João Pedro Veiga

Abstract The Monastery of Alcobaça houses in reserve the ceramic tiles that adorned the floor of the church's apse. These tiles were removed during rehabilitation works and many preserve part of their original fixing mortars. A comprehensive analysis of 21 samples was conducted using a multi-analytical approach (X-ray fluorescence, X-ray diffraction, scanning electron microscopy–energy-dispersive X-ray spectroscopy, μ-Raman spectroscopy, thermogravimetry–differential thermal analysis, optical microscopy, and colorimetry). Results suggest compositional variations in the samples from the back and sides of the ceramic tiles; however, the mineralogy and general characteristics of the aggregates remained consistent between the samples and are coherent with the local geology, suggesting a shared historical origin.

The Palace of Knossos, located on the island of Crete, Greece, is one of Europe's most important archaeological sites, serving as a testament to the Minoan civilization. Situated near the Mediterranean Sea, it is in close proximity to the seaport, airport, and industrial areas. Decay products commonly found in historical monuments within or near urban areas, such as black crusts and salt efflorescence, are also prevalent at the Palace of Knossos. To better understand the characteristics of the type of deterioration compounds found on cement in historical reconstruction zones, as well as their possible relationship with factors influencing the deterioration process, a multi-analytical approach was designed for the study of these materials. The results indicate that the black crusts primarily consist of gypsum and carbonaceous matter. However, the efflorescence salts are predominantly composed of thenardite instead of halite, despite the palace's proximity to the coastal area. These results may contribute to ongoing and future maintenance and preservation efforts for the monument.

The Chalcolithic period in the Lisbon region, Portugal, is usually divided into three phases chronologically: the Early Chalcolithic, characterized by cylindrical corrugated cups, Full Chalcolithic by so-called acacia-leaf decoration, and Late Chalcolithic by Bell Beaker pottery. The aim of this research is to determine if Chalcolithic ceramic raw materials and production techniques have remained the same over time and whether the pottery is locally produced. Regarding the Lisbon region, 149 ceramic samples from four Chalcolithic settlements (Vila Nova de São Pedro, Penedo do Lexim, Espargueira and Baútas) were evaluated concerning textural, chemical and mineralogical compositions. Textural analysis was performed using optical microscopy, chemical characterization was achieved using micro-energy dispersive X-ray fluorescence spectrometry and mineralogical characterization was undertaken using X-ray powder diffraction and petrographic microscopy as main techniques. Results suggest that production techniques may have remained similar throughout all the Chalcolithic period, with firing temperatures between 700 and 800 °C. Multivariate analysis of results from chemical and mineralogical analyses suggests that multiple sources of raw materials must have been used in the manufacture of the pottery collected at the four Chalcolithic settlements.

Fábrica de Loiça de Sacavém (ca. 1858–1994) was among the first to produce white earthenware in Portugal, becoming one of the country’s leading ceramic manufacturers during the late 19th to early 20th centuries. Research on white earthenware has accompanied the growing interest in post-industrial archaeology but is still poorly explored compared to more ancient ceramic productions. This study focused on the ceramic body, glazes, and colourants of tableware produced by Fábrica de Loiça de Sacavém during the first 50 years of its activity (1859–1910). A multi-analytical approach was selected to investigate the chemical and mineralogical composition of the ceramic body, glaze, and pigments using optical microscopy, variable-pressure scanning electron microscope energy-dispersive X-ray spectroscopy (VP-SEM-EDS), μ-Raman spectroscopy, μ-X-ray Diffraction (μ-XRD), and reflectance spectroscopy (hyperspectral image analysis). The studied tableware was produced with a Ca-poor siliceous–aluminous white earthenware ceramic body covered with transparent alkali lead or lead borosilicate glaze, and most colourants were complex Cr-based pigments. These results are in agreement with the little documental evidence from this period found in the manufacturer’s archives.

© 2016, Springer-Verlag Berlin Heidelberg.The glaze and in-glaze pigments of the historical nineteenth-century glazed tiles from the Pena National Palace (Sintra, Portugal) were characterized using a multi-analytical approach. Chemical composition and microstructural characterization were ascertained by µ-PIXE, µ-Raman, optical microscopy and VP-SEM–EDS. The manufacturing technique and colour palette in these tiles were found to be close to the ceramic pigments used in traditional majolica. The blue and purple colours derive from cobalt oxide and manganese oxide, respectively. A mixture of Pb–Sn–Sb yellow with cobalt oxide and iron oxide was used for green and dark yellow, respectively, while grey tonalities consist of a complex mixture of cobalt oxide, manganese oxide and Pb–Sn–Sb yellow in different proportions. Results obtained allowed the determination of the oxides and elements used in pigments as well as production techniques, resorting to traditional majolica manufacture, although the tiles were produced by the end of the nineteenth century.

© 2016 Taylor {&} Francis.A laboratory-based methodology was designed to assess the bioreceptivity of glazed tiles. The experimental set-up consisted of multiple steps: manufacturing of pristine and artificially aged glazed tiles, enrichment of phototrophic microorganisms, inoculation of phototrophs on glazed tiles, incubation under optimal conditions and quantification of biomass. In addition, tile intrinsic properties were assessed to determine which material properties contributed to tile bioreceptivity. Biofilm growth and biomass were appraised by digital image analysis, colorimetry and chlorophyll a analysis. SEM, micro-Raman and micro-particle induced X-ray emission analyses were carried out to investigate the biodeteriorating potential of phototrophic microorganisms on the glazed tiles. This practical and multidisciplinary approach showed that the accelerated colonization conditions allowed different types of tile bioreceptivity to be distinguished and to be related to precise characteristics of the material. Aged tiles showed higher bioreceptivity than pristine tiles due to their higher capillarity and permeability. Moreover, biophysical deterioration caused by chasmoendolithic growth was observed on colonized tile surfaces.