Furtado, C., A. Arteiro, G. Catalanotti, J. Xavier, and P. P. Camanho. "Selective ply-level hybridisation for improved notched response of composite laminates." Composite Structures. 145 (2016): 1-14. AbstractWebsite

Abstract This work presents an experimental study on the effect of ply-level hybridisation on the tensile unnotched and notched response of composite laminates. In a first assessment, notched tests were performed on laminates with nominal ply thicknesses between 0.03 mm and 0.30 mm. From the understanding of the effect of ply thickness on the damage mechanisms that govern the notched response of laminates, the concept of ply-level hybridisation is introduced, which consists in combining plies of different grades. A uniform combination of thin and conventional plies resulted in a hybrid laminate with intermediate notched response. Selective hybridisation, where thin off-axis plies are combined with thicker 0° plies, resulted in a globally enhanced notched behaviour without compromising the unnotched and fatigue responses. This work clearly shows how ply-level hybridisation, when designed to trigger specific damage mechanisms, can be used to improve the notched response of composite laminates.

Fernández-Cabo, J. L., R. Widmann, M. Arce-Blanco, R. Crocetti, J. Xavier, and A. Majano-Majano. "Assessment of wire-frame analysis models of a historical planked timber arch." Proceedings of the Institution of Civil Engineers - Structures and Buildings. 168 (2015): 680-694. AbstractWebsite
n/a
Fernandes, A., J. Lousada, J. Morais, J. Xavier, J. Pereira, and P. Melo-Pinto. "Comparison between neural networks and partial least squares for intra-growth ring wood density measurement with hyperspectral imaging." Computers and Electronics in Agriculture. 94 (2013): 71-81. Abstract
n/a
Fernandes, A., J. Lousada, J. Morais, J. Xavier, J. Periera, and P. Melo-Pinto. "Measurement of intra-ring wood density by means of imaging VIS/NIR spectroscopy (hyperspectral imaging)." Holzforschung. 67 (2013): 59-65. Abstract
n/a
Fernandes, Pedro, José Sena-Cruz, José Xavier, Patrícia Silva, Eduardo Pereira, and José Cruz. "Durability of bond in NSM CFRP-concrete systems under different environmental conditions." Composites Part B: Engineering. 138 (2018): 19-34. AbstractWebsite

Abstract This paper addresses the durability of bond between concrete and carbon fibre reinforced polymer (CFRP) strips installed according to the near-surface mounted (NSM) technique (NSM CFRP-concrete systems) under the effects of two main groups of environmental conditions: (i) laboratory-based ageing conditions; (ii) real outdoor ageing conditions. The bond degradation was evaluated by carrying out direct pullout tests on aged specimens that were previously subjected to distinct environmental conditions for different periods of exposure. Moreover, the degradation of the mechanical properties of the involved materials was investigated. The digital image correlation (DIC) method was used to document the evolution of the deformation fields at the surface over the whole region of interest consisting of concrete and epoxy adhesive at the ligament region. This information supported the discussion about the evolution of the bond resistant mechanism developed in \{NSM\} CFRP-concrete specimens during testing, as well as the assessment of the bond quality of the system. In general, the results obtained from the durability tests conducted have shown that the different exposure environments, which may be considered as quite severe, did not result in significant damage on \{NSM\} CFRP-concrete system. The maximum decrease of about 12% on bond strength was obtained for real outdoor environments. Conversely, a maximum increase of 8% on bond strength was obtained on the specimens exposed to the temperature cycles between -15��C and +60��C. \{DIC\} allowed to document the stress transfer mechanisms established between the \{CFRP\} and the concrete substrate, revealing the crack patterns and the influence widths of the \{CFRP\} reinforcement strips, which were shown to be important for avoiding group effect when using multiple parallel strengthening \{CFRP\} strips.

Fernandes, R. M. R. P., J. A. G. Chousal, M. F. S. F. de Moura, and J. Xavier. "Determination of cohesive laws of composite bonded joints under mode II loading." Composites Part B: Engineering. 52 (2013): 269-274. Abstract