Rodrigo Martins

In this work we studied the influence of the power density of hydrogen plasma on electrical and optical properties (Hall mobility, free carrier concentration, sheet resistance, optical transmittance and a.c. impedance) of indium zinc oxide films, aiming to determine their chemical stability. This is an important factor for the optimization of amorphous/nanocrystalline p-i-n hydrogenated silicon (a/nc-Si:H) solar cells, since they should remain chemically highly stable during the p layer deposition. To perform this work the transparent conductive oxide was exposed to hydrogen plasma at substrate temperature of 473 K, 87 Pa of pressure and 20 seem of hydrogen flow. The results achieved show that IZO films were reduced for all plasma conditions used, which leads mainly to a decrease on films transmittance. For the lowest power density used in the first minute of plasma exposition the transmittance of the IZO films decreases about 29%.

The aim of this paper was to present results of the role of the d.c. grid bias on the silane plasma impedance and its I-V characteristics to grow undoped amorphous silicon (a-Si:H) films by plasma enhanced chemical vapour deposition (PECVD) in conditions where some nanoparticles can be formed in the growth region of the deposition process, under proper ion bombardment. The results achieved show that the performances of the films produced are dependent on the self bias voltage that can present photosensitivities of approximately 107 (two orders of magnitude larger than the one exhibited by films grown under conventional conditions) with density of states determined by the constant photocurrent method below 4×1015 cm-3. Apart from that, the films grown are less affected by light soaking than the conventional films.

In this work we present a study of influence of ion bombardment on the optical, electrical and compositional properties of the intrinsic amorphous silicon films deposited in a modified triode plasma-enhanced chemical vapour deposition (PECVD) reactor. The application of a DC voltage to a grid placed in front of the r.f. electrode allowed us to control the energy and polarity of the ions striking the substrate during film growth. The results show a variation by two orders of magnitude in the dark conductivity from 10-10 to 6.2 × 10-12 (Ω cm)-1, while the photosensitivity varied from 2 × 105 to 2 × 107. A process plasma that takes place in the γ-type regime was associated with the use of a negative bias, while a process plasma like the one of the α-type regime was associated with the use of a positive bias. The films deposited with a bias ≈ 38 V are highly intrinsic and the abrupt change in the conductivity properties observed at this bias is attributed to a change in the density of the states ascribed to the position of the Fermi level. That is, a precise control of the energy of the ions striking the substrate during the film growth leads to improved film optoelectronic properties, very important for device applications. © 2001 Elsevier Science Ltd. All rights reserved.

This paper aims to discuss the effect of order and disorder on the electrical performances of covalent silicon semiconductors and ZnO based ionic oxide semiconductors used as active channel layers in thin film transistors. The effect of disorder on covalent semiconductors directly affects their electrical transport properties due to the asymmetric behaviour of sp states, while in ionic oxide semiconductors it is found that this effect is small due to the fact that angular disorder has no effect on the spherical symmetry of s states. To this we must add that the mobility of carriers in both systems is quite different, being also affected by electron-phonon interactions (weak in silicon and strong in ionic oxides leading to formation of polarons). Besides, the impurity doping effect and the presence of vacancies in disordered silicon and in ionic oxides behave differently, which will influence the thin film properties and so, the performances of the devices produced. © 2007 Springer-Verlag.

The role of order and disorder on the electronic performances of n -type ionic oxides such as zinc oxide, gallium zinc oxide, and indium zinc oxide used as active (channel) or passive (drain/source) layers in thin film transistors (TFTs) processed at room temperature are discussed, taking as reference the known behavior observed in conventional covalent semiconductors such as silicon. The work performed shows that while in the oxide semiconductors the Fermi level can be pinned up within the conduction band, independent of the state of order, the same does not happen with silicon. Besides, in the oxide semiconductors the carrier mobility is not bandtail limited and so disorder does not affect so strongly the mobility as it happens in covalent semiconductors. The electrical properties of the oxide films (resistivity, carrier concentration, and mobility) are highly dependent on the oxygen vacancies (source of free carriers), which can be controlled by changing the oxygen partial pressure during the deposition process and/or by adding other metal ions to the matrix. In this case, we make the oxide matrix less sensitive to the presence of oxygen, widening the range of oxygen partial pressures that can be used and thus improving the process control of the film resistivity. The results obtained in fully transparent TFT using polycrystalline ZnO or amorphous indium zinc oxide (IZO) as channel layers and highly conductive poly/nanocrystalline ZGO films or amorphous IZO as drain/source layers show that both devices work in the enhancement mode, but the TFT with the highest electronic saturation mobility and on/off ratio 49.9 cm2 V s and 4.3× 108, respectively, are the ones in which the active and passive layers are amorphous. The ZnO TFT whose channel is based on polycrystalline ZnO, the mobility and on/off ratio are, respectively, 26 cm2 V s and 3× 106. This behavior is attributed to the fact that the electronic transport is governed by the s -like metal cation conduction bands, not significantly affected by any type of angular disorder promoted by the 2p O states related to the valence band, or small amounts of incorporated metal impurities that lead to a better control of vacancies and of the TFT off current. © 2007 American Institute of Physics.

The aim of this work is to present experimental data concerning the role of the oxygen partial pressure during the production process on the properties (structure, morphology, composition, and transport properties) exhibited by doped microcrystalline silicon oxycarbide films. The films were produced by a two consecutive decomposition and deposition chamber system, where a spatial separation between the plasma and the growth regions is achieved. The films produced by this technique are highly conductive and highly transparent with suitable properties for optoelectronic applications requiring wide band-gap and low-conductivity materials. © 1995, American Vacuum Society. All rights reserved.

The core of this paper concerns the use of an amorphous transparent conductive oxide (a-TCO), whose performance is on par with the classical indium tin oxide (ITO) films as a transparent contact in organic light emitting diodes (OLEDs). The main advantage of indium zinc oxide (IZO) films relies on their amorphous structure and high mobility that turns them likely to be used with high conductivity and high transmittance even at the infrared region. The mobility of IZO films (47.8 cm2 · V-1 · s-1) surpasses the one exhibited by ITO films (26.4 cm2 · V-1 · s-1), which along with its smoother surface and better current distribution plays an important role on OLEDs performance. Besides their similar turn-on voltage, the devices using IZO anodes exhibit higher power efficiency than the ITO ones, which is 66, 18, and 62% for orange, green, and blue OLEDs, respectively. These results suggest that IZO can potentially be applied as an anode in full color displays based on OLEDs. © 2011 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

The effects of Sn thickness electrodeposited over Cu on the structural and morphological performance of the joints formed were investigated. The electrical stability of the joints formed was analyzed under extreme aggressive conditions. Results indicated that the proposed soldering technology greatly satisfied the demands concerning soldering specifications.

Indium tin oxide (ITO) has been used as the prefered electrode material for the emerging area of transparent electronics, namely for thin-film transistors (TFTs) based on oxide semiconductors. This work pretends to investigate different materials to replace ITO in inverted-staggered TFTs based on gallium-indium-zinc oxide (GIZO), one of the most promissing oxide semiconductors for TFTs. The analyzed electrode materials are indium-zinc oxide (IZO), Ti, Mo and Ti/Au. Devices are analyzed with special focus on the contact resistance fundamentals, including the extraction of source/ drain series resistances and TFTs intrinsic parameters, such as intrinsic mobility (p\) and intrinsic threshold voltage (V Ti). The obtained contact resistance values are between 10 kΩ and 20 kΩ, and the best devices have field effect mobility ((μ FE) close to 25 cm 2/V s and on/off ratio close to 10 8. © 2008 WILEY-VCH Verlag GmbH & Co. KGaA.

This paper deals with the role the substrate on the structure of undoped and n-doped polycrystalline silicon (poly-Si) films produced by Low Pressure Chemical Vapour Deposition (LPCVD). The structural and electrical properties of the films deposited on glass, glass covered with molybdenum (Mo), oxidised crystalline silicon and oxidised crystalline silicon covered with Mo were analysed using X-ray diffraction and Spectroscopic Ellipsometry, dark conductivity and Hall effect measurements. Undoped poly-Si films deposited over Mo present modifications in the crystalline structure relatively to those deposited on the other substrates. The presence of Mo changes the preferential growth orientation, enhancing the Si {111} grains orientation, leading to more compact films. The electrical measurements also confirm that the films grown on Mo substrates present better characteristics. Some differences are also observed during the initial growth stages when using glass or oxidised silicon. Very thin n-doped films present a less effective doping effect when deposited on oxidised silicon than the ones deposited on glass substrates.

The aim of this work is to present an analytical model able to interpret the role of the thin collecting resistive layer on the static performances exhibited by 1D amorphous silicon hydrogenated p-i-n thin film position sensitive detectors. The data obtained show that the devices present a linearity and a spatial resolution, of respectively, better than 99% and 20 μm for a spatial detection limit of about 80 mm, highly dependent on the characteristics exhibited by the collecting resistive layer that should have sheet resistivities in the range of 10 to 103 Ω/sq, as predicted by the model proposed. © 1996 American Institute of Physics.

This work deals with the study of the role of intra-gap density of states on the colour selection of the collection spectrum of glass/ITO/a-Six:C1-x:H/Al Schottky photodiodes. In order to optimise the voltage colour selection and to study the influence of intragap density of states in the final device performances, different undoped a-Six:C1-x:H films (1 μm thick) have been produced in a conventional Plasma Enhanced Chemical Vapour Deposition (PECVD) system using silane and a controlled mixtures of silane and methane as gas sources. The properties of the films were analysed by dark conductivity measurements, infrared spectroscopy, visible spectroscopy and constant photocurrent method (CPM), to determine the valence controllability and to correlate the silicon carbide layer composition with the performances of the devices. The performances obtained concerning the spectral response of the devices were correlated with the carbon content and the density of states of the a-Six:C1-x:H films.

The aim of this work is to study the role of hydrogen dilution and filament temperature on the properties of nanocrystalline silicon thin films (undoped and doped) produced by the hot wire technique. These deposition parameters are correlated to the film's structure, composition and electro-optical properties with special emphasis on boron doped nanocrystalline silicon carbide reported here. © 1998 Elsevier Science B.V. All rights reserved.

The objective of this work is to present an analytical model able to interpret the experimental dependence of the uniformity of films produced by the plasma-enhanced chemical vapour deposition technique on the deposition parameters (discharge pressure, gas flow temperature and rf power density). The model proposed is based on the Navier-Stokes equations applied to a gas flow considered to be quasi-incompressible and quasi-inviscous, whenever the Mach number is below 0·3. This condition leads to the establishment of the proper quasisteady-state gas flow equations, and the corresponding equations of energy and momentum balance ascribed to the mass profile of the species formed, under the presence of a low-rf-power plasma density, are able to predict the uniformity distribution of the film over the entire deposited substrate area.

This paper reports results on the role of high hydrogen dilution (above 80%) on the electro-optical and structural properties of boron doped silicon films produced by hot wire chemical vapor deposition (HW-CVD) technique, keeping constant the filament temperature. The structural, compositional, morphological, electrical and optical properties achieved show that the films present excellent homogeneity over the entire 10 x 10 cm deposited area. These results were obtained for films produced at gas pressures below 66.5 Pa, in spite of the high flow rate used. © 2001 Elsevier Science B.V. All rights reserved.

This paper deals with the study of the role of gas temperature and of the ratio of r.f. power to gas flow on the particle’s formation in amorphous silicon films grown by plasma enhanced chemical vapour deposition technique, by monitoring the plasma impedance behaviour under different process conditions. The aim is to determine in which conditions the particles formed do not deteriorate the performances of the films grown or even can lead to an improvement of the properties of the films deposited. The results achieved show the existence of two main boundary regions (β- and θ-regions) separating the so-called α-regime (no powder formed) from the γ-regime (powder formed). Those regions are reached either by heating the gas, changing the gas pressure or using high power to gas flow ratios. In the β-region the probability of incorporating nanoparticles in the films is low and the films exhibit properties similar to those of the ones grown in the α-regime, with a low density of voids incorporated. In the θ-region small nanoparticles can be incorporated leading to films with density of states below 5×1015 cm-3, widened Urbach energies and photosensitivities about two orders of magnitude larger than that of conventional amorphous silicon grown in the α-regime. © 2000 Elsevier Science Ltd.

This paper deals with the study of the role of gas temperature and of the ratio of r.f. power to gas flow on the particle's formation in amorphous silicon films grown by the plasma enhanced chemical vapour deposition technique, by monitoring the plasma impedance behaviour under different process conditions. The results achieved show the existence of two main boundary regions separating the so-called α-regime (no powder formed) from the γ-regime (powder formed). Those regions are reached either by heating the gas, changing the gas pressure or using high power to gas flow ratios, corresponding to the establishment of a balance between the plasma resistance and the plasma reactance. In the β-region the probability to incorporate nanoparticles in the films is low and the films exhibit photosensitivity's of about 105 with density of states determined by the constant photocurrent method below 6×1015 cm-3 with Urbach energies below 50 meV. In the θ-region small nanoparticles can be incorporated leading to films with density of states below 3×1015 cm-3, with Urbach energies above 50 meV and photosensitivity's above 106, about two orders of magnitude larger than that of conventional amorphous silicon grown in the α-regime.

Nanocrystalline p-doped silicon films were deposited at low substrate temperatures (around 200°C) in a hot wire reactor. In this paper we present the results on the role of the hydrogen dilution and filament temperature on the film's structure, composition, morphology and transport properties. The film's structure changes from honeycomb-like to a granular needle shape as the filament temperature changes from about 2000°C and hydrogen dilution 87%, to values above 2100°C and hydrogen dilution 90%, respectively. The nanocrystalline silicon-based films produced have optical gaps varying from 1.6 to 1.95 eV, with conductivities up to 0.2 S cm-1 and grain sizes (obtained by X-ray diffraction) in the range of 10-30 nm. © 1999 Elsevier Science B.V. All rights reserved.

In this work, we study the influence of the hydrogenated amorphous silicon (a-Si:H) surface treatment on the J-V characteristics of a-Si:H/Pd Schottky barrier photodiodes. The a-Si:H surface were etched, thermally oxidised and wet oxidised by H2O2. The a-Si:H films were characterised by spectroscopic ellipsometry, were we found that all the oxidation techniques promote an increase of the surface oxide thickness that was confirmed by the increase of the barrier height. The highest barrier was achieved by the H2O2 oxidation where a value of 1.17 eV was found. As a result of the barrier height increase, the dark reverse current density decreases up to 10-10 A/cm2 and the signal to noise ratio increases up to 106. The open circuit voltage under AM1.5 illumination conditions also increases from 0.4 to 0.5 V. These results reveal the importance of the a-Si:H surface preparation prior to metallization to improve the Schottky photodiodes properties. © 2002 Elsevier Science B.V. All rights reserved.

In this work we present the current/voltage characteristics of Si:H/Pd Schottky structures using high quality, low defect density amorphous silicon (a-Si:H) deposited by a non-conventional, modified triode PECVD method. This new configuration allows the deposition of compact and high quality a-Si:H with a photosensitivity of 107, yielding films with low bulk defects. AFM measurements also revealed that these films have a very smooth surface allowing a low defect interface between the metal and the a-Si:H. As a result, we show that by using these a-Si:H films and by proper control of the i-layer thickness the reverse dark current of the diode can be highly reduced achieving signal to noise ratio of 106, surpassing the results usually achieved by p-i-n structures.

The aim of this work is to present an analytical model which can to interpret the role of the collecting resistive layer on the static performances exhibited by 2D amorphous silicon hydrogenated p-i-n thin film position sensitive detectors. In addition, experimental results concerning the device linearity and spatial resolution are presented and checked against the predicted values of the analytical model proposed. © 1999 Elsevier Science S.A. All rights reserved.

In this work we present results of structural composition and morphological characteristics of polymorphous silicon (pm-Si:H) films deposited by PECVD at 13.56 and 27.12 MHz. In addition, the role of the excitation frequency on the growth rate will be also analyzed. The results show that by using the 27.12 MHz excitation frequency the hydrogen dilution in the plasma needed to produce pm-Si:H can be reduced by more than 50% as well as the rf power density, leading to an increase on the growth rate to values higher than 3 Å/s. Spectroscopic ellipsometry and Raman spectroscopy show that the 27.12 MHz pm-Si:H films are more ordered than the pm-Si:H films produced at 13.56 MHz, while the infrared spectroscopy show that the SiH2 concentration in the films is strongly reduced. AFM measurements reveal that the films produced at 27.12 MHz films are more structured, presenting also higher roughness. © 2004 Elsevier B.V. All rights reserved.

In this paper we present the effect of thickness on the electrical and optical properties of intrinsic/nondoped zinc oxide thin films deposited at room temperature by radio frequency magnetron sputtering, able to be used as a semiconductor material on electronic devices, like for example ozone gas sensors and ultraviolet detectors. These films are polycrystalline with a c-axis preferential orientation parallel to the substrate. The films present a resistivity that varies from 5.0 × 104 Ω cm to 1.0 × 109 Ω cm with an optical visible transmittance of 85%. The sensor response exceeds more than five orders of magnitude when exposed to UV light recovering to the initial state in the presence of ozone. © 2006 Elsevier B.V. All rights reserved.

Trimethylboron (TMB) has been receiving attention as a valid alternative to diborane and methane mixtures for the deposition of p-type silicon films for applications in optoelectronic devices such as solar cells. In this paper we report on p-type hydrogenated nanocrystalline silicon carbide (nc-Si:C:H) films produced by standard 13.56 MHz plasma enhanced chemical vapour deposition technique, using TMB as gas source, under high hydrogen dilution (98%) and using high deposition pressures (3 Torr). The films obtained were characterized by spectroscopic ellipsometry (SE), Raman spectroscopy (RS), and electrical measurements to determine their optical, structural and electrical properties. We achieved conductivities as high as 8.3 (Ω cm) -1, one of the highest values of conductivity published to date using TMB with standard rf-PECVD. Spectroscopic ellipsometry modeling revealed that the films growth mechanism proceeds through a sub-surface layer mechanism that leads to the formation of nanocrystalline silicon. Copyright © 2010 American Scientific Publishers All rights reserved.

This paper studies the dc and ac impedance behaviour of undoped ZnO thin films produced by spray pyrolysis and rf magnetron sputtering under UV light illumination, at room temperature, emphasising the role that the crystallite size, structure, surface morphology and the state of surface have on the electrical responsivities obtained. The results achieved show that the sputtered films with crystal sizes of about 4 nm exhibit dc electrical UV responsivities of 108. On the other hand, the spray pyrolysis films exhibit the lowest dc responsivities, due the high crystal sizes and state of surface contamination, to which very good capacitance responses were obtained, mainly due to the degree of porosity exhibit by these films when produced at low temperatures. Based on that, a two-phase electrical model is proposed to explain the set of behaviours observed. © 2005 Elsevier B.V. All rights reserved.