2019
Monotonic and quasi-static cyclic bond response of CFRP-to-steel joints after salt fog exposure, Yang, Yongming, Biscaia Hugo, Silva Manuel A. G., and Chastre Carlos , Composites Part B: Engineering, 2019/07/01/, Volume 168, p.532-549, (2019) AbstractWebsite

Deterioration of adhesively bonded CFRP/steel systems in salt fog environment, i.e., deicing salts and ocean environments, has to be taken into account in the design of steel strengthened structures. In the present work, monotonic and quasi-static cyclic loading were applied to CFRP-to-steel double strap joints for two kinds of CFRP laminates after being aged for a period of 5000 h to evaluate the bond behavior. The bonded joints exposed to salt fog had a different failure mode than that observed in the control specimens (0 h of exposure). The severe reduction of the maximum bond stress resulted from damage initiation that occurred in the corrosion region of the steel substrate, associated with final partial rupture on the corroded steel substrate around the edge of the bonded area: it was also correlated with reduced load carrying capacity. Results of pseudo-cyclic tests showed that the relationship between a local damage parameter (D) and normalized local dissipated energy (Wd/Gf) and the normalized slip increment (ΔS/ΔSult) exhibited almost the same trend in the un-aged and aged bonded joints. The normalized slip increment can be seen as a direct indicator for the local and global damage for the un-aged and aged bonded joints. However, monotonic and quasi-static cyclic tests results revealed that the stress concentration due to local corrosion of steel substrate could lead to brittle rupture or accelerated cumulative damage once the aged bonded interface had become weaker. The bonded joints have exhibited also a smaller relative deformation capacity between CFRP and steel.

Bond durability of CFRP laminates-to-steel joints subjected to freeze-thaw, Yang, Yongming, Silva Manuel A. G., Biscaia Hugo, and Chastre Carlos , Composite Structures, 2019/03/15/, Volume 212, p.243-258, (2019) AbstractWebsite

The degradation mechanisms of bonded joints between CFRP laminates and steel substrates under severe environmental conditions require more durability data and studies to increase the database and better understand their causes. Studies on bond properties of double-strap CFRP-to-steel bonded joints with two different composite materials as well as adhesive coupons subjected to freeze-thaw cycles for 10,000 h were conducted to reduce that gap. In addition, the equivalent to the number of thermal cycles and their slips induced in the CFRP laminates was replicated by an equivalent (mechanical) loading-unloading history condition imposed by a static tensile machine. The mechanical properties of the adhesive coupons and the strength capacity of the bonded joints were only slightly changed by the artificial aging. It was confirmed that the interfacial bond strength between CFRP and adhesive is critically related to the maximum shear stress and failure mode. The interfacial bond strength between adhesive and steel degraded with the aging. However, the equivalent thermal cyclic bond stress caused no detectable damage on the bond because only the interfacial elastic regime was actually mobilized, which confirmed that pure thermal cycles aging, per se, at the level imposed, have a low impact on the degradation of CFRP-to-steel bonded joints.

2018
CFRP-to-steel bonded joints subjected to cyclic loading: An experimental study, Yang, Yongming, Silva Manuel A. G., Biscaia Hugo, and Chastre Carlos , Composites Part B: Engineering, 1 August 2018, Volume 146, p.28–41, (2018) AbstractWebsite

Pseudo-cyclic and cyclic loading were applied to CFRP-to-steel bonded joints built with two different CFRP laminates. In this paper, the strength capacity and bond-slip curves are presented and compared. The modes of failure are also described and associated with the types of material used, and the observed performances are correlated. The analysis of the results showed a threshold value for loading and amplitude level, below which the cyclic loading caused no detectable damage. For cycles above that limit, the region of the joints around the loaded end presented degradation reflected on the bond-slip stiffness and on the increase of residual deformation. It was found that the normalized dissipated energies either obtained from the bond-slip relationship or from the load-slip response had the same trend. The experimental data allowed also to establish a relationship between the damage developed within the interface and the normalized slip. A preliminary estimate of fatigue limit based on those data is suggested.

2017
Bond characteristics of CFRP-to-steel joints, Yang, Yongming, Biscaia Hugo, Chastre Carlos, and Silva Manuel A. G. , Journal of Constructional Steel Research, Volume 138, p.401-419, (2017) Abstract

Carbon Fiber Reinforced Polymer (CFRP) composites have a large potential for strengthening and retrofitting steel parts but due to their premature debonding from steel, further data and research are still required for wider application in such situations. In the present paper, the bond characteristics of CFRP-to-steel joints in pull-pull loaded conditions were studied. Monotonic loading of the double strap joints with different bond lengths was applied and the failure modes and interfacial bond-slip curves were obtained. A tri-linear bondslip model is proposed and it was derived from the experimental data. A closed-form solution approach is also proposed based on the tri-linear bond-slip model. The strength of the CFRP-to-steel interface, the distribution of the relative displacements between bonded materials, the strains developed in the CFRP laminate and the bond stresses along the interface are reported and the closed-form solution is compared with the experimental results. Two cases are selected for presentation: (i) one with the bond length greater than the effective bond length; and, inversely, (ii) one with bond length which is shorter than the effective bond length. The results predicted by the closed-form solutions are shown to be accurate enough when compared to the experiments.