Parreira, P., G. Lavareda, A. Amaral, A. M. Botelho Do Rego, O. Conde, J. Valente, F. Nunes, and Nunes C. de Carvalho. "Transparent p-type CuxS thin films." JOURNAL OF ALLOYS AND COMPOUNDS 509 (2011): 5099-5104. Abstract

The effect of different mild post-annealing treatments in air, at 270 degrees C, for 4-6 min, on the optical, electrical, structural and chemical properties of copper sulphide (CuxS) thin films deposited at room temperature are investigated. CuxS films, 70nm thick, are deposited on glass substrates by vacuum thermal evaporation from a Cu2S:S (50:50 wt.%) sulphur rich powder mixture. The as-deposited highly conductive crystalline CuS (covellite) films show high carrier concentration (similar to 10(22) cm(-3)), low electrical resistivity (similar to 10(-4) Omega cm) and inconclusive p-type conduction. After the mild post-annealing, these films display increasing values of resistivity (similar to 10(-3) to similar to 10(-2) Omega cm) with annealing time and exhibit conclusive p-type conduction. An increase of copper content in CuxS phases towards the semiconductive Cu2S (chalcocite) compound with annealing time is reported, due to re-evaporation of sulphur from the films. However, the latter stoichiometry was not obtained, which indicates the presence of vacancies in the Cu lattice. In the most resistive films a Cu2O phase is also observed, diminishing the amount of available copper to combine with sulphur, and therefore the highest values of optical transmittance are reached (65%). The appearance on the surface of amorphous sulphates with annealing time increase is also detected as a consequence of sulphur oxidation and replacement of sulphur with oxygen. All annealed films are copper deficient in regards to the stoichiometric Cu2S and exhibit stable p-type conductivity. (C) 2011 Elsevier B.V. All rights reserved.

Parreira, P., G. Lavareda, J. Valente, F. T. Nunes, A. Amaral, and C. Nunes de Carvalho. "Optoelectronic properties of transparent p-type semiconductor CuxS thin films." PHYSICA STATUS SOLIDI A-APPLICATIONS AND MATERIALS SCIENCE 207 (2010): 1652-1654. Abstract

Nowadays, among the available transparent semiconductors for device use, the great majority (if not all) have n-type conductivity. The fabrication of a transparent p-type semiconductor with good optoelectronic properties (comparable to those of n-type: InOx, ITO, ZnOx or FTO) would significantly broaden the application field of thin films. However, until now no material has yet presented all the required properties. Cu2S is a p-type narrow-band-gap material with an average optical transmittance of about 60% in the visible range for 50 nm thick films. However, due to its high conductivity at room temperature, 10 nm in thickness seems to be appropriate for device use. Cu2S thin films with 10 nm in thickness have an optical visible transmittance of about 85% rendering them as very good candidates for transparent p-type semiconductors. In this work CuxS thin films were deposited on alkali-free (AF) glass by thermal evaporation. The objective was not only the determination of its optoelectronic properties but also the feasibility of an active layer in a p-type thin film transistor. In our CuxS thin films, p-type high conductivity with a total visible transmittance of about 50% have been achieved. (C) 2010 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim

Parreira, P., G. Lavareda, J. Valente, F. T. Nunes, A. Amaral, and C. Nunes de Carvalho. "Undoped InOx Films Deposited by Radio Frequency Plasma Enhanced Reactive Thermal Evaporation at Room Temperature: Importance of Substrate." JOURNAL OF NANOSCIENCE AND NANOTECHNOLOGY 10 (2010): 2701-2704. Abstract

Conductive and transparent undoped thin films of indium oxide (InOx), 120 nm average thick, were deposited by radio frequency plasma enhanced reactive thermal evaporation (rf-PERTE) of indium in the presence of oxygen at room temperature. Several substrates were used in order to study their influence on the main properties of these films: alkali free (AF) glass, fused silica, crystalline silicon and polyethylene terephthalate (PET). Surface morphology of the InOx films as a function of the substrates was observed by SEM and showed that the undoped InOx films obtained are nano-structured. For the c-Si substrate, InOx films with increased grain size are obtained, induced by the crystalline substrate. Films deposited on fused silica and AF glass substrates show a nano-grainy surface with similar surface morphologies. The InOx films deposited on AF glass show the highest values of both: electrical conductivity of about 1100 (Omega cm)(-1) and visible transmittance of 85%. The substrate has a greater influence on the surface morphology of the films when a polymer (PET) is used. InOx films deposited on PET show a decrease in the electrical conductivity (90 (Omega cm)(-1)) and a slight decrease in the average visible transmittance (78%).

Parreira, P., E. Torres, C. Nunes, C. Nunes de Carvalho, G. Lavareda, A. Amaral, and M. J. Brites. "Dye-sensitized 1D anatase TiO2 nanorods for tunable efficient photodetection in the visible range." SENSORS AND ACTUATORS B-CHEMICAL 161 (2012): 901-907. Abstract

TiO2 films with enhanced photosensitivity were deposited on alkali free glass substrates without intentional substrate heating by pulsed DC magnetron reactive sputtering with an average thickness of about 2 mu m. Three dyes, commercial N719 and two new organic dyes were impregnated in order to control the optical spectral selectivity of such films. The type of dye used proved to dramatically influence the device's response to radiation pulses. The practical breakthrough is the use of different dyes according to the region of the electromagnetic spectrum one wants to detect. Devices with photocurrent 6 orders of magnitude higher than the dark current (from similar to 2 x 10(-12) to 2 x 10(-6) A for a 100 V bias) were fabricated with a spectral response within the visible range of the electromagnetic spectrum. In addition, this approach is likely to allow for the fabrication of hybrid photodetectors on cheap heat sensible flexible polymeric substrates. (C) 2011 Elsevier B.V. All rights reserved.