The present work refers to an X-ray microtomography experiment aiming at the elucidation of some aspects regarding particle distribution in SiC-particle-reinforced functionally graded aluminium composites.
Precursor composites were produced by rheocasting. These were then molten and centrifugally cast to obtain the
functionally graded composites. From these, cylindrical samples, around 1 mm in diameter, were extracted, which were then irradiated with a X-ray beam produced at the European Synchrotron Radiation Facility.
The 3-D images were obtained in edge-detection mode. A segmentation procedure has been adapted in order to
separate the pores and SiC particles from the Al matrix. Preliminary results on the particle and pore distributions are presented.