated powders. SEM and transmission electron microscopy morphologies of the coated powders revealed that amorphous and homogeneous coatings have been formed around the particles. The morphology of the coated powders showed a coiled wormlike surface. The coating Al2O3 layer dominated the surface properties of the coated glass and cordierite powders. The influence of the coating layer on the processing ability of cordierite-based glass-ceramics substrates by tape casting was studied in aqueous media. It could be concluded that the coating of the powders facilitates the processing and yields green and sintered tapes with denser, more homogeneous microstructures compared with the uncoated powders.