Undoped InOx Films Deposited by Radio Frequency Plasma Enhanced Reactive Thermal Evaporation at Room Temperature: Importance of Substrate

Citation:
Parreira, P., G. Lavareda, J. Valente, F. T. Nunes, A. Amaral, and Nunes C. de Carvalho. "Undoped InOx Films Deposited by Radio Frequency Plasma Enhanced Reactive Thermal Evaporation at Room Temperature: Importance of Substrate." JOURNAL OF NANOSCIENCE AND NANOTECHNOLOGY 10 (2010): 2701-2704.

Abstract:

Conductive and transparent undoped thin films of indium oxide (InOx), 120 nm average thick, were deposited by radio frequency plasma enhanced reactive thermal evaporation (rf-PERTE) of indium in the presence of oxygen at room temperature. Several substrates were used in order to study their influence on the main properties of these films: alkali free (AF) glass, fused silica, crystalline silicon and polyethylene terephthalate (PET). Surface morphology of the InOx films as a function of the substrates was observed by SEM and showed that the undoped InOx films obtained are nano-structured. For the c-Si substrate, InOx films with increased grain size are obtained, induced by the crystalline substrate. Films deposited on fused silica and AF glass substrates show a nano-grainy surface with similar surface morphologies. The InOx films deposited on AF glass show the highest values of both: electrical conductivity of about 1100 (Omega cm)(-1) and visible transmittance of 85%. The substrate has a greater influence on the surface morphology of the films when a polymer (PET) is used. InOx films deposited on PET show a decrease in the electrical conductivity (90 (Omega cm)(-1)) and a slight decrease in the average visible transmittance (78%).

Notes:

2nd International Conference on Advanced Nano Materials, Univ Aveiro, Aveiro, PORTUGAL, 2008