Nuno Lapa

The present work aims to perform a multistep upgrading of chars obtained in the co-pyrolysis of PE, PP and PS plastic wastes, pine biomass and used tires. The quality of the upgraded chars was evaluated by measuring some of their physico-chemical properties in order to assess their valorisation as adsorbents’ precursors. The crude chars were submitted to a sequential solvent extraction with organic solvents of increasing polarity (hexane, mixture 1:1 v/v hexane:acetone and acetone) followed by an acidic demineralization procedure with 1 M HCl solution. The results obtained showed that the upgrading treatment allow the recovery of 63–81% of the pyrolysis oils trapped in the crude chars and a reduction in the char's ash content in the range of 64–86%. The textural and adsorption properties of the upgraded chars were evaluated and the results indicate that the chars are mainly mesoporous and macroporous materials, with adsorption capacities in the range of 3.59–22.2 mg/g for the methylene blue dye. The upgrading treatment allowed to obtain carbonaceous materials with quality to be reused as adsorbents or as precursors for activated carbon.

This paper is mainly focused on the characterisation of a glass material (GM) obtained from the thermal treatment of a bottom ash (BA) produced at the Municipal Solid Waste (MSW) incineration plant of Valorsul. By melting the BA at 1400ºC during 2 hours, and without using any chemical additives, a homogeneous black-coloured glass was obtained. The thermal and mechanical properties of this glass were characterised. The thermal expansion coefficient, measured by dilatometry, was 9-10 x 10-6 per ºC and the modulus of rupture, determined by four-point bending test, was 75±6 MPa, which are similar values to those exhibited by commercial soda-lime-silica glasses used in structural applications. The chemical and the ecotoxicological leaching behaviour of the GM were also analysed. The GM was submitted to a leaching procedure composed of 15 sequential extraction cycles. A liquid/solid (L/S) ratio of 2 l/kg was applied in each cycle. The leachates were filtered through a membrane of PTFE (porosity: 0.45 8m). The filtered leachates were characterised for different chemical parameters and for an ecotoxicological indicator (bacterium Vibrio fischeri). The GM was also submitted to a microwave acidic digestion for the assessment of the total metal content. The crude BA was also submitted to the same experimental procedures. The GM showed levels of chemical emission and ecotoxicity for V. fischeri much lower than those determined for the crude BA. Similar characterisation studies will be pursued with the glass-ceramics produced by adequate thermal treatment of the glass, in order to investigate the effect of the crystallization on the final properties.

This paper is mainly focused on the characterisation of a glass material (GM) obtained from the thermal treatment of a bottom ash (BA) produced at the Municipal Solid Waste (MSW) incineration plant of Valorsul. By melting the BA at 1400ºC during 2 hours, and without using any chemical additives, a homogeneous black-coloured glass was obtained. The thermal and mechanical properties of this glass were characterised. The thermal expansion coefficient, measured by dilatometry, was 9-10 x 10-6 per ºC and the modulus of rupture, determined by four-point bending test, was 75±6 MPa, which are similar values to those exhibited by commercial soda-lime-silica glasses used in structural applications. The chemical and the ecotoxicological leaching behaviour of the GM were also analysed. The GM was submitted to a leaching procedure composed of 15 sequential extraction cycles. A liquid/solid (L/S) ratio of 2 l/kg was applied in each cycle. The leachates were filtered through a membrane of PTFE (porosity: 0.45 µm). The filtered leachates were characterised for different chemical parameters and for an ecotoxicological indicator (bacterium Vibrio fischeri). The GM was also submitted to a microwave acidic digestion for the assessment of the total metal content. The crude BA was also submitted to the same experimental procedures. The GM showed levels of chemical emission and ecotoxicity for V. fischeri much lower than those determined for the crude BA. Similar characterisation studies will be pursued with the glass-ceramics produced by adequate thermal treatment of the glass, in order to investigate the effect of the crystallization on the final properties.