A successful procedure for the in situ synthesis of silver nanoparticles by chemical reduction of a silver salt on cotton and wool textiles is reported herein. The synthesis can be advantageously performed in an aqueous system when compared with an ethanolic system. SEM studies confirmed the presence of silver nanoparticles on the treated textiles, and elemental analysis by ICP revealed that, for the aqueous system, up to 3 and 4 mg of silver per gram were deposited per gram of cotton and wool fabric, respectively. This represented an increase of up to 16-fold for cotton and 3-fold for wool compared with the ethanolic system. Thus, the difference between the aqueous and ethanolic systems was more evident for cotton, albeit more silver was deposited on wool samples in all conditions. An increase in the amount of reducing agent present resulted in more silver being deposited on the textiles when using an aqueous system. The use of water presents a great advantage for possible scale-up of the method. This simple method can be applied to produce textiles for biomedical applications or presenting conductive properties. (C) 2012 Elsevier B.V. All rights reserved.

Building energy management may simultaneously integrate multiple energy areas and sources of information. The coordination of synergies allow better-informed decisions, such as performing forecasts and adjustments of energy production and storage, while adapting electrical loads to off-peak times, when energy rates are lower. This work targets the improvement and optimization of energy management operations in buildings and large complexes, by introducing a conceptual model for supporting real-time advanced reasoning and inference towards efficient energy management.

Sintered silicon nitride (Si3N4) ceramic substrates were investigated as dielectric substrates for the growth of metal-like boron-doped nanocrystalline diamond (NCD) and microcrystalline diamond coatings via the Hot Filament Chemical Vapor Deposition (HFCVD) technique. The structural, electrical and chemical properties of both the ceramic substrates and the diamond coatings may potentiate their applicability in particular in harsh environments and highly demanding situations. Boron doping was achieved via a boron oxide solution in ethanol dragged into the reaction chamber with argon. The coatings were characterized by scanning elec- tron microscopy, UV $μ$-Raman scattering, X-ray diffraction, time-of-flight secondary ion mass spectroscopy, Brale indentation for adhesion evaluation and two-point contact probe for resistivity measurements. The HFCVD technique led to a maximal growth rate of about 1 $μ$m/h. Several metal-like boron doped diamond coatings were obtained. It was found that at lower substrate temperature, lower system pressure and higher methane concentration, the resistivity of the conducting NCD coatings is about 3 orders of magnitude higher when compared with samples obtained with higher substrate temperature, higher system pressure and lower methane concentration. Nevertheless, for every metal-like boron-doped coating the use of the Si3N4 ceramic substrate guaranteed a superior adhesion level. ©

Human articular cartilage functions under a wide range of mechanical loads in synovial joints, where hydrostatic pressure (HP) is the prevalent actuating force. We hypothesized that the formation of engineered cartilage can be augmented by applying such physiologic stimuli to chondrogenic cells or stem cells, cultured in hydrogels, using custom-designed HP bioreactors. To test this hypothesis, we investigated the effects of distinct HP regimens on cartilage formation in vitro by either human nasal chondrocytes (HNCs) or human adipose stem cells (hASCs) encapsulated in gellan gum (GG) hydrogels. To this end, we varied the frequency of low HP, by applying pulsatile hydrostatic pressure or a steady hydrostatic pressure load to HNC-GG constructs over a period of 3 weeks, and evaluated their effects on cartilage tissue-engineering outcomes. HNCs (10×10 6 cells/mL) were encapsulated in GG hydrogels (1.5{%}) and cultured in a chondrogenic medium under three regimens for 3 weeks: (1) 0.4 MPa Pulsatile HP; (2) 0.4 MPa Steady HP; and (3) Static. Subsequently, we applied the pulsatile regimen to hASC-GG constructs and varied the amplitude of loading, by generating both low (0.4 MPa) and physiologic (5 MPa) HP levels. hASCs (10×10 6 cells/mL) were encapsulated in GG hydrogels (1.5{%}) and cultured in a chondrogenic medium under three regimens for 4 weeks: (1) 0.4 MPa Pulsatile HP; (2) 5 MPa Pulsatile HP; and (3) Static. In the HNC study, the best tissue development was achieved by the pulsatile HP regimen, whereas in the hASC study, greater chondrogenic differentiation and matrix deposition were obtained for physiologic loading, as evidenced by gene expression of aggrecan, collagen type II, and sox-9; metachromatic staining of cartilage extracellular matrix; and immunolocalization of collagens. We thus propose that both HNCs and hASCs detect and respond to physical forces, thus resembling joint loading, by enhancing cartilage tissue development in a frequency- and amplitude-dependant manner. © Copyright 2012, Mary Ann Liebert, Inc.