{Aluminophosphate glasses belonging to the Li2O-BaO-Al 2O3- La2O3-P2O 5 system doped with Tb3+ were prepared and investigated. Methods as Induced Coupled Plasma-Mass Spectrometry (ICP-MS), Induced Coupled Plasma-Atomic Emission Spectroscopy (ICP-AES) and X-ray diffraction (XRD) have been used to establish the elemental composition of these vitreous materials. The influence of the Tb3+ ions on the optical properties of the phosphate glasses has been investigated in relation with the structural characteristics of the vitreous matrix. The optical behavior has been studied by ultra-violet-visible (UV-Vis) spectroscopy, revealing electronic transitions specific for terbium ions. Fluorescence spectroscopy measurements have been performed by excitation in the UV and visible domains (377 nm and 488 nm) which resulted in the most significant fluorescence peaks in the Vis domain (540 and 547 nm). Structural information via vibration modes were provided by Fourier Transform Infrared (FTIR) absorption spectra in the 400-4000 cm-1 range. Absorption peaks specific for the vitreous phosphate matrix were put in evidence as P-O-P symmetrical and asymmetrical stretching vibration modes, P-O-P bend, PO2- symmetrical and asymmetrical stretching vibration modes

The use of a vacuum double crystal spectrometer, coupled to an electron-cyclotron resonance ion source (ECRIS), allows to measure low-energy x-ray transitions energies in highly-charged ions with accuracies of the order of a few parts per million. We have used this installation to measure the 1s2p 1 P1 - 1s2 1 S0 diagram line and the 1s2s 3 S1 - 1s2 1 S0 forbidden M1 transition energies in helium-like argon, the 1s2s2p 2 P j 1s2 2s 2 S1/2 transitions in lithium-like argon and the 1s2s2 2p 1 P1 - 1s2 2s2 1 S0 transition in beryllium-like argon. These transition measurements have accuracies between 2 and 4 ppm depending on the line intensity. Thanks to the excellent agreement between the simulations and the measurements, we were also able to measure the transition width of all the allowed transitions. The results are compared to recent QED and relativistic many-body calculations.

The use of a vacuum double crystal spectrometer, coupled to an electron-cyclotron resonance ion source (ECRIS), allows to measure low-energy x-ray transitions energies in highly-charged ions with accuracies of the order of a few parts per million. We have used this installation to measure the 1s2p 1 P1 - 1s2 1 S0 diagram line and the 1s2s 3 S1 - 1s2 1 S0 forbidden M1 transition energies in helium-like argon, the 1s2s2p 2 P j 1s2 2s 2 S1/2 transitions in lithium-like argon and the 1s2s2 2p 1 P1 - 1s2 2s2 1 S0 transition in beryllium-like argon. These transition measurements have accuracies between 2 and 4 ppm depending on the line intensity. Thanks to the excellent agreement between the simulations and the measurements, we were also able to measure the transition width of all the allowed transitions. The results are compared to recent QED and relativistic many-body calculations.

We report the effect of a disperse carbon interlayer between the n-a-Si:H layer and an aluminium zinc oxide (AZO) back contact on the performance of amorphous silicon solar cells. Carbon was incorporated to the AZO film as revealed by x-ray photoelectron spectroscopy and energy-dispersive x-ray analysis. Solar cells fabricated on glass substrates using AZO in the back contact performed better when a disperse carbon interlayer was present in their structure. They exhibited an initial efficiency of 11%, open-circuit voltage Voc = 1.6 V, short-circuit current JSC = 11 mA cm -2 and a filling factor of 63%, that is, a 10% increase in the J SC and 20% increase in the efficiency compared to a standard solar cell. © 2013 National Institute for Materials Science.

In the present work one host natural matrix - agar - has been doped with magnesium triflate (Mg(CF3SO3)2) with the goal of developing electrolytes for the fabrication of solid-state devices. The resulting samples have been represented by the notation Agar nMg(CF3SO3)2, where n represents the percentage of the magnesium triflate salt proportion in the electrolyte samples. The samples investigated, with n between 0.00% and 37.56%, have been obtained as transparent and thin films. The samples have been characterized by conductivity measurements, thermal analysis, cyclic voltammetry, X-ray diffraction (XRD), and scanning electron microscopy (SEM). The agar-based electrolytes were also tested as ionic conductor in an electrochromic device with the following configuration: glass/indium tin oxide (ITO)/WO 3/agar-based electrolyte/CeO2-TiO2/ITO/glass. © 2013 Copyright Taylor and Francis Group, LLC.