Microstructural characterization and properties of a glass and a glassceramic made from municipal incinerator bottom ash

Citation:
Alendouro, M. S. J. G. a, R. C. C. a Monteiro, C. F. M. L. a Figueiredo, R. M. S. a Martins, R. J. C. a Silva, M. C. b Ferro, and M. H. V. b Fernandas. "Microstructural characterization and properties of a glass and a glassceramic made from municipal incinerator bottom ash." Materials Science Forum. 455-456 (2004): 827-830.

Abstract:

A glass was made using bottom ash produced by a Portuguese municipal solid waste (MSW) incinerator. The bottom ash was the single batch material used in the formation of the glass, which was obtained through a conventional melt-quenching method. The glass was then converted to glass-ceramic for further recycling to construction materials. After submitting the glass samples to several heat treatments, between 820 and 1050°C and during different times, it was verified that the optimum heat treatment schedule for the ceramization of the glass was at 1000°C for 10h, as confirmed by microstructural observation and by X-ray diffraction. The major crystalline phases precipitated in the glass-ceramic were wollastonite (CaSiO3) and diopside (Ca(Mg,Al)(Si,Al)2O6). Microstructural analysis of the glass-ceramic revealed that the crystalline phases were present as dendrites and fiber-like structures that were homogeneously distributed in the material. The glassceramic showed good mechanical properties with a hardness of 5.6 MPa and a bending strength of 101 MPa. This material had a density of 2.8 gcm-3 and a thermal expansion coefficient of 9.10-6°C-1. The glass and the glass-ceramic showed an excellent chemical stability against leaching in acidic solution and in alkaline solution. In summary, both the glass and the glass-ceramic have good chemical and mechanical properties and can, therefore, be applied as construction materials.

Notes:

cited By 1

Related External Link