Space charge studies in LDPE using combined isothermal and non-isothermal current measurements

Citation:
Lanca, M. C., E. R. Neagu, R. M. Neagu, C. J. Dias, J. N. Marat-Mendes, and D. K. Das-Gupta, "Space charge studies in LDPE using combined isothermal and non-isothermal current measurements", Ieee Transactions on Dielectrics and Electrical Insulation, vol. 11, no. 1, pp. 25-34, 2004.

Abstract:

Using a recently developed procedure combining isothermal and non-isothermal current measurements space charge trapping and transport in LDPE was successfully studied. Unaged, thermally and electrically aged samples were investigated. The samples were conditioned before each measurement in order to obtain reproducible results. In the non-isothermal measurements appeared a broad peak (40degreesC to 50degreesC) that was possible to decompose into two or three peaks (35, 45 and 65degreesC). At even higher temperature another peak was sometimes present (85degreesC) depending on the prior sample conditioning. The space charge is trapped near the surface in deep traps (maximum depth of approximate to 15 mum). Relaxation times, mobilities and activation energies have been calculated for different charging/discharging conditions. For unaged samples the reproducibility of the results was poor while for the aged polyethylene it was quite good, meaning that aging helps conditioning. In the electrically aged LDPE there is a decrease of conductivity and the broad peak of the non-isothermal spectra shows a slight shift towards higher temperatures when compared with the data found in the thermally aged polymer.

Notes:

n/a

Related External Link