João Pedro Veiga

Abstract The Monastery of Alcobaça houses in reserve the ceramic tiles that adorned the floor of the church's apse. These tiles were removed during rehabilitation works and many preserve part of their original fixing mortars. A comprehensive analysis of 21 samples was conducted using a multi-analytical approach (X-ray fluorescence, X-ray diffraction, scanning electron microscopy–energy-dispersive X-ray spectroscopy, μ-Raman spectroscopy, thermogravimetry–differential thermal analysis, optical microscopy, and colorimetry). Results suggest compositional variations in the samples from the back and sides of the ceramic tiles; however, the mineralogy and general characteristics of the aggregates remained consistent between the samples and are coherent with the local geology, suggesting a shared historical origin.

Fábrica de Loiça de Sacavém (ca. 1858–1994) was among the first to produce white earthenware in Portugal, becoming one of the country’s leading ceramic manufacturers during the late 19th to early 20th centuries. Research on white earthenware has accompanied the growing interest in post-industrial archaeology but is still poorly explored compared to more ancient ceramic productions. This study focused on the ceramic body, glazes, and colourants of tableware produced by Fábrica de Loiça de Sacavém during the first 50 years of its activity (1859–1910). A multi-analytical approach was selected to investigate the chemical and mineralogical composition of the ceramic body, glaze, and pigments using optical microscopy, variable-pressure scanning electron microscope energy-dispersive X-ray spectroscopy (VP-SEM-EDS), μ-Raman spectroscopy, μ-X-ray Diffraction (μ-XRD), and reflectance spectroscopy (hyperspectral image analysis). The studied tableware was produced with a Ca-poor siliceous–aluminous white earthenware ceramic body covered with transparent alkali lead or lead borosilicate glaze, and most colourants were complex Cr-based pigments. These results are in agreement with the little documental evidence from this period found in the manufacturer’s archives.

This paper presents a comprehensive study of the evidence for ancient tin mining at the Ervedosa mine (Vinhais, Portugal). The geological context of the site indicates a rich cassiterite (SnO2) deposit, which was subject to mining in the twentieth century. Some ancient mining and ore processing stone tools were recovered during the twentieth century mining operations, namely one hammer, one pounder, one flat anvil and five small tools used both as pounders and crushing anvils, evidencing prehistoric mining activities. XRF and SEM–EDS chemical analyses were performed on primary and secondary cassiterite samples from the mining site, demonstrating the abundance and chemical heterogeneity of the tin (Sn) ores. The stone tools can be ascribed to Bronze Age or, at the latest, Early Iron Age (2nd millennium to the first half of 1st millennium BCE) by comparison with similar tools from other Iberian and European archaeological contexts. High-resolution photogrammetric 3D models of the tools are made available in this study. The historical descriptions of the findings and the research made on the technical archives about the mine allowed correlating the tools to mining in a primary context, focused on rich quartz veins in granitic or greisen bedrock, rather than mining in a secondary context. XRF and SEM–EDS analyses performed on the stone material and on surface adherences support their identification as specific types of hard rocks, such as granite, amphibolite and quartzite, and allowed the detection of Sn-rich adherent particles, confirming their use for Sn-material processing. The potential relation between the cassiterite resources and the local later prehistoric (Bronze Age to Early Iron Age) settlement pattern is also discussed. The results raise awareness and provide relevant data about the existence of tin mining in primary contexts during later prehistoric times in the NW Iberian Peninsula.

The Palace of Knossos, located on the island of Crete, Greece, is one of Europe's most important archaeological sites, serving as a testament to the Minoan civilization. Situated near the Mediterranean Sea, it is in close proximity to the seaport, airport, and industrial areas. Decay products commonly found in historical monuments within or near urban areas, such as black crusts and salt efflorescence, are also prevalent at the Palace of Knossos. To better understand the characteristics of the type of deterioration compounds found on cement in historical reconstruction zones, as well as their possible relationship with factors influencing the deterioration process, a multi-analytical approach was designed for the study of these materials. The results indicate that the black crusts primarily consist of gypsum and carbonaceous matter. However, the efflorescence salts are predominantly composed of thenardite instead of halite, despite the palace's proximity to the coastal area. These results may contribute to ongoing and future maintenance and preservation efforts for the monument.

Bluish-grey limestones have been extensively used as ornamental stones for decoration purposes in buildings, as well as in works of art, and accordingly, have been the target of intense exploration. In Portugal, the Jurassic limestone massif known as the Maciço Calcário Estremenho (MCE), has been the source of grey-coloured ornamental stones, namely the Azul Valverde (one of the most well-known bluish-grey limestones) and Atlantic Blue varieties, both of which may undergo colour changes in outdoor environments. In this sense, it is important to understand the sudden colour change from bluish-grey to yellow/beige in the same limestone block in a quarry, or even, what happens to the colour when polished limestone is placed outdoors. This study was undertaken using various techniques, namely XRF (X-ray fluorescence spectrometry), XRD (X-ray diffraction), SEM (scanning electron microscopy), DTA–TG (differential thermal analysis/thermogravimetry) and colourimetry. Synchrotron radiation was also used at the European Synchrotron Radiation Facility (ESRF, Grenoble, France) where XANES (X-ray Absorption Near Edge Structure) spectra at Fe K-edge were collected to ascertain the speciation state of Fe in different coloured zones of the limestone, previously checked by EDXRF (energy dispersive X-ray fluorescence). The presence of Fe2+ and Fe3+ are responsible for the greyish and yellow/brown colour, respectively. On the other hand, the UV radiation from the sun causes a quickened and severe bleaching/fading on the dark blue/grey polished limestone.

Findings of Iron Age metallurgical activities related to tin metal and mining are very rare. In the present work, we present a detailed study of the Outeiro de Baltar hillfort, dated to the Late Iron Age/Early Roman period, located in a place where 20th century tin mining work took place. Elemental and microstructural analysis by portable, micro and wavelength dispersive X-ray fluorescence spectrometry (pXRF, micro-XRF and WDXRF) and scanning electron microscopy with energy dispersion spectrometer (SEM-EDS) showed that metallurgical debris found at the archaeological site is related to tin smelting and binary and ternary bronze productions. Analysis of the artefacts of diverse typologies found at the site showed that a variety of metals and alloys were in circulation and use. Samples of tin ores (cassiterite) from the region were analyzed for comparison with an archaeological tin slag from the site. The analytical results point to the production of tin metal using local cassiterite and the production of bronze by directly adding cassiterite into a smelting process. Furthermore, data of remote sensing (airborne Light Detection and Ranging (LiDAR) and historical aerial imagery) and Geographical Information System (GIS) mapping were combined with archival mining documentation and maps to retrieve a landscape context for the site. The study showed that the place of the Outeiro de Baltar hillfort (NW Iberia) was mined periodically over time.

Glass samples with a molar composition (64+x)ZnO-(16-x)B2O3-20SiO2, where x=0 or 1, were successfully synthesized using a melt-quenching technique. Based on differential thermal analysis data, the produced glass samples were submitted to controlled heat-treatments at selected temperatures (610, 615 and 620{\{}$\backslash$textdegree{\}}C) during various times ranging from 8 to 30h. The crystallization of willemite (Zn2SiO4) within the glass matrix was confirmed by means of X-ray diffraction (XRD) and scanning electron microscopy (SEM). Under specific heat-treatment conditions, transparent nanocomposite glass-ceramics were obtained, as confirmed by UV-vis spectroscopy. The influence of temperature, holding time and glass composition on crystal growth was investigated. The mean crystallite size was determined by image analysis on SEM micrographs. The results indicated an increase on the crystallite size and density with time and temperature. The change of crystallite size with time for the heat-treatments at 615 and 620{\{}$\backslash$textdegree{\}}C depended on the glass composition. Under fixed heat-treatment conditions, the crystallite density was comparatively higher for the glass composition with higher ZnO content. {\{}©{\}} 2016.

© 2016, Springer-Verlag Berlin Heidelberg.The glaze and in-glaze pigments of the historical nineteenth-century glazed tiles from the Pena National Palace (Sintra, Portugal) were characterized using a multi-analytical approach. Chemical composition and microstructural characterization were ascertained by µ-PIXE, µ-Raman, optical microscopy and VP-SEM–EDS. The manufacturing technique and colour palette in these tiles were found to be close to the ceramic pigments used in traditional majolica. The blue and purple colours derive from cobalt oxide and manganese oxide, respectively. A mixture of Pb–Sn–Sb yellow with cobalt oxide and iron oxide was used for green and dark yellow, respectively, while grey tonalities consist of a complex mixture of cobalt oxide, manganese oxide and Pb–Sn–Sb yellow in different proportions. Results obtained allowed the determination of the oxides and elements used in pigments as well as production techniques, resorting to traditional majolica manufacture, although the tiles were produced by the end of the nineteenth century.

© 2016 Elsevier B.V. All rights reserved.Different glasses based on the ZnO-B2O3-SiO2 system, with a ZnO content ≥ 60 mol{%} and a fixed SiO2 content (20 mol{%}), were synthesised using a melt-quenching method. Glass samples with zinc oxide concentrations as high as 65 mol{%} were prepared successfully without deteriorating the glass-forming ability. The glass samples were submitted to controlled heat-treatments, and the effect of the ZnO/B2O3 molar ratio on the formation of crystalline phases within the glass matrix was investigated by means of differential thermal analysis (DTA), X-ray diffraction (XRD) and scanning electron microscopy (SEM). DTA results indicated that the glass transition and the onset crystallization temperatures of the studied glasses tended to increase with the increment on the ZnO/B2O3 ratio. XRD data showed that the zinc binary crystalline phases, willemite (Zn2SiO4), a zinc orthosilicate, and zinc borate (Zn3B2O6) could be present in the crystallized glasses, depending on the heat-treatment conditions. The formation of willemite was promoted by an increasing ZnO/B2O3 ratio. Microstructural observations performed by SEM indicated that under controlled experimental parameters (glass composition, heat-treatment temperature and time) the precipitation of nanocrystals within the glass matrix can be achieved, resulting in transparent and translucent willemite glass-ceramics.

© 2016 Taylor {&} Francis.A laboratory-based methodology was designed to assess the bioreceptivity of glazed tiles. The experimental set-up consisted of multiple steps: manufacturing of pristine and artificially aged glazed tiles, enrichment of phototrophic microorganisms, inoculation of phototrophs on glazed tiles, incubation under optimal conditions and quantification of biomass. In addition, tile intrinsic properties were assessed to determine which material properties contributed to tile bioreceptivity. Biofilm growth and biomass were appraised by digital image analysis, colorimetry and chlorophyll a analysis. SEM, micro-Raman and micro-particle induced X-ray emission analyses were carried out to investigate the biodeteriorating potential of phototrophic microorganisms on the glazed tiles. This practical and multidisciplinary approach showed that the accelerated colonization conditions allowed different types of tile bioreceptivity to be distinguished and to be related to precise characteristics of the material. Aged tiles showed higher bioreceptivity than pristine tiles due to their higher capillarity and permeability. Moreover, biophysical deterioration caused by chasmoendolithic growth was observed on colonized tile surfaces.