Duarte AR, Mano JF, Reis RL. {Dexamethasone-loaded scaffolds prepared by supercritical-assisted phase inversion}. Acta Biomaterialia. 2009;5:2054-62.
AbstractThe aim of this study was to evaluate the possibility of preparing dexamethasone-loaded starch-based porous matrices in a one-step process. Supercritical phase inversion technique was used to prepare composite scaffolds of dexamethasone and a polymeric blend of starch and poly(l-lactic acid) (SPLA) for tissue engineering purposes. Dexamethasone is used in osteogenic media to direct the differentiation of stem cells towards the osteogenic lineage. Samples with different drug concentrations (5-15 wt.{%} polymer) were prepared at 200 bar and 55 °C. The presence of dexamethasone did not affect the porosity or interconnectivity of the polymeric matrices. Water uptake and degradation studies were also performed on SPLA scaffolds. We conclude that SPLA matrices prepared by supercritical phase inversion have a swelling degree of nearly 90{%} and the material presents a weight loss of ∼25{%} after 21 days in solution. Furthermore, in vitro drug release studies were carried out and the results show that a sustained release of dexamethasone was achieved over 21 days. The fitting of the power law to the experimental data demonstrated that drug release is governed by an anomalous transport, i.e., both the drug diffusion and the swelling of the matrix influence the release of dexamethasone out of the scaffold. The kinetic constant was also determined. This study reports the feasibility of using supercritical fluid technology to process in one step a porous matrix loaded with a pharmaceutical agent for tissue engineering purposes. © 2009 Acta Materialia Inc.
Duarte AR, Mano JF, Reis RL. {Perspectives on: Supercritical fluid technology for 3d tissue engineering scaffold applications}. Journal of Bioactive and Compatible Polymers. 2009;24:385-400.
AbstractSupercritical fluid technology has proven to be useful for many pharmaceutical applications and is now emerging as an alternative to conventional processes for the preparation of 3D structures and injectable particles suitable to be used in regenerative medicine. A current overview of the basic principles underlying supercritical fluid technology, the state of the art and future potential of this technology are presented.
Duarte AR, Mano JF, Reis RL. {Preparation of chitosan scaffolds loaded with dexamethasone for tissue engineering applications using supercritical fluid technology}. European Polymer Journal. 2009;45:141-8.
AbstractSupercritical fluid impregnation was tested to prepare a new scaffold loaded with a bioactive compound. Dexamethasone is used in osteogenic media to direct the differentiation of stem cells towards the osteogenic lineage. Dexamethasone was impregnated in chitosan scaffolds at different operating conditions, in order to optimize the impregnation process. Pressure and temperature affect the carbon dioxide density and influence the swelling of the polymer and the drug solubility in the fluid phase, therefore these are two important parameters that were studied in this work. Chitosan sponges prepared by freeze drying were impregnated with the active compound at pressures from 8.0 up to 14.0 MPa and temperatures from 35 up to 55 °C. The effect of the impregnation contact time (3 h and 6 h) was also evaluated. From the experiments performed we can conclude that the yield of impregnation is lower when increasing pressure and temperature. The contact time will mainly influence the amount of drug impregnated in the scaffold and for higher contact times the impregnation yield is also higher. Scanning electron microscopy shows particles of dexamethasone in the bulk of the scaffold, which confirms the feasibility of the supercritical fluid impregnation technology for the preparation of delivery devices. The loading capacity of the scaffolds was determined by spectroscopic analysis and the highest loading was achieved for the experiments performed at 8.0 MPa and 35 °C. Furthermore, in vitro drug release studies were carried out and the results show that dexamethasone was sustainably released. Supercritical fluid impregnation proved to be feasible for the preparation of a drug delivery system for bone tissue engineering purposes. © 2008 Elsevier Ltd. All rights reserved.
Duarte AR, Mano JF, Reis RL. {Preparation of starch-based scaffolds for tissue engineering by supercritical immersion precipitation}. Journal of Supercritical Fluids. 2009;49:279-85.
AbstractThe aim of this study was to evaluate the possibility of preparing starch-based porous matrixes using supercritical fluid technology. Supercritical immersion precipitation technique was used to prepare scaffolds of a polymeric blend of starch and poly(l-lactic acid) for tissue engineering purposes.Immersion precipitation experiments were carried out at different operational conditions and highly porous and interconnected scaffolds were obtained. Two organic solvents, dichloromethane and chloroform were tested, and from the results obtained chloroform was the more favourable for the process. The effect of polymer solution concentration (5 up to 20 wt{%}), temperature (35 up to 55 °C) and pressure (100 up to 200 bar) in the SPLA (50:50 wt{%}) membrane morphology, porosity and interconnectivity was evaluated. All the conditions tested were in the region of total miscibility between the organic solvent and carbon dioxide. Additionally, a blend with a different starch-poly(l-lactic acid) ratio (30:70 wt{%}) was tested. Bicontinuous structures were formed indicating that the L-L demixing process that governs the phase inversion is the spinodal decomposition. © 2008 Elsevier B.V. All rights reserved.
Duarte AR, Caridade SG, Mano J?, Reis RL. {Processing of novel bioactive polymeric matrixes for tissue engineering using supercritical fluid technology}. Materials Science and Engineering C. 2009;29:2110-5.
AbstractThe aim of this study was to develop a new process for the production of bioactive 3D scaffolds using a clean and environmentally friendly technology. The possibility of preparing composite scaffolds of Bioglass?? and a polymeric blend of starch and poly(l-lactic acid) (SPLA50) was evaluated. Supercritical phase-inversion technique was used to prepare inorganic particles loaded starch-based porous composite matrixes in a one-step process for bone tissue engineering purposes. Due to their osteoconductive properties some glasses and ceramics are interesting materials to be used for bone tissue engineering purposes; however their poor mechanical properties create the need of a polymeric support where the inorganic fraction can be dispersed. Samples impregnated with different concentrations of Bioglass?? (10 and 15{%} wt/wt polymer) were prepared at 200??bar and 55????C. The presence of Bioglass?? did not affect the porosity or interconnectivity of the polymeric matrixes. Dynamic mechanical analysis has proven that the modulus of the SPLA50 scaffolds increases when glass particles are impregnated within the matrix. In vitro bioactivity studies were carried out using simulated body fluid and the results show that a calcium-phosphate layer started to be formed after only 1??day of immersion. Chemical analysis of the apatite layer formed on the surface of the scaffold was performed by different techniques, namely EDS and FTIR spectroscopy and X-ray diffraction (XRD). The ion concentration in the simulated body fluid was also carried out by ICP analysis. Results suggest that a bone-like apatite layer was formed. This study reports the feasibility of using supercritical fluid technology to process, in one step, a porous matrix loaded with a bioactive material for tissue engineering purposes. ?? 2009 Elsevier B.V. All rights reserved.
Duarte AR, Mano JF, Reis RL. {Supercritical fluids in biomedical and tissue engineering applications: a review}. International Materials Reviews. 2009;54:214-22.
AbstractOver the past several years, the definition of a scaffold for tissue engineering has changed dramatically, from a material that acts only as an inert structural support for cell attachment to serving as a more complex and dynamic environment for tissue development. This paper is a review on the existing and on the new emerging techniques based on supercritical fluid technology for the preparation of scaffolds and particles for tissue engineering applications. Supercritical fluid technology has already proven to be feasible for many pharmaceutical applications and is now emerging as an alternative to conventional materials' processing methods for the preparation of three-dimensional structures and injectable particles suitable to be used in regenerative medicine. The basic principles underlying each technique are here presented as well as the advantages and disadvantages of each process. The state of the art is reviewed and the major conclusions of the studies reported in the literature are discussed.