A novel type of plasmonic light trapping structure is presented in this paper, composed of metal nanoparticles synthesized in colloidal solution and self-assembled in uniform long-range arrays using a wet-coating method. The high monodispersion in size and spherical shape of the gold colloids used in this work allows a precise match between their measured optical properties and electromagnetic simulations performed with Mie theory, and enables the full exploitation of their collective resonant plasmonic behavior for light-scattering applications. The colloidal arrays are integrated in plasmonic back reflector (PBR) structures aimed for light trapping in thin film solar cells. The PBRs exhibit high diffuse reflectance (up to 75{%}) in the red and near-infrared spectrum, which can pronouncedly enhance the near-bandgap photocurrent generated by the cells. Furthermore, the colloidal PBRs are fabricated by low-temperature ({\textless}120 °C) processes that allow their implementation, as a final step of the cell construction, in typical commercial thin film devices generally fabricated in a superstrate configuration. © 2014 the Partner Organisations.

One of the most promising approaches to produce industrial-compatible Transparent Conducting Materials (TCMs) with excellent characteristics is the fabrication of TCO/metal/TCO multilayers. In this article, we report on the electro-optical properties of a novel high-performing TCO/metal/TCO structure in which the intra-layer is a micro-structured metallic grid instead of a continuous thin film. The grid is obtained by evaporation of Ag through a mask of polystyrene colloidal micro-spheres deposited by the Langmuir-Blodgett method and partially dry-etched in plasma. IZO/Ag grid/IZO structures with different thicknesses and mesh dimensions have been fabricated, exhibiting excellent electrical characteristics (sheet resistance below 10 $Ømega$/□) and particularly high optical transmittance in the near-infrared spectral region as compared to planar (unstructured) TCM multilayers. Numerical simulations were also used to highlight the role of the Ag mesh parameters on the electrical properties.

The interaction of light with wavelength-sized photonic nanostructures is highly promising for light management applied to thin-film photovoltaics. Several light trapping effects come into play in the wave optics regime of such structures that crucially depend on the parameters of the photonic and absorbing elements. Thus, multi-parameter optimizations employing exact numerical models, as performed in this work, are essential to determine the maximum photocurrent enhancement that can be produced in solar cells.Generalized spheroidal geometries and high-index dielectric materials are considered here to model the design of the optical elements providing broadband absorption enhancement in planar silicon solar cells. The physical mechanisms responsible for such enhancement are schematized in a spectral diagram, providing a deeper understanding of the advantageous characteristics of the optimized geometries. The best structures, composed of TiO2 half-spheroids patterned on the cells' top surface, yield two times higher photocurrent (up to 32.5 mA/cm2 in 1.5 $μ$m thick silicon layer) than the same devices without photonic schemes.These results set the state-of-the-art closer to the theoretical Lambertian limit. In addition, the considered light trapping designs are not affected by the traditional compromise between absorption enhancement versus current degradation by recombination, which is a key technological advantage.

Paper substrates, coated with ZnO nanorods (NRs) decorated with Ag nanoparticles (NPs), allowed the production of inexpensive, highly-performing and extremely reproducible three-dimensional (3D) SERS platforms. The ZnO NRs were synthesized by a simple, fast and low-temperature hydrothermal method assisted by microwave radiation and made SERS-active by decorating them with a dense array of silver nanoparticles deposited via a single-step thermal evaporation technique. Using Rhodamine 6G (R6G) as a probe molecule, with an amount down to 10-9 M, the SERS substrates allowed a Raman signal enhancement of 107. The contribution of the inter-Ag-NPs gaps for 3D geometry, ZnO NRs orientation and the large sensing area allowed by theNRscaffolds, were determinant factors for the significant Raman enhancement observed. The results demonstrate that plasmonic nanorod forests, covered with Ag NPs, are efficient SERS substrates with the advantages of being recyclable, flexible, lightweight, portable, biocompatible and extremely low-cost.

© 2014 IOP Publishing Ltd. This work reports on highly efficient surface enhanced Raman spectroscopy (SERS) constructed on low-cost, fully recyclable and highly reproducible cardboard plates, which are commonly used as disposable packaging material. The active optical component is based on plasmonic silver nanoparticle structures separated from the metal surface of the cardboard by a nanoscale dielectric gap. The SERS response of the silver (Ag) nanoparticles of various shapes and sizes were systematically investigated, and a Raman enhancement factor higher than 106for rhodamine 6G detection was achieved. The spectral matching of the plasmonic resonance for maximum Raman enhancement with the optimal local electric field enhancement produced by 60 nm-sized Ag NPs predicted by the electromagnetic simulations reinforces the outstanding results achieved. Furthermore, the nanoplasmonic SERS substrate exhibited high reproducibility and stability. The SERS signals showed that the intensity variation was less than 5{%}, and the SERS performance could be maintained for up to at least 6 months.

© 2016 WILEY-VCH Verlag GmbH {&} Co. KGaA, Weinheim The post-deposition modification of ZnO-based transparent conductive oxides (TCOs) can be the key to produce thin films with optoelectronic properties similar to indium tin oxide (ITO), but at a much lower cost. Here, we present electro-optical results achieved for post-deposition annealing of Al–Zn–O (AZO), AZO:H, Ga–Zn–O:H (GZO:H), and Zn–O:H (ZNO:H) thin films deposited by RF sputtering at room temperature. These studies comprise results of thermal annealing at atmospheric pressure, vacuum, forming gas, H2and Ar atmospheres, and H2and Ar plasmas, which lead to significant enhancement of their electro-optical properties, which are correlated to morphological and structural improvements. The post-deposition annealing leads to an enhancement in resistivity above 40{%} for AZO, AZO:H, and GZO:H, reaching $\rho$ ≈ 2.6–3.5 × 10−4$Ømega$cm, while ZnO:H showed a lower improvement of 13{%}. The averaged optical transmittance in the visible region is about 89{%} for the investigated TCOs. Such results match the properties of state-of-art ITO ($\rho$ ≈ 10−4$Ømega$cm and transmittance in VIS range of 90{%}) employing much more earth-abundant materials.

The copper zinc tin sulfide (CZTS) compound is a promising candidate as an alternative absorber material for thin-film solar cells. In this study, we investigate the direct formation of Cu1.92ZnSnx(Sb1-x)S4 compounds [CZT(A)S], with x=1, 0.85, 0.70, and 0.50, via a mechanochemical synthesis (MCS) approach, starting from powders of the corresponding metals, zinc sulfide, and sulfur. The thermal stability of the CZT(A)S compounds was evaluated in detail by in situ synchrotron high-energy x-ray diffraction measurements up to 700 °C. The CZT(A)S compounds prepared via MCS revealed a sphalerite-type crystal structure with strong structural stability over the studied temperature range. The contribution of the MCS to the formation of such a structure at room temperature is analyzed in detail. Additionally, this study provides insights into the MCS of CZTS-based compounds: the possibility of a large-scale substitution of Sn by Sb and the production of single phase CZT(A)S with a Cu-poor/Zn-poor composition. A slight increase in the band gap from 1.45 to 1.49-1.51 eV was observed with the incorporation of Sb, indicating that these novel compounds can be further explored for thin-film solar cells.

A semiclassical method is developed to calculate the energy absorption of an electronic system located in the near field of a metal nanoparticle sustaining surface plasmons. The results are found to be similar to those of photon absorption from ordinary transversal radiation. However, they are affected by a geometrical factor that can increase the absorption by several orders of magnitude. As example, we investigate ellipsoidal-shaped metal nanoparticles which, under favorable conditions, may provide near field aborption enhancements almost as large as 10(4), and in many cases above 10. (C) 2008 American Institute of Physics. [DOI: 10.1063/1.3014035]

© 2017 Elsevier B.V. Ultrasonic spray pyrolysis deposition of ZnO-based materials offers an attractive high-throughput low-cost route towards industrial production of high-quality transparent conductive oxide (TCO) thin-films. In this work, undoped and aluminium-doped ZnO films have been grown employing ultrasonic spray pyrolysis at relatively low-temperate (300 °C), followed by a post-annealing treatment. The role of Al concentration in the starting solution, as well as the rapid thermal annealing (RTA) atmosphere, were investigated and correlated to the morphological, structural, electrical and optical properties of the films. The remarkable enhancement of electrical conductivity attained here is mainly ascribed to the combined effects of: (1) homogenous incorporation of Al3+into the ZnO matrix, which enhances crystal quality providing higher electronic mobility; and (2) the RTA which releases the localized electrons caused by oxygen absorption and thereby increases the free carrier density. Under optimum deposition conditions, a low resistivity and a high optical transmittance around 4 × 10−3$Ømega$ cm and 87{%}, respectively, were obtained. The application of the RTA post-process after low temperature growth has several advantages relative to the direct growth at high temperature (usually 400–575 °C), such as shorter growth time and lower cost associated to the spray pyrolysis equipment requirements and usage. The results suggest that the electrical and optical properties of the ZnO:Al films can be further improved for solar cell applications by controlling the temperature of the post-deposition annealing in reducing atmosphere.

Indium tin oxide (ITO) is the current standard state-of-the-art transparent conductive oxide (TCO), given its remarkable optical and electrical properties. However, the scarcity of indium carries an important drawback for the long-term application due to its intensive use in many optoelectronic devices such as displays, solar cells, and interactive systems. Zinc oxide-based TCOs can be a cost-effective and viable alternative, but the limitations imposed by their transmittance versus resistivity tradeoff still keep them behind ITO. In this work, an in-depth study of the structural and compositional material changes induced by specific postannealing treatments is presented, based on aluminum zinc oxide (AZO) and hydrogenated AZO (AZO:H) thin films grown by rf-magnetron sputtering at room temperature that allows an extensive understanding of the films' electrical/structural changes and the ability to tune their physical parameters to yield increasingly better performances, which put them in line with the best ITO quality standards. The present investigation comprises results of thermal annealing at atmospheric pressure, vacuum, forming gas, H2 and Ar atmospheres and plasmas. Overall the study being performed leads to a decrease in resistivity above 40{%}, reaching $\rho$ ≈ 3 × 10−4 $Ømega$ cm, with an average optical transmittance in the visible region around 88{%}. Such results are equivalent to the properties of state-of-the-art ITO.

{\textless}p{\textgreater}Opto-electronics on/with paper is fostering a novel generation of flexible and recyclable devices for sunlight harvesting and intelligent optical sensing.{\textless}/p{\textgreater}