Abstract This paper reports the first attempt of developing macro-scale auxetic structures based on re-entrant hexagon design from braided composite materials for civil engineering applications. Braided composite rods (BCRs) were produced and arranged as longitudinal and horizontal elements to produce three types of auxetic structures: (1) basic re-entrant hexagon structure, (2) basic structure modified by adding straight longitudinal elements and (3): structure-2 modified by changing structural angle. The influence of various material and structural parameters as well as structure type on Poisson's ratio and tensile properties was thoroughly investigated. The auxetic behaviour was found to strongly depend on the structural angle and straight elements, resulting in lower auxeticity with lower angles and in presence of straight elements. Material parameters influenced the auxetic behaviour to a lesser extent and a decrease in auxetic behaviour was noticed with increase in core fibre linear density and using stiffer fibres such as carbon. The reverse effect was observed in case of tensile strength and work of rupture. Among these structures, structure-3 exhibited good auxetic behaviour, balanced tensile properties, and high energy absorption capacity and their auxetic behaviour could be well predicted with the developed analytical model. Therefore, these novel structures present good potential for strengthening of civil structures.

Cathode ray tube glass waste was used to produce glass foams by a powder sintering route. The glass waste powder was mixed with small amounts (5 and 8 wt%) of coal fly ash, which acted as foaming agent, and the compacts of the mixed powders were heated at different sintering temperatures in the range 600–800 °C for various dwell times (30–120 min). The effect of the different processing conditions on the microstructural characteristics (porosity, pore size and pore size distribution), mechanical resistance and thermal conductivity of the produced foams was investigated. The volume of pores tended to increase with sintering temperature and time, and glass foams (with a porosity higher than 50 %) were only achieved after sintering at 750 °C. The average pore size increased with sintering temperature and dwell time, and pore growth was particularly accentuated at 800 °C, where coalescence of the pores occurred, with a consequent decrease in compressive strength. Selected combinations of the sintering temperature, dwell time and foaming agent led to glass foams with a satisfactory microstructural homogeneity, which exhibited mechanical strength and thermal conductivity values similar to commercial foams used as thermal insulating materials. © 2016, Springer Science+Business Media New York.

Abstract With the aim of characterising a commercially available epoxy adhesive used for fibre-reinforced polymers strengthening applications, when submitted to different environmental conditions, mainly thermal (TC), freeze–thaw (FT), and wet–dry (WD) cycles and immersion in pure (PW) and water with chlorides (CW) for periods of exposure that lasted up to 16 months, an experimental program was carried out. Several methodologies were used in its characterization, mainly the scanning electron microscope (SEM), dynamic mechanical analysis (DMA), standard tensile tests (STT) coupled with digital image correlation (DIC). In general the results revealed that the chemical composition was not affected by the environmental conditions. Nevertheless, it was verified through \{DMA\} and \{STT\} that the modulus of elasticity and tensile strength of the epoxy adhesive increased in the TC, while the specimens submitted to \{PW\} and \{CW\} faced a high degradation in terms of its mechanical properties. Eventually, the glass transition temperature (Tg) was not affected by the environmental conditions, apart from the specimens subjected to \{TC\} and FT, presenting a higher and lower Tg, respectively, when compared with the reference specimens.

n/a

Abstract Mixed-mode I+II fracture characterization of human cortical bone was analyzed in this work. A miniaturized version of the Single Leg Bending test (SLB) was used owing to its simplicity. A power law criterion was verified to accurately describe the material fracture envelop under mixed-mode I+II loading. The crack tip opening displacements measured by digital image correlation were used in a direct method to determine the cohesive law mimicking fracture behavior of cortical bone. Cohesive zone modeling was used for the sake of validation. Several fracture quantities were compared with the experimental results and the good agreement observed proves the appropriateness of the proposed procedure for fracture characterization of human bone under mixed-mode I+II loading.