Carmo Lança

The electrical methods used to study the molecular movements are based on the movement of the dipoles under DC or AC electric field. We have proposed recently a combined measuring protocol to analyze charge injection/extraction, transport, trapping and de-trapping in polar or non-polar dielectric materials. The method is used here to analyze the molecular movements in polyimide in the temperature range from 293 to 572 K. A strong relaxation was observed around 402 K and a very weak relaxation around 345 K. This is the beta relaxation which is quite complex. As concern the behavior at high temperatures, above the beta relaxation, a high peak was observed that shifts continuously to higher temperatures as the charging temperature and/or the charging field increase. The maximum current of the peak increases and the temperature corresponding to the maximum current increases as the charging temperature and/or the charging field increase, given a direct observation of the so called cross-over effect related to current decay for sample charged at high fields and/or high temperatures.

The final thermally stimulated discharge current method allows a better selection of the experimental conditions for sample polarization. By decreasing the ratio between the charging time and the discharging time, the apparent peak is of the same order of magnitude as the genuine peaks and there is only a partial overlap between then. Two peaks have been identified for polyamide 11, one associated with the glass transition around 60 °C and the second associated with the Curie transition around 96 °C.

The final thermally stimulated discharge current method allows a better selection of the experimental conditions for sample polarization. By decreasing the ratio between the charging time and the discharging time, the apparent peak is of the same order of magnitude as the genuine peaks and there is only a partial overlap between then. Two peaks have been identified for polyamide 11, one associated with the glass transition around 60 degrees C and the second associated with the Curie transition around 96 degrees C.

During electric polarization charge is injected into the material. The structure is decorated with space charge and during the subsequent heating an apparent peak and the genuine peaks that are related to dipole randomization and charge detrapping are observed. The method is used here to analyze the molecular movements in polyimide in the temperature range from 293 to 623K. Two weak relaxations have been observed around 337K and around 402K. The electrical conductivity changes with temperature in agreement with the Arrhenius law only below (W=(0.84±0.03) eV ) and above ( W=(0.82±0.03) eV) the temperature range where the β relaxation is observed. The variation of the electrical conductivity with temperature, in the range of the β relaxation, is controlled by the variation of the charge currier mobility with temperature and it shows a non-Arrhenius behavior. We suggest that the β1 sub-glass relaxation is related to the rotation or oscillation of phenyl groups and the β2 sub-glass relaxation is related to the rotation or oscillation of the imidic ring. At higher temperatures an apparent peak was observed. The relaxation time of the trapped charge, at 573K, is high than 8895s.

During electric polarization charge is injected into the material. The structure is decorated with space charge and during the subsequent heating an apparent peak and the genuine peaks that are related to dipole randomization and charge detrapping are observed. The method is used here to analyze the molecular movements in polyimide in the temperature range from 293 to 623 K. Two weak relaxations have been observed around 337 K and around 402 K. The electrical conductivity changes with temperature in agreement with the Arrhenius law only below (W= (0.84 +/- 0.03) eV) and above ( W (0.82 +/- 0.03) eV) the temperature range where the beta relaxation is observed. The variation of the electrical conductivity with temperature, in the range of the beta relaxation, is controlled by the variation of the charge currier mobility with temperature and it shows a non-Arrhenius behavior. We suggest that the beta(1) sub-glass relaxation is related to the rotation or oscillation of phenyl groups and the beta(2) sub-glass relaxation is related to the rotation or oscillation of the imidic ring. At higher temperatures an apparent peak was observed. The relaxation time of the trapped charge, at 573 K, is high than 8895 s. (C) 2010 Elsevier B.V. All rights reserved.