Estimations of the debonding process of aged joints through a new analytical method

Citation:
Biscaia, H. C., C. Chastre, and M. A. G. Silva. "Estimations of the debonding process of aged joints through a new analytical method." Composite Structures. 211 (2019): 577-595. copy at https://docentes.fct.unl.pt/hb/publications/estimations-debonding-process-aged-joints-through-new-analytical-method-0

Abstract:

The estimation of the long-term durability of adhesively bonded interfaces between Fiber Reinforced Polymers (FRP) and concrete substrates is crucial because degradation potentiates FRP premature debonding. One of the main reasons for mistrusting the use of FRP composites is the premature debonding phenomenon, which, associated to degradation, has been preventing their widespread use. In this research work, an analytical model is proposed that introduces ageing to estimate the effects of degradation of Glass (G) FRP externally bonded to concrete. Cycles were used to experimentally accelerate ageing of beam specimens, namely, (i) salt fog cycles; (ii) wet-dry cycles with salted water; (iii) temperature cycles between −10 °C and +30 °C; and (iv) temperature cycles between +7.5 °C and +47.5 °C. Based on the experimental results obtained and a corresponding bond-slip curve, the analytical model predicts the complete debonding process between FRP composites and a substrate. Consequently, the temporal evolution of the degradation of the bonded interfaces can be calculated and compared with the initial situation prior to exposure. The effects of the environmental conditions are reported and compared. © 2018 Elsevier Ltd

Notes:

cited By 11

Related External Link