Ana Rita C. Duarte

Fast-dissolving delivery systems (FDDS) have received increasing attention in the last years. Oral drug delivery is still the preferred route for the administration of pharmaceutical ingredients. Nevertheless, some patients, e.g. children or elderly people, have difficulties in swallowing solid tablets. In this work, gelatin membranes were produced by electrospinning, containing an encapsulated therapeutic deep-eutectic solvent (THEDES) composed by choline chloride/mandelic acid, in a 1:2 molar ratio. A gelatin solution (30{%} w/v) with 2{%} (v/v) of THEDES was used to produce electrospun fibers and the experimental parameters were optimized. Due to the high surface area of polymer fibers, this type of construct has wide applicability. With no cytotoxicity effect, and showing a fast-dissolving release profile in PBS, the gelatin fibers with encapsulated THEDES seem to have promising applications in the development of new drug delivery systems.

© 2014 American Institute of Chemical Engineers. Significance: Natural deep eutectic solvents (NADES) are defined as a mixture of two or more solid or liquid components, which at a particular composition present a high melting point depression becoming liquids at room temperature. NADES are constituted by natural molecules and fully represent the green chemistry principles. For these reasons, the authors believe that the submitted manuscript is a highly valuable contribution to the field of green chemistry and chemical engineering. For the first time, the possibility to use NADES as enhancers of supercritical fluid technology is revealed.

Some approaches have been developed in our group to investigate the role of novel ionic liquids as process and property modifiers of natural-based polymers. In our previous work, we proposed the use of ionic liquids as plasticizing agents for the creation of porous structures from a semi-crystalline natural-based polymer. The current work intended to complement the previous studies, evaluating the ability of ionic liquid (IL) to plasticize polymers such as blends of starch-poly-lactic acid (SPLA) and its effect on supercritical fluid foaming process (SCF) and providing more insights on the mechanisms involved. For this purpose, blends of starch with poly (lactic) acid, with different ratios of starch and poly-lactic acid of 50:50 and 30:70 were modified and processed using 1-butyl-3-methylimidazolium chloride ([bmim]Cl). Supercritical fluid foaming was studied at different soaking times (1, 3 and 6h) using carbon dioxide at 20.0MPa and 40°C. The blends were characterized by different techniques, such as infra-red spectroscopy, differential scanning calorimetry and compression and tensile mechanical analysis. The morphology of the foamed structures was analyzed by scanning electron microscopy and micro-computed tomography. The results suggest that after 3h of soaking time an equilibrium state of carbon dioxide into the bulk samples is attained, yielding structures with 6{%} and 15{%} of porosity, for SPLA70 and SPLA50 respectively. The solubility of carbon dioxide within the matrices was studied for the same conditions and the results demonstrate a higher sorption degree in the samples doped with ionic liquid. Sorption and desorption diffusion coefficients of supercritical CO 2 in the SPLA matrix were determined for the raw polymer and for the SPLA doped with [bmim]Cl. It was found that the lower desorption diffusion coefficients are related with the higher porosity obtained by the foaming process. © 2013.

Aerogels are a special class of ultra-light porous materials with growing interest in biomedical applications due to their open pore structure and high surface area. However, they usually lack macroporosity, while mesoporosity is typically high. In this work, carbon dioxide induced gelation followed by expansion of the dissolved CO{\textless}inf{\textgreater}2{\textless}/inf{\textgreater} was performed to produce hybrid calcium-crosslinked alginate-starch hydrogels with dual meso- and macroporosity. The hydrogels were subjected to solvent exchange and supercritical drying to obtain aerogels. Significant increase in macroporosity from 2 to 25{%} was achieved by increasing expansion rate from 0.1 to 30 bar/min with retaining mesoporosity (BET surface and BJH pore volume in the range 183-544m{\textless}sup{\textgreater}2{\textless}/sup{\textgreater}/g and 2.0-6.8cm{\textless}sup{\textgreater}3{\textless}/sup{\textgreater}/g, respectively). In vitro bioactivity studies showed that the alginate-starch aerogels are bioactive, i.e. they form hydroxyapatite crystals when immersed in a simulated body fluid solution. Bioactivity is attributed to the presence of calcium in the matrix. The assessment of the biological performance showed that the aerogels do not present a cytotoxic effect and the cells are able to colonize and grow on their surface. Results presented in this work provide a good indication of the potential of the alginate-starch aerogels in biomedical applications, particularly for bone regeneration.

Electrospun structures were proposed as scaffolds owing to their morphological and structural similarities with the extracellular matrix found in many native tissues. These fibrous structures were also proposed as drug release systems by exploiting the direct dependence of the release rate of a drug on the surface area. An osteogenic differentiation factor, dexamethasone (DEX), was incorporated into electrospun polycaprolactone (PCL) nanofibers at different concentrations (5, 10, 15 and 20 wt.{%} polymer), in a single-step process. The DEX incorporated into the polymeric carrier is in amorphous state, as det ermined by DSC, and does not influence the typical nanofibers morphology. In vitro drug release studies demonstrated that the dexamethasone release was sustained over a period of 15 days. The bioactivity of the released dexamethasone was assessed by cultivating human bone marrow mesenchymal stem cells (hBMSCs) on 15 wt.{%} DEX-loaded PCL NFMs, under dexamethasone-absent osteogenic differentiation medium formulation. An increased concentration of alkaline phosphatase and deposition of a mineralized matrix was observed. Phenotypic and genotypic expression of osteoblastic-specific markers corroborates the osteogenic activity of the loaded growth/differentiation factor. Overall data suggests that the electrospun biodegradable nanofibers can be used as carriers for the sustained release of growth/differentiation factors relevant for bone tissue engineering strategies. © 2010 Elsevier Ltd.